Experimental Investigation on the Stab Resistance of Warp Knitted Fabrics

• Autorzy: Miao X , Jiang G , Kong X , Zhao S

Warianty tytułu

PL

Eksperymentalne badanie odporności na przebicie dzianin osnowowych

• Języki publikacji: EN

Abstrakty

EN

The stab resistance of two guide bar warp knitted fabric made from ultra-high molecular weight polyethylene was characterised by a maximum load, and energy at the maximum load and load versus displacement curves under quasi-static test conditions are presented. Penetration angles and side were designed. Samples with different lapping, densities and layers were tested, with a woven fabric used as the original reference. The results showed that warp knitted fabric with a moderate density and longer underlaps on the front guide bar performed better. The penetration angle and side have no observable influence on warp knitted fabrics’ stab resistance. Furthermore the performance of warp knitted fabrics during a knife penetration shows the difference from woven fabric in the damage process.

PL

W artykule stwierdzono, że odporność na przebicie specjalnych dzianin osnowowych wykonanych z włókien polietylenowych o ultra wysokim ciężarze cząsteczkowym można charakteryzować poprzez maksymalne obciążenie przy przebiciu, energię w chwili maksymalnego obciążenia i krzywymi obciążenia w funkcji przemieszczenia w warunkach testowych quasi statycznych. Między innymi określono kąty penetracji . Przygotowano próbki o różnej strukturze, masie liniowej i ilości warstw. Wyniki porównywano w stosunku do wyników uzyskanych dla tkaniny. Wyniki wskazują, że dzianiny osnowowe o średniej masie liniowej i dłuższych łącznikach oczek są bardziej odporne na przebicie. Natomiast nie stwierdzono wyraźnego wpływu kąta przebicia. Ogólnie stwierdzono wyraźną różnicę zachowania się dzianin w stosunku do tkanin przy penetracji nożem.

Słowa kluczowe

EN

stab resistance; warp knitted fabric; penetration; ultra-high molecular weight polyethylene (UHMWPE)

PL

dzianina osnowowa; penetracja; polietylen o bardzo wysokiej masie cząsteczkowej

• Wydawca: Sieć Badawcza Łukasiewicz - Łódzki Instytut Technologiczny
• Czasopismo: Fibres & Textiles in Eastern Europe
• Rocznik: 2014
• Tom: Vol. 22, no. 5 (107)
• Strony: 65--70
• Opis fizyczny: Bibliogr. 10 poz., rys., tab.

Twórcy

autor

Miao X

• P. R. China, WuXi, JiangNan University, Ministry of Education, Engineering Research Center of Warp Knitting Technology

autor

Jiang G

• P. R. China, WuXi, JiangNan University, Ministry of Education, Engineering Research Center of Warp Knitting Technology

autor

Kong X

• P. R. China, WuXi, JiangNan University, Ministry of Education, Engineering Research Center of Warp Knitting Technology

autor

Zhao S

• P. R. China, WuXi, JiangNan University, Ministry of Education, Engineering Research Center of Warp Knitting Technology

Bibliografia

• 1. Mayo JB, Wetzel E, Hosur MV, Jeelani S. Stab and puncture characterization of thermoplastic-impregnated aramid fabrics. International Journal of Impact Engineering 2009; 36: 1095-1105.
• 2. Decker MJ, C.J. Halbach, C.H. Nam, N.J. Wagner, and E.D. Wetzel. Stab resistance of shear thickening fluid (STF)- treated fabrics. Comp. Sci. Tech. 2007; 67, 3-4: 565-578.
• 3. Leonowicz M, Kozłowska J, Wierzbicki Ł, Olszewska K, Zielińska D, Kucińska I, Wiśniewski A. Rheological fluids as a potential component of textile products. FIBRES & TEXTILES in Eastern Europe 2014; 22, 1, 103: 28-33.
• 4. Olszewska K, Polak J, Zielińska D, Struszczyk MH, Kucinska I, Wierzbicki L, Kozlowska J, Leonowicz M, Wiśniewski A. Textile Composites with Magnetorheological Fluids for Potential Application in Multi-Threat Protections. Preliminary Stab - Resistance Studies. Fibres & Textiles in Eastern Europe 2013; 21, 5, 101: 112-116.
• 5. Wang L, Zhang S, Gao WM, Wang X. FEM analysis of knife penetration through woven fabrics. Computer Modeling Eng. Sci. 2007; 20, 1: 11-20.
• 6. Decker MJ, Halbach CJ, Nam CH, Wagner NJ, Wetzel ED. Stab resistance of shear thickening fluid (STF)-treated fabrics. Comp. Sci. Tech. 2007; 67, 3-4: 565-578.
• 7. Duong Tu Tien, Jong S. Kim, You Huh. Stab-resistant property of the fabrics woven with the aramid/cotton core-spun yarns. Fibers and Polymers 2010; 11, 3: 500-506.
• 8. Termonia Y. Puncture resistance of fibrous structures. Int. J. Impact Eng. 2006; 32, 9: 1512-1520.
• 9. Flambard X, Polo J. Stab resistance of multi-layers knitted structures: Comparison between para-aramid and PBO fibers. J. Adv. Mater. 2004; 36, 1: 30-5.
• 10. National Institute of Justice. Stab resistance of personal body armor, Standard 0115.00. Washington, DC: National Institute of Justice; 2000.