Fatigue life of S960QL steel welded joints

• Autorzy: Goss C. , Marecki P. , Grzelak K.

Identyfikatory

DOI

10.5604/12345865.1131308

Warianty tytułu

PL

Trwałość zmęczeniowa połączeń spawanych ze stali S960QL

• Języki publikacji: EN

Abstrakty

EN

During fatigue tests connectivity, welded steel XABO960 achieved a significant reduction in the durability of welded samples compared to samples taken from the parent material. For an explanation of the reasons for this phenomenon, residual stress and fatigue tests microfractography breakthroughs were studied. The study confirmed the occurrence of the weld area of substantial positive inclusions, residual stresses, and a high silicon content and sulphides which reduce the fatigue life of the welded joints [1, 2]. The explanation of these adverse events will be the subject of further research.

PL

Przedstawiono rezultaty badań zmęczeniowych stali S960QL i jej połączeń spawanych. Badano próbki płaskie z materiału rodzimego i spawane czołowo. Wyznaczono wykres trwałości zmęczeniowej. Przedstawiono rezultaty pomiaru naprężeń własnych i badania makro- i mikrostrukturalne przełomów zmęczeniowych.

Słowa kluczowe

EN

fatigue life; welded joint

PL

trwałość zmęczeniowa; połączenia spawane

• Wydawca: Wojskowa Akademia Techniczna im. Jarosława Dąbrowskiego
• Czasopismo: Biuletyn Wojskowej Akademii Technicznej
• Rocznik: 2014
• Tom: Vol. 63, nr 4
• Strony: 13--19
• Opis fizyczny: Bibliogr. 7 poz., tab., wykr., il.

Twórcy

autor

Goss C.

• Military University of Technology, Faculty of Mechanical Engineering, Department of Construction Machinery, 00-908 Warsaw, 2 Kaliskiego Str.

autor

Marecki P.

• Military University of Technology, Faculty of Mechanical Engineering, Department of Construction Machinery, 00-908 Warsaw, 2 Kaliskiego Str.

autor

Grzelak K.

• Military University of Technology, Faculty of Mechanical Engineering, Department of Construction Machinery, 00-908 Warsaw, 2 Kaliskiego Str.

Bibliografia

• [1] Klesnil M., Lukáš P., Fatigue of metallic materials, Academia Prague, Prague, 1992.
• [2] Maddox S., Fatigue strength of welded structures, Abington Publishing, Cambridge, 1991.
• [3] Standard ASTM E739-91: „Standard Practice for Statistical Analysis of Linear or Linearized Stress-Life (S-N) and Strain-Life (ε-N) Fatigue Data”.
• [4] Śnieżek L., Analysis of the fatigue life of the pipeline industry, Military University of Technology, Warsaw, 2010 (in Polish).
• [5] Goss Cz., Marecki P., Fatigue test welded joints steel S960QL, Materials Science Forum, vol. 726, 2012.
• [6] Lech-Grega M., Report No. 3129/N/1/4 — The residual stress measured, Skawina, 2011 (in Polish).
• [7] Goss Cz., Marecki P., The durability fatigue problems welded joint with steel S890QL, Biul. WAT, Warszawa, 2012 (in Polish).

Uwagi

EN

The paper has been prepared in the frame of implementation of the project financed by NCN No. N N502 077838.