The barrier layer protecting wooden products against fire action with the use of component plywood Part I Core material – plywood

• Autorzy: Jóźwiak Mariusz , Fojutowski Andrzej

Identyfikatory

DOI

10.5604/01.3001.0014.7353

• Języki publikacji: EN

Abstrakty

EN

The barrier layer protecting wooden products against fire action with the use of component plywood Part I Core material – plywood. Research on the barrier layer protecting wooden products against fire action with the use of component plywood are presented on the example of the composite plywood. The composite plywood consisting of: 3-layer protected against fire component plywood and 9-layer core plywood - beech UF- industrial, classic – not protected against fire (thickness 14.5 mm) was produced. Fire resistance of the component plywood was sufficient to protect core plywood against fire. The combustion index ranged from 0.68 to 0.75 and the flammability index oscillated between 0.06 and 0.07 which allows to classify composite plywood as a hardly flammable material acc. to PN-96/B-02874. Component plywood can be a semi-finished product useful for the production of fireproof wood- based materials.

PL

Warstwa barierowa zabezpieczająca wyroby drzewne przed działaniem ognia przy zastosowaniu sklejki komponentowej. Część I. Materiał rdzeniowy – sklejka. Na przykładzie sklejki kompozytowej przedstawiono badania efektywności warstwy barierowej zabezpieczającej wyroby drzewne przed działaniem ognia z użyciem sklejki komponentowej. Wyprodukowano sklejkę kompozytową składającą się z: 3-warstwowej sklejki komponentowej zabezpieczonej przeciwogniowo oraz 9-warstwowej sklejki rdzeniowej - bukowej UF - przemysłowej, klasycznej - niezabezpieczonej przeciwogniowo (grubość 14.5 mm) . Zabezpieczenie przeciwogniowe sklejki komponentowej okazało się wystarczające do ochrony sklejki rdzeniowej przed ogniem. Wskaźnik spalania sklejki kompozytowej wahał się od 0.68 do 0.75, a wskaźnik palności wahał się w granicach 0.06 – 0.07, co pozwala zaklasyfikować sklejkę kompozytową, jako materiał trudno zapalny wg PN-96 / B-02874. Sklejka komponentowa może być półfabrykatem przydatnym do produkcji trudno zapalnych materiałów drewnopochodnych.

Słowa kluczowe

EN

plywood; fire; barrier; protection; resin; MUF; adhesive

• Wydawca: Wydawnictwo Szkoły Głównej Gospodarstwa Wiejskiego w Warszawie
• Czasopismo: Annals of Warsaw University of Life Sciences - SGGW. Forestry and Wood Technology
• Rocznik: 2020
• Tom: No. 111
• Strony: 137--142
• Opis fizyczny: Bibliogr. 19 poz., rys., tab,

Twórcy

autor

Jóźwiak Mariusz

• Łukasiewicz Research Network - Wood Technology Institute

autor

Fojutowski Andrzej

• Łukasiewicz Research Network - Wood Technology Institute

Bibliografia

• 1. CZAPLICKA-KOLARZOWA K., ŚLUSARSKI L., SÓJKA-LEDAKOWICZ J., STRYKOWSKI W., FOJUTOWSKI A., WĘSIERSKI T., WRÓBLEWSKI D., 2010. Możliwości ograniczenia skutków pożarów metodami inżynierii materiałowej (Possibility of limiting the effects of fires using material engineering methods). Inżynieria Materiałowa nr 2/2010, 179-181.
• 2. FOJUTOWSKI A., 2002. Środki do zabezpieczania drewna (Wood preservatives). Materiały Budowlane (364). nr 12, 3-5.
• 3. JÓŹWIAK M. (2011): Badania fizykochemicznych procesów zachodzących w czasie starzenia się klejowych żywic MUF (Studies on physicochemical processes during the aging of adhesive MUF resins). Wydawnictwo UP Poznań.
• 4. JÓŹWIAK M., FOJUTOWSKI A. [2018]: Research on the effect of MUF resins as an agent for fire protection of plywood veneers in the form of a thermosetting adhesive film. Ann. WULS - SGGW, For. and Wood Technol. 104, 2018, 22-25.
• 5. JÓŹWIAK M., FOJUTOWSKI A. (2019): Component plywood made using melamine-urea-formaldehyde resin condensed by no-waste method as a building materials. WOOD – SCIENCE – ECONOMY 3rd International Scientific Conference, October 21-22, 2019, Poznań, 01.09.2019.
• 6. QINGWEN W., FENGQIANG W., YUNCHU H. JIAN L., 2009. Progress in Fire-Retardant Research on Wood and Wood-Based Composites: a China Perspective. Doc. No. IRG/WP 09-40476.
• 7. ÖSTMAN B., BRANDON D., FRANTZICH V., 2017. Fire safety engineering in timber buildings. Fire safety journal. Elsevier. Vol. 91. no Special Issue. 11-20.
• 8. TERZI E., KARTAL S. N., WHITE R. H., SHINODA K., IMAMURA Y., 2011: Fire performance and decay resistance of solid wood and plywood treated with quaternary ammonia compounds and common fire retardants. Eur. J. Wood Prod. (2011) 69: 41–51.
• 9. BN-75/6327-01; Aminowe żywice klejowe ciekłe (Liquid amine adhesive resins).
• 10. PN-96/B-02874; Ochrona przeciwpożarowa budynków - Metoda badania stopnia palności materiałów budowlanych (Fire protection of buildings - Method for testing the degree of flammability of building materials); PN-96/B-02874: 1996/Az1:1999.
• 11. PN-EN 13501-1; Klasyfikacja ogniowa wyrobów budowlanych i elementów budynków – Część 1: Klasyfikacja na podstawie badań reakcji na ogień (Fire classification of construction products and building elements – Part 1: Classification using test data from reaction to fire tests).
• 12. PN-EN ISO 1182: 2004; Badanie reakcji na ogień wyrobów budowlanych – Badania niepalności (Reaction to fire tests for products – Non-Combustibility Test).
• 13. PN-EN 314-1: 2007; Sklejka. Jakość sklejenia. Część 1: Metody badań (Plywood - Bonding quality - Part 1: Test methods).
• 14. PN-EN 314-2:2001 Sklejka. Jakość sklejenia. Część 2: Wymagania (Plywood - Bonding quality - Part 2: Requirements).
• 15. PN-EN 827:2006; Kleje. Oznaczanie umownej i stałej zawartości suchej substancji (Adhesives - Determination of conventional solids content and constant mass solids content).
• 16. PN-EN 717-3:1999; Płyty drewnopochodne. Oznaczanie emisji formaldehydu. Część 3. Emisja formaldehydu metodą butelkową (Wood-based panels - Determination of formaldehyde release - Part 3: Formaldehyde release by the flask method).
• 17. PN-EN 1243:2001; Kleje. Oznaczanie wolnego formaldehydu w kondensatach aminowych i amidoformaldehydowych (Adhesives - Determination of free formaldehyde in amino and amidoformaldehyde condensates).
• 18. PN-ISO 1148:1996; Tworzywa sztuczne. Wodne dyspersje polimerów i kopolimerów. Oznaczanie pH (Plastics – Aqueous dispersions of polymers and copolymers – Determination of pH).
• 19. PN-92/C-89402; Tworzywa sztuczne. Żywice w stanie ciekłym lub w postaci emulsji albo dyspersji. Oznaczanie lepkości pozornej metodą Brookfielda (Plastics. Resins in the liquid state or as emulsions or dispersions. Determination of apparent viscosity by the Brookfield’s method).

Uwagi

Opracowanie rekordu ze środków MEiN, umowa nr SONP/SP/546092/2022 w ramach programu "Społeczna odpowiedzialność nauki" - moduł: Popularyzacja nauki i promocja sportu (2022-2023).