Alumina/graphene composite in friction and wear tests. Part 2

• Autorzy: Wojteczko A. , Wiązania G. , Michalska K. , Łuszcz M. , Wojteczko K. , Rutkowski P. , Ziąbka M. , Kot M. , Pędzich Z.

Warianty tytułu

PL

Kompozyt tlenku glinu/grafenu w badaniach tarcia i zużycia. Cz. 2

• Języki publikacji: EN

Abstrakty

EN

The presented work is a continuation of tribological research on alumina/graphene composites. In our previous publication the results of wear tests on the above mentioned composite at room temperature, but also at temperatures of 150, 300 and 500°C were presented. The studies showed that this composite is promising in relation to pure alumina at ambient temperature and 150°C. In order to determine more precisely the temperatures at which the tested material can work, abrasion tests were carried out at two additional temperatures, 80 and 200°C, and the results are presented in the following paper. Noticeable plastic deformation and wear greater than at room temperature was detected already at 80°C but it was still significantly lower than at 150°C when the composite wore significantly less than pure alumina. The test carried out in 200°C gave results similar to those for 300°C, which indicates significant degradation of the material at this temperature.

PL

Prezentowana praca jest kontynuacją badań tribologicznych nad kompozytem tlenek glinu/grafen. W naszej poprzedniej publikacji prezentowano wyniki badań ścieralności dla wspomnianego kompozytu w temperaturze pokojowej, ale również temperaturach 150, 300 oraz 500°C. Badania wykazały, że kompozyt ten jest obiecujący w odniesieniu do czystego korundu w temperaturze otoczenia oraz 150°C. W celu dokładniejszego wyznaczenia temperatur, w których może pracować badany materiał, przeprowadzono próby ścieralności w dwóch dodatkowych temperaturach, 80 oraz 200°C, i wyniki przedstawiono w niniejszej publikacji. Już temperatura 80°C prowadziła do wyraźnej deformacji plastycznej i zużycia większego niż w temperaturze pokojowej, ale wciąż było wyraźnie niższe niż to w 150°C, dla których kompozyt zużywał się mniej niż czysty tlenek glinu. Natomiast test przeprowadzony w temperaturze 200°C dał wyniki zbliżone do tych dla 300°C, co świadczy o wyraźnej degradacji materiału w tej temperaturze.

Słowa kluczowe

EN

alumina; alumina/graphene composite; wear; friction; ball-on-disc

PL

tlenek glinu; kompozyt tlenek glinu/grafen; zużycie; tarcie; kula-tarcza

• Wydawca: Polskie Towarzystwo Materiałów Kompozytowych
• Czasopismo: Composites Theory and Practice
• Rocznik: 2018
• Tom: R. 18, nr 4
• Strony: 245--248
• Opis fizyczny: Bibliogr. 7 poz., rys.

Twórcy

autor

Wojteczko A.

• AGH - University of Science and Technology, Faculty of Materials Science and Ceramics, Department of Ceramics and Refractory Materials al. A. Mickiewicza 30, 30-059 Krakow, Poland

autor

Wiązania G.

• AGH - University of Science and Technology, Faculty of Mechanical Engineering and Robotics, Department of Machine Design and Technology al. A. Mickiewicza 30, 30-059 Krakow, Poland

autor

Michalska K.

• AGH - University of Science and Technology, Faculty of Materials Science and Ceramics, Department of Ceramics and Refractory Materials al. A. Mickiewicza 30, 30-059 Krakow, Poland

autor

Łuszcz M.

• AGH - University of Science and Technology, Faculty of Materials Science and Ceramics, Department of Ceramics and Refractory Materials al. A. Mickiewicza 30, 30-059 Krakow, Poland

autor

Wojteczko K.

• AGH - University of Science and Technology, Faculty of Materials Science and Ceramics, Department of Ceramics and Refractory Materials al. A. Mickiewicza 30, 30-059 Krakow, Poland

autor

Rutkowski P.

• AGH - University of Science and Technology, Faculty of Materials Science and Ceramics, Department of Ceramics and Refractory Materials al. A. Mickiewicza 30, 30-059 Krakow, Poland

autor

Ziąbka M.

• AGH - University of Science and Technology, Faculty of Materials Science and Ceramics, Department of Ceramics and Refractory Materials al. A. Mickiewicza 30, 30-059 Krakow, Poland

autor

Kot M.

• AGH - University of Science and Technology, Faculty of Mechanical Engineering and Robotics, Department of Machine Design and Technology al. A. Mickiewicza 30, 30-059 Krakow, Poland

autor

Pędzich Z.

• AGH - University of Science and Technology, Faculty of Materials Science and Ceramics, Department of Ceramics and Refractory Materials al. A. Mickiewicza 30, 30-059 Krakow, Poland

Bibliografia

• [1] Gutierrez-Gonzalez C.F., Smirnov A., Centeno A., Fernández A., Alonso B., Rochad V.G., Torrecillas R., Zurutuza A., Bartolome J.F., Wear behavior of graphene/alumina composite, Ceramics International 2015, 41, 7434-7438.
• [2] Rutkowski P., Klimczyk P., Jaworska L., Stobierski L., Zientara D., Tran K., Mechanical properties of pressure sintered alumina-graphene composites, Materiały Ceramiczne/Ceramic Materials 2016, 68, 2, 168-175.
• [3] Ahmad I., Kennedy A., Zhu Q.Y., Wear resistant properties of multiwalled carbon nanotubes reinforced Al2O3 nanocomposites, Wear 2010, 269, 71-78.
• [4] Wojteczko A., Wiązania G., Michalska K., Łuszcz M., Wojteczko K., Rutkowski P., Ziąbka M., Kot M., Pędzich Z., Alumina/graphene composite in friction and wear tests at elevated temperature, Composites - Theory and Practice 2018, 18, 3, 162-166.
• [5] Markandan K., Chin J.K., Tan M.T.T., Recent progress in graphene based ceramic composites: a review, International Journal of Materials Research 2017, 32, 84-106.
• [6] Gutiérrez-Mora F., Cano-Crespo R., Rincón A., Moreno R., Domínguez-Rodríguez A., Friction and wear behavior of alumina-based graphene and CNFs composites, Journal of the European Ceramic Society 2017, 37, 3805-3812.
• [7] ISO 20808:2016 Standard, Determination of friction and wear characteristics of monolithic ceramics by ball-on-disc method.

Uwagi

Opracowanie rekordu w ramach umowy 509/P-DUN/2018 ze środków MNiSW przeznaczonych na działalność upowszechniającą naukę (2018).