Effect of Yarn Parameters on the Knittability of Glass Ply Yarn

• Autorzy: Xiao-ming L. , Nan-liang C. , Xun-wei F.

Warianty tytułu

PL

Wpływ parametrów przędzy na zdolność dziania szklanych przędz plecionych

• Języki publikacji: EN

Abstrakty

EN

Knitted glass fabrics as a kind of reinforcement have received great attention in the composites industry in recent years. Glass yarns, however, are very difficult to be processed in the knitting process due to their high stiffness, low elongation and high coefficient of friction. In this paper, the knittability of glass ply yarns, which are of different yarn parameters, were investigated by testing their mechanical performance using a self-developed knit simulating apparatus. The experimental results show that damage caused to glass yarn during the knitting process is closely related to yarn parameters. Composition modification,fibre diameter reduction,optimizing of sizing formulation and yarn twist introduction canprovide glass yarn with a much better performance during severe abrasive interaction.

PL

W ostatnich latach wystąpił duży wzrost zainteresowania zastosowaniem przędz szklanych do otrzymywania dzianin i jako wzmocnienie kompozytów. Niestety przędze szklane są trudne do przetwarzania w procesie dziania ze względu na ich dużą sztywność, małe wydłużenie i wysoki współczynnik tarcia. W przedstawionej pracy badano przydatność do dziania szklanych przędz plecionych o różnych parametrach za pomocą specjalnie skonstruowanego przyrządu imitującego dzianie. Podczas badań stwierdzono, że uszkodzenia przędz spowodowane procesem dziania są ściśle uzależnione od parametrów przędzy. Można uzyskać znaczną poprawę warunków dziania poprzez modyfikację składu przędzy, redukcję średnicy włókien, optymalizację składu preparacji oraz skręt przędzy

Słowa kluczowe

EN

knittablility; glass ply yarn; twist level; sizing; abrasion damage resistance

PL

dzianie; szkło warstwowe przędzy; poziom skrętu; wielkość; odporność na ścieranie

• Wydawca: Sieć Badawcza Łukasiewicz - Łódzki Instytut Technologiczny
• Czasopismo: Fibres & Textiles in Eastern Europe
• Rocznik: 2008
• Tom: Vol. 16, no. 5 (70)
• Strony: 90--93
• Opis fizyczny: Bibliogr. 13 poz., rys., tab.

Twórcy

autor

Xiao-ming L.

• College of Textiles, Dong Hua University, Shanghai 201620, P.R.China
• Engineering Research Center of Technical Textiles, Ministry of Education, Donghua University, Shanghai 201620, P.R.China

autor

Nan-liang C.

• College of Textiles, Dong Hua University, Shanghai 201620, P.R.China
• Engineering Research Center of Technical Textiles, Ministry of Education, Donghua University, Shanghai 201620, P.R.China

autor

Xun-wei F.

• College of Textiles, Dong Hua University, Shanghai 201620, P.R.China

Bibliografia

• 1. Leong K.H., Ramakrishna S., Bibo G.A., Huang Z.M., Composites Part A, 2000, 31A, 197-220.
• 2. Lau K.W., Dias T., Journal of the Textile Institute, 1994, 85, 173-190.
• 3. Savci S., Curikis J.I., Plailthorpe M.T., Textile Research Journal, 2001, 71, 15-21.
• 4. Long H.R., Knitting Industry (Chinese journal), 2001, 6, 37-39.
• 5. Hong H., Mei Z., Autex Research Journal, 2005, 5, 141-148.
• 6. Flory J.F., Goksoy M., Hearle J.W.S., Journal of the Textile Institute, 1988, No 3, 417-431.
• 7. Brorens P.H., Lappage J., Bedford J., Ranford S.L., Journal of the Textile Institute, 1990, 81, 126-134.
• 8. Donmez S., Marmarali A., Textile Research Journal, 2004, 74, 1049-1054.
• 9. Chand S., Journal of the Textile Institute, 1995, 86, 490-491.
• 10. Ulku S., Ortlek H.G. and Omeroglu S., Fibres & Textiles in Eastern Europe, 2003, No. 3 (42), 38-41.
• 11. ASTM D578-05 Standard Specificationfor Glass Fibre Strands.
• 12. Morton W.E., An introduction to the study of spinning. Longmans, Green & Co. 1949.
• 13. Hearle J.W.S., El-Behery H.M.A.E., and Thakur V.M., Journal of the Textile Institute, 1959, 50, T83.