Polyesters with Enhanced Heat Resistance. Plastics and Fibres

• Autorzy: Dutkiewicz S. , Grochowska-Łapienis D. , Boryniec S. , Twarowska-Schmidt K.

Warianty tytułu

PL

Termoodporne tworzywa i włókna poliestrowe

• Języki publikacji: EN

Abstrakty

EN

Dimethyl terephthalate (DMT) and dimethyl 2,6-naphthalate (DMN) copolymers with ethylene glycol (EG) were obtained by the melt polycondensation method. Melt points and glass transition temperatures were determined for selected copolymers using DSC. The evaluation of their thermal stability was based on TGA results. Changes in relative viscosities and the lowering of the mass of the polymer samples after long-lasting heating at 200°C as well as changes in the melt viscosity after 1 h of heating at 290°C were also investigated. Fire resistance was evaluated on the basis of the oxygen index (OI) tests. The mechanical properties and thermal stability of fibres obtained from DMT/DMN copolyesters were also determined.

PL

Metodą polikondensacji w stopie otrzymano kopolimery dimetylotereftalanu (DMT) i 2,6-dimetylonaftalanu (DMN) z udziałem glikolu etylenowego. Dla wybranych kopolimerów oznaczono temperatury topnienia i zeszklenia metodą DSC oraz termostabilność metodą TGA. Zbadano zmiany lepkości względnej i masy polimerów po długotrwałym wygrzewaniu w temperaturze ponad 200°C oraz zmiany lepkości stopowej polimerów po wygrzewaniu w temperaturze 290°C w czasie 60 min. Odporność na palenie określono, wyznaczając indeks tlenowy Ol. Z kopoliestrów DMN/DMT wytworzono włókna. Oceniono właściwości mechaniczne oraz termostabilność włókien.

Słowa kluczowe

EN

dimethyl terephthalate; dimethyl 2,6-naphthalate; thermoresistant polyesters; thermoresistant fibres

PL

dimetylotereftalan; 2,6-dimetylonaftalan; poliestry termoodporne; włókna termoodporne

• Wydawca: Sieć Badawcza Łukasiewicz - Łódzki Instytut Technologiczny
• Czasopismo: Fibres & Textiles in Eastern Europe
• Rocznik: 2003
• Tom: Vol. 11, no. 2 (41)
• Strony: 28--31
• Opis fizyczny: Bibliogr. 14 poz., rys., tab.

Twórcy

autor

Dutkiewicz S.

• Institute of Chemical Fibres ul. M. Skłodowskiej-Curie 19/27,90-570 Łódź, Poland

autor

Grochowska-Łapienis D.

• Institute of Chemical Fibres ul. M. Skłodowskiej-Curie 19/27,90-570 Łódź, Poland

autor

Boryniec S.

• University of Bielsko-Biała, Institute of Textile Engineering and Polymer Materials PI. Fabryczny 5,43-300 Bielsko-Biała

autor

Twarowska-Schmidt K.

• Institute of Chemical Fibres ul. M. Skłodowskiej-Curie 19/27,90-570 Łódź, Poland

Bibliografia

• 1. Yih-Min Sun, Jeng Yueh Shieh, Chun-Shan Wang: Eur. Polym. J. 1997, 33, 317.
• 2. K. Yonetake, H. Yashiro, N. Madechi, M. Ueda, T. Masuko, Polymer 1998, 39, 5523.
• 3. P. Rim: Chem. Fibr. Inter. 1996, 46, 204.
• 4. H. J. Koslowski : Chem. Fibr. Inter. 1999, 49, 178.
• 5. Pat. US. 4 729 915.
• 6. Pat. US. 4 804 736.
• 7. Pat. US. 5 294 695.
• 8. Pat. US. 5 466 525.
• 9. BN-81/7559-07.
• 10. PN-EN ISO 2062:1997.
• 11. PN-ISO 4589-2:1999.
• 12. X. Lu, A.H. Windle, Polymer, 1995, 36, 451.
• 13. Pat. WO 99/48978.
• 14. E. Andersen, H.G. Zachmann, Colloid Polym. Sci. 1994, 272, 1.