The effect of GTAW processing on the structure and microhardness of C45 Steel

• Autorzy: Bylica A. , Adamiak S.
• Języki publikacji: EN

Abstrakty

EN

The work presented test results of surface upgrading of C45 Steel with concentrated heat flux using GTAW method. The surface layer of C45 Steel was remelted with stable speed of 200 mm/min welding head advance and using the intensity of electric arc current form 50 up to 300A and 300 A stable intensity of electric arc current the speed of head advance was changed in the rangę from 200 mm/min up to 800 mm/min. Microscope tests of obtained structure and measures of the hardness of remelted surface layers were conducted. The correlation between the intensity of electric arc current of its the feed rate and material microhardness was derived.

PL

W pracy przedstawiono wyniki badań uszlachetniania powierzchniowego stali C45 skoncentrowanym strumieniem ciepła z zastosowaniem metody GTAW. Dokonano nadtopienia warstwy wierzchniej stali C45 przy stałej szybkości przesuwu głowicy spawalniczej 200 mm/min i zastosowaniu natężenia prądu łuku elektrycznego od 50 do 300A oraz stałym natężeniu prądu luku elektrycznego 300 A zmieniano prędkość przesuwu głowicy od 200 mm/min do 800 mm/min. Przeprowadzono badania mikroskopowe otrzymanej struktury oraz wykonano pomiary twardości nadtopionych warstw. Podano zależność pomiędzy natężeniem prądu łuku elektrycznego i szybkością jego przesuwu a mikrotwardością struktury.

Słowa kluczowe

EN

C45 steel; surface layer remelting; martensite; GTAW method

PL

stal C45; przetapianie warstwy wierzchniej; martenzyt; metoda GTAW

• Wydawca: Komisja Odlewnictwa Polskiej Akademii Nauk Oddział w Katowicach
• Czasopismo: Archives of Foundry Engineering
• Rocznik: 2008
• Tom: Vol. 8, iss. 1 spec.
• Strony: 45--48
• Opis fizyczny: Bibliogr. 7 poz., rys., wykr.

Twórcy

autor

Bylica A.

• Institute of Technics, University of Rzeszów, ul. Rejtana 16a, 35-111 Rzeszów, Poland

autor

Adamiak S.

• Institute of Technics, University of Rzeszów, ul. Rejtana 16a, 35-111 Rzeszów, Poland

Bibliografia

• [1] A.W. Orlowicz A. Trytck, Shaping of microstructure and service properties of cast iron castings by surfnce refinement with elektric arc plasma, Archivcs of foundry, Vol. 7, No 23, 2007, (in Polish).
• [2] A.W. Orłowicz, A. Trytek, Effect of rapid solidification on sliding wear of iron castings, Wear 9258, 2002.
• [3] Z. Nitkiewicz, J. Iwaszko, The use of arc plasma in surface engineering. Materiał engineering, 6, 373-375, 2000, (in Polish).
• [4] Y. Adonyj, R.W. Richardson, W.A. Beaslack, Investigation of arc force effects in surface GTAW welding. Welding Journal, 9, 35-44, 1996.
• [5] Z. Opiekun, A.Trytek, The influence of plasma-generating gas on the quantity of heat taken by surface layer partially remelted casts of the MAR-M509 alloy, Archives of Foundry, Year 2006, no 18(1/2), 401-106, 2006, (in Polish).
• [6] W. Orłowicz, M. Mróz, A. Trytek, Heating efficiency in the GTAW process. Acta Metallurgica Slovaca, No 2, 539-543, 1999.
• [7] M. Mróz, A. Orłowicz, M. Tupaj, Thermal coefficients of the GTAW method. Archives of Foundry, Year 2005, no 17, 217-224, 2005, (in Polish).