Evaluation of the Electrospinning Manufacturing Process based on the Preparation of PVA Composite Fibres

• Autorzy: Huang C-C. , Lin C. K. , Lu C. T. , Lou C. W. , Chao C. Y. , Lin J. H.

Warianty tytułu

PL

Ocena procesu wytwarzania włókien kompozytowych z polialkoholu winylowego poprzez elektroprzędzenie

• Języki publikacji: EN

Abstrakty

EN

Poly (vinyl alcohol) (PVA) is a highly biocompatible, biodegradable and non-toxic synthetic material. Chitosan and gelatin, as well as PVA, have been widely used materials in recent years owing to their excellent biocompatibility, biodegradability, bacteriostasis and other desired characteristics. In this study, PVA/chitosan and PVA/gelatin nanofibrous composite membranes were fabricated using the electrospinning technique. The volume ratios of the PVA/chitosan and PVA/gelatin solutions were varied (90/10, 80/20, 70/30, 60/40, 50/50, 40/60), and the electrical field was increased from 0.5 to 1 kV/cm. The micro-morphology of the composite membranes was examined by scanning electronic microscopy (SEM) to compare the spinnability of PVA/Chitosan with that of the PVA/Gelatin electrospun membrane. Observation results indicate that when the volume ratio of the PVA/Chitosan and PVA/Gelatin solutions was 80/20, an optimal condition was obtained. SEM photographs of the PVA/Chitosan and PVA/Gelatin membranes demonstrate that PVA/Chitosan and PVA/Gelatin exhibited good spinnibility.

PL

PAW jest syntetycznym nietoksycznym polimerem o dużej biokompatybilności, biodegradowalnym. Dzięki takim cechom charakterystycznym jak również możliwości nadania właściwości bakteriostatycznych, chitozan, żelatyna i PAW są szeroko stosowane. Opisano produkcję kompozytowych membran wytworzonych z włókien PAW/chitozan i PAW/żelatyna otrzymanych metodą elektroprzędzenia. Objętościowy stosunek składników PAW/chitozan i PAW/żelatyna w roztworach przędzących wynosił 90:10%, 80:20%, 70:30%, 60:40%, 50:50% i 40:60%. Pole elektrostatyczne zwiększano z 0,5 kV/cm do 1 kV/cm. Mikromorfologię kompozytowych membran badano za pomocą SEM. Porównanie przędliwości roztworów przędzalniczych PAW/chitozan i PAW/żelatyna wykazały, że kiedy stosunek objętościowy PAW/chitozan i PAW/żelatyna był 80:20% to uzyskano optymalne warunki formowania. Fotografie SEM wykonanych membran kompozytowych wykazują bardzo dobrą przędliwość zastosowanych roztworów.

Słowa kluczowe

EN

electrospinning; PVA; gelatin; chitosan

PL

elektroprzędzenie; PVA; żelatyna

• Wydawca: Sieć Badawcza Łukasiewicz - Łódzki Instytut Technologiczny
• Czasopismo: Fibres & Textiles in Eastern Europe
• Rocznik: 2009
• Tom: Vol. 17, no. 3 (74)
• Strony: 34--37
• Opis fizyczny: Bibliogr. 10 poz., rys., tab.

Twórcy

autor

Huang C-C.

• Department of Fashion Design, Ling Tung University, Taiwan, Taiwan R. O. C.

autor

Lin C. K.

• Laboratory of Fibre Application and Manufacturing, Graduated Institute of Textile Engineering, Feng Chia University, Taiwan, Taiwan R. O. C.

autor

Lu C. T.

• Institute of Life Sciences, Central Taiwan University of Science and Technology, Taiwan, Taiwan R. O. C.

autor

Lou C. W.

• Department of Fashion Design, Ling Tung University, Taiwan, Taiwan R. O. C.

autor

Chao C. Y.

• Laboratory of Fibre Application and Manufacturing, Department of Fibre and Composite Materials, Feng Chia University, Taichung, Taiwan R. O. C.

autor

Lin J. H.

• Laboratory of Fibre Application and Manufacturing, Graduated Institute of Textile Engineering, Feng Chia University, Taiwan, Taiwan R. O. C.

Bibliografia

• 1. Ohgo K, Zhao CH, Kobayashi M, AsakuraT, Polymer 44 (2003) pp. 841–846.
• 2. Zong XH, Ran SF, Fang D, Hsiao SB, Chu B., Polymer 44 (2003) 4959–4967.
• 3. Yang DZ, Li YN, Nie J, Carbohydrate Polymers 69 (2007) pp. 538-543.
• 4. Adomaviciute E, Milasius R, The Infuence of Applied Voltage on Poly(vinyl alcohol) (PVA) Nanofibre Diameter, Fibres and Textiles in Eastern Europe Vol. 15 (2007) No. 5-6(64-65) pp. 69-72.
• 5. Ren GL, Xu XH, Liu Q, Cheng J, Yuan XY, Wu LL, Wan YZ, Reactive & Functional Polymers 66 (2006) pp. 1559–1564
• 6. Bhattarai N, Edmondson D, Veiseh O, Matsen FA, Zhang MQ, Biomaterials 26 (2005) pp. 6176–6184.
• 7. Ignatova M, Starbova K, Markova N, Manolovaa N, Rashkov I, Carbohydrate Research 341(2006) pp. 2098-2107.
• 8. Kucharska M, Niekraszewicz A, Struszczyk H, Application of selected usability forms of chitosan for dressings, Fibres and Textiles in Eastern Europe Vol. 10 No. 2(37) (2002) pp. 74-76.
• 9. Wisniewska-Wrona M, Niekraszewicz A, Struszczyk H, Guzinska K, Estimation of Polymer Compositions Containing Chitosan for Veterinary Applications, Fibres and Textiles in Eastern Europe Vol. 10 (2002) No. 3(38) pp. 82-85.
• 10. Pielka S, Paluch D, Staniszewska-Kus J, Zywicka B, Solski L, Szosland L, Czarny A, Zaczynska E, Wound Healing Acceleration by a Textile Dressing Containing Dibutyrylchitin and Chitin, Fibres and Textiles in Eastern Europe Vol. 11 (2003) No. 2(41) pp. 79-84.