Microstructure Evolution and Mechanical Properties of C-Mn Cold Rolled Dual Phase Steel after Continuous Annealing Process in Laboratory Conditions

• Autorzy: Šebek M. , Horňak P. , Zimovčák P. , Longauer S.

Identyfikatory

DOI

10.2478/amm-2014-0140

Warianty tytułu

PL

Zmiany mikrostruktury i właściwości mechaniczne walcowanej na zimno, dwufazowej stali C-Mn po procesie ciągłego wyżarzania w warunkach laboratoryjnych

• Języki publikacji: EN

Abstrakty

EN

The article deals with the influence of annealing parameters on evolution of microstructure and mechanical properties of dual phase steel. Dual phase steel was annealed in laboratory conditions according to the three chosen cycles of annealing: into intercritical region (780°C), into austenite region (920°C) and into austenite region (920°C) by subsequently cooling into intercritical region (780°C) with the hold at the temperature of 495°C. Simulation of annealing regimes by thermo-mechanical simulator Gleeble was done. The obtained microstructure consists from three phases: ferritic matrix, martensite and martensite/ bainite grains. For the microstructure identification the TEM and nanoindentation experiments were performed.

PL

Praca dotyczy wpływu parametrów wyżarzania na zmiany mikrostruktury i właściwości mechaniczne stali dwufazowej C-Mn. Stal dwufazową poddano wyżarzaniu w warunkach laboratoryjnych według trzech wybranych cykli: w zakresie między krytycznym (780°C). w obszarze austenitu (920°C) i w obszarze austenitu (920°C) ze schładzaniem do zakresu międzykrytycznego (780°C) przy temperaturze wytrzymania 495°C. Przeprowadzono symulację schematów wyżarzania przy użyciu symulatora obróbki cieplno-plastycznej Gleeble. Uzyskana mikrostruktura składa się z trzech faz: osnowy terrytycznej. martenzytu oraz ziaren martenzytu/bainitu. W celu identyfikacji mikrostruktury wykonano badania metodą TEM oraz nanoindentacji.

Słowa kluczowe

EN

dual phase steel; microstructure; annealing simulation; TEM observation; nanoindentation method

PL

stal dwufazowa; mikrostruktura; wyżarzanie ciągłe; metoda TEM; nanoindentacja

• Wydawca: Institute of Metallurgy and Materials Science of Polish Academy of Sciences ; Committee of Materials Engineering and Metallurgy of Polish Academy of Sciences
• Czasopismo: Archives of Metallurgy and Materials
• Rocznik: 2014
• Tom: Vol. 59, iss. 2
• Strony: 821--824
• Opis fizyczny: Bibliogr. 12 poz., rys. tab.

Twórcy

autor

Šebek M.

• Technical University of Košice, Faculty of Metallurgy, Department of Materials Science, Košice, Slovak Republic

autor

Horňak P.

• Technical University of Košice, Faculty of Metallurgy, Department of Materials Science, Košice, Slovak Republic

autor

Zimovčák P.

• U. S. Steel Košice, S.R.O., 044 54 Kosice Slovak Republic

autor

Longauer S.

• Technical University of Košice, Faculty of Metallurgy, Department of Materials Science, Košice, Slovak Republic

Bibliografia

• [1] International Iron and Steel Institute, Committee on Automotive Applications, Advanced High Strength Steel (AHSS), Application Guidelines 4.1 [online]. Available online at: http://www.worldautosteel.org.
• [2] O. Kwon, K. Lee, G. Kim, K. Chin, New trends in advanced high strength steel developments for automotive application. Materials Science Forum 638-642, 136-141 (2010).
• [3] R. O. Rocha, T. M. F. Melo, E. V. Pereloma, D. B. Santos, Materials Science and Engineering A 391, 296-304 (2005).
• [4] Q. G. Meng, J. Li, J. Wang, Z. G. Zhang, L. X. Zhang, Mater Des. 30, 2379-2385 (2009).
• [5] L. Gao, Q. Song, J. Yuan, Effect of continuous annealing parameters on the microstructure and magnetic property of cold rolled dual phase steel, Advanced Materials Research 476-478, 241-247 (2012).
• [6] B. Demir, M. J. Erdogan, Mater. Process. Technol. 208 (75), 647-654 (2008).
• [7] G. B. Li, Z. Z. Zhao, D. Tang, Microstructure Evolution and Mechanical Properties of 780 MPa Hot Dip Galvanized Dual-Phase Steel, Advanced Materials Research 146-147, 1331-1335 (2011).
• [8] C. Ma, D. L. Chen, S. D. Bhole, G. Boundreau, A. Lee, E. Biro, Materials Science and Engineering A 485, 334-346 (2008).
• [9] K. Shuang, K. Yonglin, Y. Hao, L. Rendong, Y. Ling, Iron and Steel. 42, 65-70 (2007).
• [10] I. Hrivňák, Teória zvaritělnosti kovovazliatin, 1st. ed., Veda, (1989).
• [11] Thyssen Krupp Steel Europe: DP-Wand DP-Kdual-phase steels for the manufacture of complex high-strength structural elements, 1-15 (2009).
• [12] M. Delincé, P. J. Jacques, T. Pardoen, Separation of size-dependent strengthening contributions in fine-grained Dual Phase steels by nanoindentation., Acta Materialia 54, 3395-3404 (2006).