Synthesis Of SiC/Cu Composite Powders From Polycarbosilane And Cupric Nitrate Trihydrate

Treść / Zawartość
Identyfikatory
Warianty tytułu
PL
Synteza kompozytowych proszków SiC/Cu z polikarbosilanu i trihydratu azotanu miedzi(II)
Języki publikacji
EN
Abstrakty
EN
SiC/Cu composite powders with the barrier coating of SiC-Al onto SiC powders were synthesized from Al-containing polycarbosilane precursor and Cu-nitrate hydrate. Curing at 200°C and high temperature pyrolysis at 1600°C was used to achieve the crystallization of precursor, forming the SiC-Al coating on the surface of SiC powders. A core-shell structure with the core of SiC and the shell of Cu was constructed by calcination and hydrogen-reduction of Cu nitrate hydrate. XRD and SEM analysis revealed that the β-SiC and 4H-SiC phases were formed on the surface of the initial α-SiC powders. Also, it was observed by EDX mapping that core powders of SiC were homogeneously surrounded with the fine Cu particles on their surface.
Twórcy
autor
  • Department of Materials Science and Engineering, Seoul National University of Science and Technology, Seoul 139-743, Korea
autor
  • Department of Materials Science and Engineering, Seoul National University of Science and Technology, Seoul 139-743, Korea
autor
  • Department of Materials Science and Engineering, Seoul National University of Science and Technology, Seoul 139-743, Korea
autor
  • Department of Materials Science and Engineering, Seoul National University of Science and Technology, Seoul 139-743, Korea
Bibliografia
  • [1] G. Sundberg, P. Paul, C. Sung, T. Vasilos, J. Mater. Sci. 41, 485 (2006).
  • [2] Th. Schubert, B. Trindade, T. Weißgräber, B. Kieback, Mater. Sci. Eng. A 475, 39 (2008).
  • [3] R. Zhang, L. Gao, J. Guo, Ceram. Intern. 30, 401 (2004).
  • [4] K.-M. Shu, G. C. Tu, Mater. Sci. Eng. A 349, 236 (2003).
  • [5] G. W. Liu, M. L. Muolo, F. Valenza, A. Passerone, Ceram. Intern. 36, 1177 (2010).
  • [6] R. Zhang, L. Gao, J. Guo, J. Am. Ceram. Soc. 86, 1446 (2003).
  • [7] K. K. Gan, M. Y. Gu, G. Mu, J. Mater. Sci. 43, 1318 (2008).
  • [8] J. Hong, K.-Y. Cho, D.-G. Shin, J.-I. Kim, S.-T. Oh, D.-H. Riu, J. Mater. Chem. A 2, 2781 (2014).
  • [9] Y. Hasegawa, M. Iimura, S. Yajima, J. Mater. Sci. 15, 720 (1980).
  • [10] F. Bouillon, F. Langlais, R. Pailler, R. Naslain, F. Cruege, P.V. Huong, J.C. Sarthou, A. Delpuech, C. Laffon, P. Lagarde, M. Monthioux, A. Oberlin, J. Mater. Sci. 26, 1333 (1991).
  • [11] H. Q. Ly, R. Taylor, R. J. Day, F. Heatley, J. Mater. Sci. 36, 4045 (2001).
  • [12] S.-T. Oh, J.-S. Lee, T. Sekino, K. Niihara, Scr. Mater. 44, 2117 (2001).
  • [13] Gmelins Handbuch der Anorganischen Chemie, Cu. 8. Aufl., System-Nummer 60. Verlag Chemie GmbH, Weinheim 1958.
  • [14] G. Fierro, M. Lojacono, M. Inversi, P. Porta, R. Lavecchia, F. Cioci, J. Catal. 148, 709 (1994).
Uwagi
PL
Opracowanie ze środków MNiSW w ramach umowy 812/P-DUN/2016 na działalność upowszechniającą naukę.
Typ dokumentu
Bibliografia
Identyfikator YADDA
bwmeta1.element.baztech-921fb443-1046-472a-97c5-832211b9ed5e
JavaScript jest wyłączony w Twojej przeglądarce internetowej. Włącz go, a następnie odśwież stronę, aby móc w pełni z niej korzystać.