Prediction of changes in properties of pipes from polyethylene in the research of simulation of ageing

• Autorzy: Gnatowski A. , Chyra M.
• Języki publikacji: EN

Abstrakty

EN

This study presents a comparative analysis of specimens before and after photochemical and electrochemical ageing processes. The specimens were cut out of the pipes obtained through extrusion. The examinations were carried out for two commercial grades of polyethylene. Ageing with UV radiation was carried out using a gas discharge lamp, whereas simulation of electrochemical ageing was performed in a water solution of NaCl. Tensile strength testing, differential scanning calorimetry, colour and gloss measurements and hardness testing using the method of ball indentation were carried out for both types of specimens (after ageing and without ageing). Analysis of the results of the examinations revealed that ageing caused significant changes in properties of the specimens. In the samples after ageing was observed decrease in tensile strength. Found a decrease in the degree of crystallinity and changing temperatures physical changes. In the samples after ageing was observed different values of the parameters describing the colour. In samples after ageing also reported a reduction in gloss and hardness.

Słowa kluczowe

EN

pipes; polyethylene; ageing; thermal properties; mechanical properties; colour; gloss

PL

rury; polietylen; starzenie; właściwości termiczne; właściwości mechaniczne; kolor; szkło

• Wydawca: Centrum Badań i Innowacji Pro-Akademia ; Ukrainian Academy of Sciences - Research and Development Centre for Industrial Problems of Development
• Czasopismo: Acta Innovations
• Rocznik: 2015
• Tom: no. 16
• Strony: 39--47
• Opis fizyczny: Bibliogr. 14 poz., wykr.

Twórcy

autor

Gnatowski A.

• Częstochowa University of Technology, Department of Polymer Processing, 19c Armii Krajowej Av., 42-201 Częstochowa, Poland

autor

Chyra M.

• Częstochowa University of Technology, Department of Polymer Processing, 19c Armii Krajowej Av., 42-201 Częstochowa, Poland

Bibliografia

• [1] Z. Dobkowski, Lifetime prediction for polymer materials using OIT measurements by the DSC method, Polimery 3 (2005) 213-215.
• [2] D. Sobków, K. Czaja, Wpływ warunków przyspieszonego starzenia na proces degradacji poliolefin, Polimery 9 (2003) 627-632.
• [3] A. Gnatowski, Badania struktury i właściwości termicznych polietylenu i kompozytów polietylenu z włóknem tekturowym po procesach wygrzewania i starzenia promieniami UV, Composites Theory and Practise (2009) 3 238-243.
• [4] T. Jachowicz, A. Krzyżak, Wpływ starzenia naturalnego na wybrane właściwości rur z polietylenu, Matrol (2009) 70-76.
• [5] A. Pusz, K. Michalik, Creep damage mechanisms in gas pipes made of high density polyethylene, Archives of Materials Science and Engineering 2 (2009) 89-95.
• [6] M. Maity, B.B. Khatua, C.K. Das, Effect of processing on the thermal stability of the blends based on polyurethane, Polymer degradation and stability 72 (2001) 499-503.
• [7] Brabowska B.: Biodegradacja tworzyw polimerowych, Archives of Foundry Engineering 10 (2010) 57-60.
• [8] K. Czaja K.: Poliolefiny, WNT, Warszawa, 2005.
• [9] M. Kwacz, J. Zadrosz, Przykłady zastosowań rur z tworzyw sztucznych w sieciach podziemnych cz. II, Nowoczesne Budownictwo Inżynieryjen 3 (2008) 66-71.
• [10] E. Piekarska, Rury z polietylenu - niezawodność funkcjonowania w wodociągach, sieciach paliw gazowych i kanalizacji, Przetwórstwo Tworzyw 2 (2008) 39-44.
• [11] J. Molenda, M. Wrona, E. Siwiec, Zastosowanie modelu CIE lab w badaniach barwy lotnych popiołów, Problemy Eksploatacji 3 (2012) 177-187.
• [12] A. Gnatowski, Influence of injection moulding condition and annealing on thermal properties, structure, color and gloss of composite polyamide 6 with glass beads, Composites Theory and Practise 2, (2012) 115-120.
• [13] M. EL-Nouby, M. El Shazy, Attenuation of UV-B radiation in the atmosphere: Clouds effect, at Qena (Egypt), Atmospheric Environment, 41 (2007) 4856-4864.
• [14] F. Joao, N. Eduardo, P. Amauri, J. Soares, Modeling hourly and daily fractions of UV, PAR and NIR to global solar radiation under various sky conditions at Botucatu, Brazil, Applied Energy, 86 (2009) 299-309.

Uwagi

Opracowanie rekordu w ramach umowy 509/P-DUN/2018 ze środków MNiSW przeznaczonych na działalność upowszechniającą naukę (2018).