Microstructure and microhardness of annealed austenitic cast steel

• Autorzy: Christodoulou P. , Chylińska R. , Garbiak M. , Piekarski B.

Warianty tytułu

PL

Mikrostruktura i mikrotwardość staliwa austenitycznego

• Języki publikacji: EN

Abstrakty

EN

The study proposes how to use the random HV0.01 microhardness measurements in the description of changes in the microstructure of 0,3C-18Cr-30Ni cast steel with an addition of titanium. The cast steel was investigated in four technological states, i.e. after annealing at 800°C for 10, 100, 500 and 1000 hours. Microhardness measurements were performed on unetched metallographic sections applying a 10 G load for 10 seconds. The measurements were taken at random, each time imposing a grid with 200 points on the surface of a metallographic section. Microhardness distribution density functions were detennined for the investigated technological cast steel States. To peaks occurring in different microhardness distribution density functions were assigned areas of the microstructure characterised by different content of the structural components.

PL

W pracy zaproponowano sposób wykorzystania losowego pomiaru mikrotwardości HV0,01 do opisu zmian w mikrostrukturze staliwa 0,3 C-18Cr-30Ni z dodatkiem tytanu. Badano staliwo w czterech stanach technologicznych - po wyżarzaniu w temperaturze 800°C przez 10, 100, 500 i 1000 godzin. Pomiary mikrotwardości przeprowadzono na zgładach nietrawionych, stosując obciążenie 10 G przez 10 sekund. Pomiary wykonano losowo, każdorazowo nakładając na powierzchnię zgładu siatkę 200 punktów. Wyznaczono funkcje gęstości rozkładów mikrotwardości dla badanych stanów technologicznych staliwa. Pikom występującym w poszczególnych funkcjach gęstości rozkładów mikrotwardości przyporządkowano obszary mikrostruktury charakteryzujące się odmiennym udziałem składników strukturalnych.

Słowa kluczowe

EN

austenitic cast steel; microhardness; precipitation

PL

staliwo austenityczne; mikrotwardość; procesy wydzieleniowe

• Wydawca: Wydawnictwo SIGMA-NOT
• Czasopismo: Inżynieria Materiałowa
• Rocznik: 2013
• Tom: Vol. 34, nr 3
• Strony: 145--148
• Opis fizyczny: Bibliogr. 11 poz., rys., tab.

Twórcy

autor

Christodoulou P.

• FLSmidth Ludowici, Pinkenba, Australia

autor

Chylińska R.

• Institute of Materials Science, West Pomeranian Uiversity of Technology, Szczecin

autor

Garbiak M.

• Institute of Materials Science, West Pomeranian Uiversity of Technology, Szczecin

autor

Piekarski B.

• Institute of Materials Science, West Pomeranian Uiversity of Technology, Szczecin

Bibliografia

• [1] Błażowski St., Mikoszewski J.: Pomiary twardości metali. WNT, Warszawa (1981).
• [2] Praca zbiorowa pod red. K. Przybylowicza i St. Jasieńskiej: Nowoczesne metody badawcze w metalurgii i metaloznawstwie. Skrypt AGH nr 797, Kraków (1981).
• [3] Christodoulou P., Garbiak M., Piekarski B.: Materials micro-hardness “finger prints”. Mat. Sci. and Eng., A457 (2007) 350÷367.
• [4] Chylińska R.: Procesy wydzieleniowe w żarowytrzymałym staliwie typu 30Ni-18Cr stabilizowanym dodatkami niobu i tytanu. PhD thesis, Zachodniopomorski Uniwersytet Technologiczny W Szczecinie, Szczecin (2010).
• [5] Garbiak M.: Ocena wpływu niobu i tytanu na strukturę i właściwości mechaniczne staliwa typu 30Ni-18Cr. PhD thesis, Politechnika Szczecińska, Szczecin (2006).
• [6] Garbiak M.: Applying microhardness to microstructure analysis. Chem. Listy 104 (2010) 267÷270.
• [7] Chambers J. M., Hastie T. J.: Statistical models in S. Chapman & Hall Inc. (1993).
• [8] Garbiak M., Piekarski B.: Węgliki eutektyczne w staliwie austenitycznym. 1(2010)12÷16.
• [9] Users Manual. ProFit v.1.0c, Philips Electronics N. V. (1996).
• [10] http://www.sigmaplot.com/products/peakfit/peak%20fitting.php.
• [11] Piekarski B.: The influence ofNb, Ti, and Si additions on the liquidus and solidus temperatures and primary microstructure refinement in 0.3C-30Ni- 18Cr cast steel. Mater. Char. 61 (2010) 899÷906