The effect of modified bentonites on the thixotropic properties of coating materials and their resistance against mold fungi settlement

• Autorzy: Oleksy M. , Lecka-Szlachta K. , Heneczkowski M. , Galina H.

Warianty tytułu

PL

Wpływ modyfikowanych bentonitów na właściwości tiksotropowe materiałów powłokowych oraz na odporność na działanie grzybów

• Języki publikacji: EN

Abstrakty

EN

Biostatic and thixotropic properties of bentonites modified with quaternary ammonium salts (QAS) in a waterborne paint and acrylic lacquer are presented. The fungistatic properties were tested for two commercially available bentonites modified with QAS. The bentonites were added to emulsion acrylic paint and acrylic lacquer in the amount of 2 or 4 wt. %. The resulting compositions were put on gypsum plaster disks and treated with Aspergillus niger and Penicillium chrysogenum, the molds frequently met in human environments. Microbiological tests were performed using procedures consistent with Polish Standards with modifications which stemmed from the materials used. The presence of bentonites modified with QAS substantially improved the resistance of coatings against microorganism colonization. Thixotropic properties of paint compositions containing modified bentonites were also found improved.

PL

Zbadano wpływ dodatku do kompozycji farby emulsyjnej lub lakieru akrylowego, bentonitów modyfikowanych IV-rz. solami amoniowymi (QAS), na właściwości hamujące rozwój grzybów. Oceniano grzyboodporność dwóch handlowych bentonitów: Specjal i SN, modyfikowanych wybranymi handlowymi QAS (tabele 1, 2), dodawanymi do farby lub lakieru w ilości 2 lub 4 % mas. Przygotowane kompozycje nanoszono na krążki gipsowe i poddawano działaniu, najczęściej występujących w środowisku człowieka grzybów pleśniowych Aspergillus niger oraz Penicillium chrysogenum. Badania mikrobiologiczne prowadzono według wytycznych polskiej normy z pewnymi modyfikacjami wynikającymi ze specyfiki badanych materiałów (tabela 3). Najlepsze właściwości grzybostatyczne wykazywały bentonity modyfikowane QAS Bardac LF oraz Bardac 22, co jest konsekwencją ich budowy chemicznej (tabele 4, 5, rys. 2, 3). Oznaczano także wpływ dodatku modyfikowanych bentonitów na właściwości tiksotropowe badanych kompozycji (tabela 6).

Słowa kluczowe

EN

emulsion acrylic paint; acrylic lacquer; bentonites; quaternary ammonium salts; Aspergillus niger; Penicillium chrysogenum; antifungal activity

PL

farba akrylowa; lakier akrylowy; bentonity; czwartorzędowe sole amoniowe; Aspergillus niger; Penicillium chrysogenum; aktywność grzybobójcza

• Wydawca: Sieć Badawcza Łukasiewicz – Instytut Chemii Przemysłowej
• Czasopismo: Polimery
• Rocznik: 2013
• Tom: T. 58, nr 7-8
• Strony: 562--568
• Opis fizyczny: Bibliogr. 34 poz., rys., wykr.

Twórcy

autor

Oleksy M.

• Rzeszow University of Technology Faculty of Chemistry, ul. W. Pola 2, 35-959 Rzeszów, Poland

autor

Lecka-Szlachta K.

• Rzeszow University of Technology Faculty of Chemistry, ul. W. Pola 2, 35-959 Rzeszów, Poland

autor

Heneczkowski M.

• Rzeszow University of Technology Faculty of Chemistry, ul. W. Pola 2, 35-959 Rzeszów, Poland

autor

Galina H.

• Rzeszow University of Technology Faculty of Chemistry, ul. W. Pola 2, 35-959 Rzeszów, Poland

Bibliografia

• 1. Spychaj T., Spychaj S.: „Paints and Waterborne Adhesives” (in Polish), WNT, Warsaw 1996.
• 2. Santiago F., Mucientes A. E., Osorio M., Rivera C.: Eur. Polym. J. 2007, 43, 1.
• 3. Gobbert Ch., Schichtel M., Nonninger R.: Farbe Lack 2002, 108, 20.
• 4. Shirakawa M. A., John V. M., Gaylarde C. C., Gaylarde P., Gambale W.: Mater. Struct./Materiaux et Constructions 2004, 37, 472.
• 5. Emtiazi G., Nahvi I., Salehbaig M.: Res. Bull. Isfahan Univ. 1999, 1, 15.
• 6. Emtiazi G.: Poll. Res. 2000, 19, 31.
• 7. Emtiazi G., Naghavi N., Bordbar A.: Biodegradation 2001, 12, 259.
• 8. Marini M., Boni M., Iseppi R, Toselli M., Pilati F.: Eur. Polym. J. 2007, 43, 3621.
• 9. Ranalli G., Zanardini E., Sorlini C.: „Encyclopedia of Microbiology”, Elsevier, Oxford 2009, pp. 191—205.
• 10. Nohr R. S, MacDonald G. J.: J. Biomater. Sci. Polym. Ed. 1994, 5, 607.
• 11. Lin J., Murthy S. K., Olsen B. D., Gleason K. K., Klibanov A. M.: Biotechnol. Lett. 2003, 25, 1661.
• 12. Lin J., Qiu S., Lewis K., Klibanov A. M.: Biotechnol. Bioeng. 2003, 83, 168.
• 13. Jafra S., £ojkowska E.: Biotechnologia 1999, 2(45), 94.
• 14. Pat. PL 1 934 473 B1 (2007).
• 15. Pat. WO 2 006 041 251 (2006).
• 16. Pat. US 6 468 521 (2002).
• 17. Pat. WO 206 026 026 (2006).
• 18. Pat. Jap. 60 202 162 (1985).
• 19. Pat. Jap. 11 263 704 (1999).
• 20. Pat. GB 1 036 404 (1966).
• 21. Pat. Chin. 1 616 559 (2005).
• 22. Pat. Chin. 1 730 581 (2006).
• 23. Pat. DE 4 226 222 (1990).
• 24. Ślusarczyk A., Piotrkowska M.: Polimery 2008, 53, 743.
• 25. Xie Y., Krause A., Militz H., Mai C.: Prog. Org. Coat. 2006, 57, 291.
• 26. Tezel U., Pierson J. A., Pavlostathis S. G.:Water Res. 2006, 40, 3660.
• 27. Oleksy M., Galina H.: Polimery 1999, 44, 430.
• 28. Galina H., Oleksy M.: „Quaternary ammonium salts and their applications” (in Polish), Wyd. Inst.Techn. Drewna, Poznań 2001, pp. 133—146.
• 29. Oleksy M., Heneczkowski M.: Polimery 2005, 50, 143.
• 30. Oleksy M., Heneczkowski M., Galina H.: J. Appl. Polym. Sci. 2005, 96, 793.
• 31. Oleksy M., Heneczkowski M., Galina H.: Polimery 2007, 52, 345.
• 32. Pat. PL 178 899 (2000).
• 33. Pat. PL 178 900 (2000).
• 34. Obłak E., Gamian A.: Postepy Hig. Med. Dosw. 2010, 64, 201.