Research of Tribological Properties Of Polylactide (PLA) in the 3D Printing Process in Comparison to the Injection Process

• Autorzy: Pawlak Wojciech , Wieleba Wojciech , Wróblewski Roman

Warianty tytułu

PL

Porównanie wpływu procesu druku 3D oraz procesu wtryskiwania na właściwości tribologiczne polilaktyd (PLA)

• Języki publikacji: EN

Abstrakty

EN

This article presents the results of studies on the tribological properties of linear wear and kinetic friction of polylactide processed by 3D printing (FFF) and injection moulding. Research was conducted on a pin on disc apparatus, and the test specimens used were polylactide cylinders with the counter specimen of C45 steel disc. Research was planned and executed with the planned experiment method for two variables: velocity of the counter specimen and pressure. The range of specified values was in the following sections: p = (0.2;0.6) MPa and v = (0.2;1.0) m/s . The conducted experiment had a target of defining the influence of a somewhat new method of 3D printing on the tribological properties of materials that might find application in prototyping plain bearings.

PL

W niniejszej pracy przedstawiono wyniki badań właściwości tribologicznych: zużycia liniowego oraz tarci kinetycznego dla polilaktydu przetworzonego w procesie druku 3D (FFF) oraz w procesie wtryskiwania. Badania przeprowadzone zostały na aparaturze pin on disc, próbkę stanowił materiał badany, przeciwpróbkę – tarcza stalowa C45. Badania zostały zaplanowane i przeprowadzone przy pomocy eksperymentu rotalnego dla dwóch zmiennych – prędkości obrotowej tarczy stalowej oraz nacisku. Zakres określonych wartości zawierał się w przedziałach: p = (0.2;0.6) MPa and v = (0.2;1.0) m/s . Przeprowadzony eksperyment miał na celu przedstawienie wpływu stosunkowo nowej metody druku 3D na właściwości tworzyw sztucznych, mogących znaleźć zastosowanie w wytwarzaniu prototypowych lub krótkobieżnych łożysk ślizgowych.

Słowa kluczowe

EN

PLA; polylactic; polylactide; 3D printing; additive manufacturing; FFF; FDM; linear wear; injection; wear; friction

PL

PLA; polilaktyd; druk 3D; wytwarzanie przyrostowe; FFF; FDM; zużycie liniowe; wtryskiwanie; zużycie; tarcie

• Wydawca: Stowarzyszenie Inżynierów i Techników Mechaników Polskich
• Czasopismo: Tribologia
• Rocznik: 2019
• Tom: nr 1
• Strony: 25--28
• Opis fizyczny: Bibliogr. 6 poz., rys., tab.

Twórcy

autor

Pawlak Wojciech

• Wrocław University of Science and Technology, Faculty of Mechanical Engineering, ul. Łukasiewicza 7/9, 50-371 Wrocław, Poland

autor

Wieleba Wojciech

• Wrocław University of Science and Technology, Faculty of Mechanical Engineering, ul. Łukasiewicza 7/9, 50-371 Wrocław, Poland

autor

Wróblewski Roman

• Wrocław University of Science and Technology, Faculty of Mechanical Engineering, ul. Łukasiewicza 7/9, 50-371 Wrocław, Poland

Bibliografia

• 1. Pawlak W.: Wear and coefficient of friction of PLA-graphite composite in 3D printing technology, Engineering Mechanics 2018.
• 2. https://tractus3d.com/our-industrial-3d-printers/t650p-peek-3d-printer/
• 3. Wenzheng Wu, Peng Geng, Guiwei Li, Di Zhao, Haibo Zhang, Ji Zhao: Influence of layer thickness and raster angle on the mechanical properties of 3D-Printed PEEK and a comparative mechanical study between PEEK and ABS. In Materials 2015, 09.2015, 5834 5846.
• 4. Capanidis D.: Tribological research of multicomponent composite on a polyoxymethylene base during friction with steel, Tribologia 03/2009, 19–30.
• 5. Capanidis D., Wieleba W.: Badanie tarcia i zużycia kompozytów polimerowych. Laboratory instruction, Mechanical Department, Wrocław University of Science and Technology (in Polish).
• 6. Pawlak W., Wieleba W., Kluczyński J., Śnieżek L.: The influence of the addition of graphite on the tribological properties of polylactic (PLA) applied in 3D printing technology, Tribologia 01/2018, 89–93.

Uwagi

Opracowanie rekordu w ramach umowy 509/P-DUN/2018 ze środków MNiSW przeznaczonych na działalność upowszechniającą naukę (2019).