Rheological Properties of Biocelsol/Viscose Blend Solutions and Properties of Regenerated Cellulose Films

• Autorzy: Marcinčin A. , Dolgoš O. , Rusnák A. , Ciechanska D. , Wawro D.

Warianty tytułu

PL

Właściwości reologiczne roztworów Bicelsol/wiskoza oraz właściwości folii wytwarzanych z celulozy regenerowanej

• Języki publikacji: EN

Abstrakty

EN

The dissolving of cellulose in suitable solvents to prepare fibre-forming and film-forming solutions has been a very attractive field of research for more than a hundred years. In this paper we present the rheological properties of alkali solutions of enzyme-treated cellulose (BiocelsolTM) and the blend of Biocelsol-viscose solutions. The effect of solution composition, storage temperature and time on the viscosity and deviation from the Newtonian flow were investigated. The reproducibility of the basic rheological parameters of Biocelsol alkali solutions was also investigated. The effect of the rheological properties of Biocelsol/viscose blend solutions on the tenacity of the regenerated cellulose films is discussed, as well.

PL

Rozpuszczanie celulozy w odpowiednich rozpuszczalnikach w celu uzyskania roztworów nadających się do wytwarzania włókien i folii jest tematem przyciągającym uwagę naukowców od ponad stu lat. W tej pracy zaprezentowaliśmy właściwości reologiczne roztworów alkalicznych enzymatycznie obrabianej celulozy (BiocelsolTM) oraz roztworów mieszanych Biocelsol/wiskoza. Badano wpływ składu roztworów, temperatury i czasu przechowywania na lepkość i odchylenie od przepływu płynu newton’owskiego. Sprawdzano powtarzalność wyników podstawowych parametrów reologicznych alkalicznych roztworów Biocelsol. Badano wpływ właściwości reologicznych roztworów mieszanych Biocelsol/wiskoza na wytrzymałość na rozciąganie folii wytworzonych z celulozy regenerowanej.

Słowa kluczowe

EN

rheological properties; spinning solutions viscose; Biocelsol; cellulose films

PL

właściwości reologiczne; roztwory przędzalnicze wiskozy; Biocelsol; folie celulozowe

• Wydawca: Sieć Badawcza Łukasiewicz - Łódzki Instytut Technologiczny
• Czasopismo: Fibres & Textiles in Eastern Europe
• Rocznik: 2007
• Tom: Vol. 15, no. 2 (61)
• Strony: 20--25
• Opis fizyczny: Bibliogr. 14 poz., rys., tab.

Twórcy

autor

Marcinčin A.

• Slovak University of Technology, Faculty of Chemical and Food Technology, Institute of Polymer Materials, Department of Fibres and Textile Chemistry, Radlinského 9, 812 37 Bratislava, Slovakia

autor

Dolgoš O.

• Slovak University of Technology, Faculty of Chemical and Food Technology, Institute of Polymer Materials, Department of Fibres and Textile Chemistry, Radlinského 9, 812 37 Bratislava, Slovakia

autor

Rusnák A.

• Slovak University of Technology, Faculty of Chemical and Food Technology, Institute of Polymer Materials, Department of Fibres and Textile Chemistry, Radlinského 9, 812 37 Bratislava, Slovakia

autor

Ciechanska D.

• Institute of Chemical Fibres, ul. M. Skłodowskiej-Curie 19/27 Łódź, Poland

autor

Wawro D.

• Institute of Chemical Fibres, ul. M. Skłodowskiej-Curie 19/27 Łódź, Poland

Bibliografia

• 1. Heinze, T. and Liebert T.: Unconventional methods in cellulose functionalization. Progress in Polymer Science, 2001. 26(9): p. 1689-1762.
• 2. Petrovan S., Collier J. R., and Negulescu I. I. : Rheology of cellulosic N-methylmorpholine oxide monohydrate solutions of different degrees of polymerization. Journal of Applied Polymer Science, 2001. 79(3): p. 396-405.
• 3. Bleishmidt, N.V., Dreval V. E., Borodina O. E., et al.: Vysokomol. soed., 1997. A39: p. 1033.
• 4. Strusczyk, H.: Chem. Fiber Int., 1996. 46: p. 265.
• 5. Mikolajczyk, W., Wawro D., and Strusczyk H.: Cellulose Carbamate Spinning Solutions Prepared for the Manufacture of Fibres. Fibres and Textiles in Eastern Europe, 1998. 21(2): p. 53.
• 6. Rahkamo L., Siika-Aho M., Vehviläinen M., et al.: Modification of hardwood dissolving pulp with purified Trichoderma reesei cellulases. Cellulose, 1996. 3(1): p. 153-163.
• 7. Shengdong Z., Yuanxin W., Qiming C., et al.: Dissolution of cellulose with ionic liquids and its application: a mini-review. Green Chemistry, 2006. 8(4): p. 325-327.
• 8. Klemm D., Philipp B., Heinze T., et al., Comprehensive Cellulose Chemistry. Functionalization of Cellulose. Vol. 2. 1998: Wiley-VCH. p. 31-66.
• 9. Kamide K., Okajima K., and Kowsaka K.: Dissolution of Natural Cellulose into Aqueous Alkali Solution: Role of Super-Molecular Structure of Cellulose. Polymer Journal, 1992. 24(1): p. 71-86.
• 10. Mikolajczyk W. and Mikolajczyk T.: Evaluation of Rheological Properties of Cellulose Carbamate Spinning Solutions at the Temperatures of Their Processing. Fibres and Textile in Eastern Europe, 1998. 21(2): p. 56-58.
• 11. Roy C., Budtova T., and Navard P.: Rheological Properties and Gelation of Aqueous Cellulose-NaOH Solutions. Biomacromolecules, 2003. 4(2): p. 259 -264.
• 12. Roy C., Budtova T., Navard P., et al.: Structure of Cellulose-Soda Solutions at Low Temperatures. Biomacromolecules, 2001. 2(3): p. 687 -693.
• 13. Ciechanska D., Wawro D., Stęplewski W., et al.: Formation of Fibre from Bio-modified Cellulose Pulp. Fibres and Textile in Eastern Europe, 2005. 54(6): p. 19.
• 14. Zhou J., Zhang L., Cai J., et al.: Cellulose microporous membranes prepared from NaOH/urea aqueous solution. Journal of Membrane Science, 2002. 210(1): p. 77-90.