Corrosion of X2CRNiN23-4 lean duplex stainless steel annealed at 485°C

• Autorzy: Lipiński T.

Warianty tytułu

PL

Korozja stali nierdzewnej Lean duplex w gatunku X2CrNiN 23-4 po wyżarzaniu w temperaturze 485°C

• Języki publikacji: EN

Abstrakty

EN

Lean duplex stainless steels are ferritic-austenitic steel, and they present the excellent corrosion resistance of austenite steel and the high mechanical behaviour of ferrite steel. General important corrosion problems in duplex stainless steels at 475°C have been already detected. Although the worst temperature is 475°C, corrosion can still form at lower or higher temperatures. The purpose of this work was to ascertain how 30-minutes isothermal heat treatments at 485°C and corrosion time effect the relative mass loss and profile roughness parameters of X2CrNiN23-4 lean duplex stainless steel. The real critical temperature for researching steel was determinate by the DSC method. Corrosion tests were conducted in a nitric acid medium by the measurement of loss in mass (Huey test). The corrosive media was boiling nitric acid V 65%. The corrosion rate of the X2CrNiN23-4 steel was measured in mm/year and in g/m2.

PL

Stale nierdzewne Lean duplex są stalami ferrytyczno-austenitycznymi o doskonałej odporności na korozję stali austenitycznej, a wysokich właściwościach mechanicznych stali ferrytycznej. Ważny problem korozji stali odpornej na korozję duplex w temperaturze 475°C został już stwierdzony. Chociaż najniekorzystniejszą temperaturą jest 475°C, korozja może przebiegać zarówno w temperaturze niższej, jak i wyższej. Celem niniejszej pracy było zbadanie, jak 30-minutowe izotermiczne wyżarzanie stali w temperaturze 485°C oraz czas przetrzymywania w ośrodku korozyjnym wpłynie na ubytek masowy oraz chropowatość powierzchni stali lean duplex w gatunku X2CrNiN23-4. Rzeczywista temperatura krytyczna dla badań stali została określona metodą DSC. Badanie korozyjne (ubytku masy) prowadzono w środowisku kwasu azotowego V 65% w temperaturze wrzenia (test Huey). Prędkość korozji stali X2CrNiN23-4 określono w mm/rok i w g/m2.

Słowa kluczowe

EN

stainless steel; duplex steel; corrosion; corrosion rate; profile roughness

PL

stal nierdzewna; stal duplex; korozja; szybkość korozji; profil chropowatości

• Wydawca: Wydawnictwo Naukowe Instytutu Technologii Eksploatacji - Państwowego Instytutu Badawczego
• Czasopismo: Problemy Eksploatacji
• Rocznik: 2016
• Tom: no. 3
• Strony: 187--195
• Opis fizyczny: Bibliogr. 6 poz., rys., tab., wykr.

Twórcy

autor

Lipiński T.

• University of Warmia and Mazury in Olsztyn, Faculty of Technical Sciences, Department of Material and Machine Technology

Bibliografia

• 1. Angelini E., De Benedetti B., Rosalbino F.: Microstructural evolution and localized corrosion resistance of an aged superduplex stainless steel. Corros Sci 2004, 46/6, 1351-1367.
• 2. Bastos I., Tavares S., Dalarda F., Nogueira R.: Effect of microstructure on corrosion behavior of superduplex stainless steel at critical environment conditions. Scripta Mater 2007, 57/10, 913-916.
• 3. Tavares S., Pardal J., Lima L.D., Bastos I.N., Nascimento A.M., De Souza J.: Characterization of microstructure, chemical composition, corrosion resistance and toughness of a multipass weld joint of superduplex stainless steel UNS S32750. Mater Charact 2007, 58/7, 610-616.
• 4. Szabracki P., Lipiński T.: Effect of aging on the microstructure and the intergranular corrosion resistance of X2CrNiMoN25-7-4 duplex stainless steel. Sol St Phen 2013, 203-204, 59-62.
• 5. Wharton J.A., Wood R.J.K., Mellor B.G.: Wavelet analysis of electrochemical noise measurements during corrosion of austenitic and superduplex stainless steels in chloride media. Corros Sci 2003, 45, 97-122.
• 6. Łabanowski J., Świerczyńska A., Topolska S.: Effect of microstructure on mechanical properties and corrosion resistance of 2205 duplex stainless steel. Pol Marit Res 2014, 4/84, 108-112.

Uwagi

PL

Opracowanie ze środków MNiSW w ramach umowy 812/P-DUN/2016 na działalność upowszechniającą naukę.