The influence of storage time of oxo-degradable polyethylene film on the mechanical properties

• Autorzy: Gibas E. , Rymarz G.

Warianty tytułu

PL

Wpływ czasu składowania oxo-degradowalnej folii polietylenowej na właściwości mechaniczne

• Języki publikacji: EN

Abstrakty

EN

A method for the preparation of prodegradant, the transition metal compound containing iron and manganese, in a one-step manufacturing process was described. The catalytic system (prodegradant) iron-manganese stearate containing about 3-3.5% of each metal was selected to the application studies. To assess the resistance of plastic materials to weather condition, aging tests were applied, in which the plastic materials undergo destructive processes and afterwards strength tests were performed. The results of mechanical tests of polyethylene films with the addition of concentrated OXO-BIO aged under atmospheric conditions and accelerated weathering were described. Films containing 12.5% and 25% of OXO-BIO were stored for 6 months at room temperature in darkness, and then were subjected to atmospheric aging. The results of strength tests were described. After 6-month storage period, slight differences of initial mechanical properties of films (being within the tolerance limits of determined parameters) were noted.

PL

Opracowano metodę otrzymywania mieszaniny prodegradanta, czyli związku zawierającego metale przejściowe żelaza i manganu, w jednoetapowym procesie produkcyjnym. Do badań aplikacyjnych wytypowano układ katalizujący (prodegradant), będący mieszaniną stearynianu żelaza(III) i stearynianu manganu(II), zawierający około 3-3,5% każdego z metali. Do oceny odporności materiałów z tworzyw sztucznych na działanie warunków atmosferycznych zastosowano testy starzeniowe, w których tworzywa ulegają procesom destrukcyjnym, a następnie wykonano badania wytrzymałościowe. Omówiono wyniki badań mechanicznych folii polietylenowych z dodatkiem koncentratu OXO-BIO starzonych w warunkach atmosferycznych i przyspieszonych. Folie zawierające 12.5% oraz 25% OXO-BIO magazynowano przez okres 6 miesięcy w temperaturze pokojowej w zaciemnieniu, a następnie poddano starzeniu atmosferycznemu. Omówiono wyniki badań wytrzymałościowych. Po 6-miesięcznym okresie składowania zauważono niewielkie różnice w wyjściowych parametrach mechanicznych folii, mieszczących się w granicach tolerancji wartości określonych parametrów.

Słowa kluczowe

EN

polyethylene film; prodegradant; strength test

PL

folia polietylenowa; prodegradant; badania wytrzymałościowe

• Wydawca: Sieć Badawcza Łukasiewicz – Instytut Inżynierii Materiałów Polimerowych i Barwników
• Czasopismo: Przetwórstwo Tworzyw
• Rocznik: 2015
• Tom: T. 21, Nr 4 (166)
• Strony: 318--323
• Opis fizyczny: Bibliogr. 10 poz., rys., tab.

Twórcy

autor

Gibas E.

• Institute for Engineering of Polymer Materials and Dyes, Paint and Plastics Department, Gliwice

autor

Rymarz G.

• Institute for Engineering of Polymer Materials and Dyes, Paint and Plastics Department, Gliwice

Bibliografia

• [1] B. Cichy, J. Kwiecień, M. Piątkowska, E. Kużdżał, E. Gibas, G. Rymarz, Potyolefin axo-degtadation accclerators - a new trend to promote environmental protection, Pol. J.Chem.Technol„ 2010, 12 (4) 44-52
• [2] Z. Florjańczyk, M. Dąbowski, E. Chwojnowska, K. Łokaj, J. Ostrowska, Polimery syntetyczne i naturalne w nowoczesnych materiałach wielkocząsteczkowych. Cz, 1 Polimery z surowców odnawialnych i nanokompozyty polimerowe. Polimery, 2009, 54, 611-625
• [3] A. Boberg, Patent Polymer composition degradable under the influence of ultraviolet light and/or sunlight, US 3865767,1975
• [4] H. Kaczmarek, A. Felczak, D. Bajer, Photooxidative degradation of carboxylated poly (vinyl chloride), Polym. Bull. 2009, 62, 503-510
• [5] A. P. Kumara, D. Depana, N. S. Tomerb, R. P. Singha, Nanoscale particles for polymer degradation and stabilization - Trends and future perspectives, Prog. Polym. Sci., 2009,34,479-515
• [6] M. Giurginca, L. Popa, T. Zaharescu, Thermooxidative degradation and radio-processing of ethylcne vinyl acetate elastomers, Polym. Degrad. Stab., 2003, 82, 463-466
• [7] B. Nowak, J. Pająk, S. Łabużek, G. Rymarz, E. Talik, Biodegradation of poly(ethylene terephthalate) modified with polyester "Bionolle®" by Penicillium funiculosum, Polimery 2011, 56, 35-44
• [8] I. Eyenga, W. W. Focke, L. C. Prinsloo, A. T. Tolmay, Photodegradation: a solution for the shopping bag „Visual Pollution" problem?, Macromol. Symp. 2002, 178,139-152
• [9] A. Krzan, S. Hemjinda, S. Miertus, A. Corti, E. Chiellini: Standarization and certification in the area of environmentally degradable plastics, Polym. Degrad. Stab., 2006, 91(12), 2819-2833
• [10] E. Gibas, G. Rymarz, B. Cichy, E. Kużdżał, M. Turkowska, L. Hexel, M. Soja, Studies on oxo-degradation of LDPE films containing manganese and iron stearates as the prodegradant, Advances in Plastics Technology 2011, Chapter 7, 69-77