Vermicular cast iron production in the “Inmold” technology (in the Metalpol casting house) and the assessment of its thermal fatigue resistance

• Autorzy: Zych J. , Żyrek A.
• Języki publikacji: EN

Abstrakty

EN

The method of obtaining the vermicular cast iron in the “Inmold” technology and the results of the thermal fatigue investigations, are presented in the paper. The influence of the maximum cycle temperature (T_max) on the thermal fatigue resistance was examined by means of the L.F. Coffin method. The cast iron structure change caused by the thermal fatigue is presented in the paper. When the vermicular cast iron is subjected to the thermal fatigue the matrix ferritisation occurs, which leads to the strength, R_m., decrease. The heating process of the vermicular cast iron is slower as compared to the spheroidal cast iron, whereas the cooling process is faster. Under the same conditions of heat exchanging the vermicular cast iron is heated to a much lower temperature than the spheroidal one. Together with the maximum heating temperature increase the thermal fatigue resistance decreases.

Słowa kluczowe

EN

thermal fatigue; Inmold method; vermicular cast iron

PL

zmęczenie cieplne; metoda in mold; żeliwo wermikularne

• Wydawca: Komisja Odlewnictwa Polskiej Akademii Nauk Oddział w Katowicach
• Czasopismo: Archives of Foundry Engineering
• Rocznik: 2011
• Tom: Vol. 11, iss. 3 spec.
• Strony: 255--260
• Opis fizyczny: Bibliogr. 8 poz., rys., tab., wykr.

Twórcy

autor

Zych J.

• AGH University of Science and Technology, Faculty of Foundry Engineering, al. A. Mickiewicza 30, 30-059 Krakow

autor

Żyrek A.

• Metalpol Sp.z o. o., Kolejowa 6, 34-350 Węgierska Górka

Bibliografia

• [1] Zych J. - „Thermal fatigue of cast iron for metallic moulds’. Prace Komisji Metal. Odlew. Metalurgia 38, (1988) s.107-116 PAN Katowice.
• [2] Zych J. -„Investigating thermal fatigue of cast iron”. IX Sympozjum Naukowe. Kraków AGH 1983.
• [3] Zych J, Jędrzejczy k D.:„Research on thermal fatigue behavior of the vermicular graphite cast iron ”: Przegląd Odlewnictwa 1991, Nr 6 s. 215-218.
• [4] Zych J.: „Resistance to thermal fatigue cast iron with steroidal, vermicular end flakes graphite” : Solidification of Metals and Alloys, PAN , Katowice 24 (1995), s. 135-140.
• [5] Podrzucki Cz.: Żeliwo. Struktura, właściwości, zastosowanie. Wydawnictwo STOP. Kraków 1991.
• [6] Weroński A. – „Thermal fatigue of metals”. Warszawa 1983.
• [7] Normy : PN-75/H-04661 , PN-EN ISO 945:1999.
• [8] Instrukcje zakładowe odlewni Metalpol dotyczące produkcji żeliwa sferoidalnego i szarego.