Ultrasonic Assisted Active-Passive Filling Friction Stir Repairing to Eliminate Volume Defects

Treść / Zawartość
Identyfikatory
Warianty tytułu
Języki publikacji
EN
Abstrakty
EN
Ultrasonic assisted active-passive filling friction stir repairing (A-PFFSR) was proposed to repair volume defects in the metallic parts. Sound joints without interfacial defects could be achieved. Firstly, the ultrasonic was beneficial to improving material flow and atom diffusion, and then eliminated kissing bond defects compared to conventional A-PFFSR joints. Secondly, the equiaxed grains were refined by ultrasonic vibration. Lastly, the repairing passes were reduced due to the ultrasonic, which decreased softening degree of the repaired joints. The maximum tensile strength of 150 MPa was achieved. Therefore, this strategy to repair the volume defects is feasibility and potential in the remanufacturing fields of aerospace and transportation.
Twórcy
autor
  • Luoyang Ship Material Research Institute, Luoyang 471023, P. R. China
autor
  • Shenyang Aerospace University, College of Aerospace Engineering, Shenyang 110136, P. R. China
autor
  • Shenyang Aerospace University, College of Aerospace Engineering, Shenyang 110136, P. R. China
autor
  • Luoyang Ship Material Research Institute, Luoyang 471023, P. R. China
autor
  • Shenyang Aerospace University, College of Aerospace Engineering, Shenyang 110136, P. R. China
Bibliografia
  • [1] R. Zettler, T. Donath, J.F. Dos Santos, F. Beckman, D. Lohwasser. Adv. Eng. Mater. 8 (6), 487-490 (2006). doi:10.1002/adem.200600062
  • [2] R. Zettler, A.A.M. Da Silva, S. Rodrigues, A. Blanco, J.F. Dos Santos. Adv. Eng. Mater. 8 (5), 415-421 (2006). doi:10.1002/adem.200600030
  • [3] B. He, L. Cui, D.P. Wang, H.J. Li, C.X. Liu. Acta Metall. Sin. (English Lett. 2019 (2019). doi:10.1007/s40195-019-00951-x
  • [4] G. Wang, Y. Zhao, Y. Hao. J. Mater. Sci. Technol. 34 (1), 73-91 (2017). doi:10.1016/j.jmst.2017.11.041
  • [5] X. Meng, Y. Jin, S. Ji, D. Yan. J. Mater. Sci. Technol. 34 (10) (2018). doi:10.1016/j.jmst.2018.02.022
  • [6] G.K. Padhy, C.S. Wu, S. Gao. J. Mater. Sci. Technol. 34, 1-38 (2017). doi:10.1016/j.jmst.2017.11.029
  • [7] W.F. Xu, Y.X. Luo, M.W. Fu. Mater. Charact. 138, 48-55 (2018). doi:10.1016/j.matchar.2018.01.051
  • [8] Z. Liu, S. Ji, X. Meng, Z. Li. Can. Metall. Q. 57 (2), 181-185 (2018). doi:10.1080/00084433.2017.1412555
  • [9] F. Acerra, G. Buffa, L. Fratini, G. Troiano. Int. J. Adv. Manuf. Technol. 48 (9-12), 1149-1157 (2010). doi:10.1007/s00170-009-2344-9
  • [10] X. Zhang, Z.P. Cano, B. Wilson, J.R. McDermid, J.R. Kish. Can. Metall. Q. 56 (3), 308-321 (2017). doi:10.1080/00084433.2017.1327500
  • [11] C. Gunter, M.P. Miles, F.C. Liu, T.W. Nelson. J. Mater. Sci. Technol. 34 (1), 140-147 (2017). doi:10.1016/j.jmst.2017.10.023
  • [12] S. Ji, X. Meng, L. Ma, H. Lu, S. Gao. Mater. Des. 68 (2015). doi:10.1016/j.matdes.2014.12.009
  • [13] S. Ji, X. Meng, J. Xing, L. Ma, S. Gao. High Temp. Mater. Process. 35 (8), 843-851 (2016). doi:10.1515/htmp-2015-0063
  • [14] H. Liu, H. Zhang. Trans. Nonferrous Met. Soc. China. 19 (3), 563-567 (2009). doi:10.1016/S1003-6326(08)60313-1
  • [15] D.F. Metz, M.E. Barkey. Int. J. Fatigue. 43, 178-187 (2012). doi:10.1016/j.ijfatigue.2012.04.002
  • [16] Y.C. Lim, L. Squires, T.Y. Pan, ... Z. Feng. Mater. Des. 69, 37-43 (2015). doi:10.1016/j.matdes.2014.12.043
  • [17] Y.X. Huang, B. Han, S.X. Lv, ... Y. Li. Sci. Technol. Weld. Joi. 17 (3), 225-230 (2012). doi:10.1179/1362171811Y.0000000100
  • [18] B. Han, Y. Huang, S. Lv, L. Wan, J. Feng, G. Fu. Mater. Des. 51, 25-33 (2013). doi:10.1016/j.matdes.2013.03.089
  • [19] Y.X. Huang, B. Han, Y. Tian, ... Y. Li. Sci. Technol. Weld. Joi. 16 (6), 497-501 (2011). doi:10.1179/1362171811Y.0000000032
  • [20] S.D. Ji, X.C. Meng, R.F. Huang, L. Ma, S.S. Gao. Mater. Sci. Eng. A. 664, 94-102 (2016). doi:10.1016/j.msea.2016.03.131
  • [21] S. Ji, X. Meng, Y. Zeng, L. Ma, S. Gao. Mater. Des. 97, 175-182 (2016). doi:10.1016/j.matdes.2016.02.088
  • [22] R. Huang, S. Ji, X. Meng, Z. Li. J. Mater. Process Technol. 255, 765-772 (2018). doi:10.1016/j.jmatprotec.2018.01.019
  • [23] S. Niu, B. Wu, L. Ma, Z. Lv, D. Yan. d, 2461-2468 (2018).
  • [24] Z. Liu, X. Meng, S. Ji, Z. Li, L. Wang. J. Manuf. Process. 31, 552-559 (2018). doi:10.1016/j.jmapro.2017.12.022
  • [25] S. Ji, X. Meng, Z. Liu, R. Huang, Z. Li. Mater. Lett. 201, 173-176 (2017). doi:10.1016/j.matlet.2017.05.011
  • [26] X.C. Liu, C.S. Wu. Mater. Des. 90, 350-358 (2016). doi:10.1016/j.matdes.2015.10.131
  • [27] G.K. Padhy, C.S. Wu, S. Gao. Sci. Technol. Weld. Joi. 20 (8), 631-649 (2015). doi:10.1179/1362171815Y.0000000048
  • [28] Z. Ma, Y. Jin, S. Ji, X. Meng, L. Ma, Q. Li. J. Mater. Sci. Technol. 35 (1), 94-99 (2019). doi:10.1016/j.jmst.2018.09.022
  • [29] M. Thomä, G. Wagner, B. Straß, B. Wolter, S. Benfer, W. Fürbeth. J. Mater. Sci. Technol. 34 (1), 163-172 (2017). doi:10.1016/j.jmst.2017.10.022
  • [30] S. Ji, S. Niu, J. Liu, X. Meng. J. Mater. Process Technol. 2019 (2019). doi:10.1016/j.jmatprotec.2018.12.010
  • [31] X.C. Liu, C.S. Wu. J. Mater. Process Technol. 225, 32-44 (2015). doi:10.1016/j.jmatprotec.2015.05.020
  • [32] W. Li, J. Li, Z. Zhang, D. Gao, W. Wang, C. Dong. Mater. Des. 62, 247-254 (2014). doi:10.1016/j.matdes.2014.05.028
  • [33] S.D. Ji, X.C. Meng, L. Ma, S.S. Gao. Int. J. Adv. Manuf. Technol. 87 (9-12), 3051-3058 (2016). doi:10.1007/s00170-016-8734-x
  • [34] Y. Huang, X. Meng, Y. Xie, J. Li, L. Wan. Compos. Part A, Appl. Sci. Manuf. 112 (April), 328-336 (2018). doi:10.1016/j.compositesa.2018.06.027
  • [35] M. Guan, Y. Wang, Y. Huang, J. Li. Mater. Lett. 255, 126506 (2019). doi:10.1016/j.matlet.2019.126506
Uwagi
1. This work is supported by the National Natural Science Foundation of China (No. 51705339).
2. Opracowanie rekordu ze środków MNiSW, umowa Nr 461252 w ramach programu "Społeczna odpowiedzialność nauki" - moduł: Popularyzacja nauki i promocja sportu (2021).
Typ dokumentu
Bibliografia
Identyfikator YADDA
bwmeta1.element.baztech-8361c13a-61a9-41d1-a25e-ab43a27c1d2a
JavaScript jest wyłączony w Twojej przeglądarce internetowej. Włącz go, a następnie odśwież stronę, aby móc w pełni z niej korzystać.