The Effect of Silicon Orientation on Thickness and Chemical Bonding Configuration of SiOxNy Thin Films

Autorzy
Treść / Zawartość
Identyfikatory
Warianty tytułu
Języki publikacji
EN
Abstrakty
EN
Fourier Transform Infrared (FTIR) Spectroscopy and Capacitance-Voltage measurements are used to characterize the chemical bonding configuration and crystallographic orientations for SiOxNy thin films grown by glass assisted CO2 laser. FTIR spectra detected the Si-O and Si-N strongest absorption bands are close to each other at wave number in the range (700-1000 cm-1) depending on silicon substrates, and Si-O stretching bond at wave number around (~1088.285 cm-1) with a FWHM of 73.863 cm-1 for the two samples, the presences of hydrogen impurities like Si-H and N-H in the films were also identified and calculated. From C-V measurement film thickness were calculated and found to be 19.2 and 17.2 nm for SiOxNy/Si(111) and SiOxNy/Si(100) respectively. From the flat band voltage of -5.4 and -1.3 measured the two samples, their interface trap densities were found to be 1.4 × 1013 and 1.57 × 1013 ev-1•cm-2 respectively.
Rocznik
Tom
Strony
1--9
Opis fizyczny
Bibliogr. 22 poz., rys., tab.
Twórcy
autor
  • Physics Department, College of Science, University of Salahaddin, Erbil, Kurdistan, Iraq
Bibliografia
  • [1] N. Konofaos, E. K. Evangelou, Sci. Technol. 18 (2003) 56-59.
  • [2] F. Rebib, E. Tomasella, M. Dubois, J. Cellier, T. Sauvage, M. Jacquet, Thin solid films 515 ( 2007) 3480-3487.
  • [3] F. Rebib, E. Tomasella, V. Micheli, C. Eypert, J. Cellier, N. Laidani, Opt. Mater. 31 (2009) 510-513.
  • [4] M. Bedjaoui, B. Despax, Thin solid film 518 (2010) 4142-4149.
  • [5] F. Rrebib, E. Tomasella, V. Micheli, C. Eypert, J. Cellier, N. Laidani, Opt. Mater. 31 (2009) 510-513.
  • [6] S. H. Mohamed, Physica B 406 (2011) 211-215.
  • [7] Y. Liu, I. K. Lin, X. Zhang, Mat. Sci. Engineering A 489 (2008) 294-301.
  • [8] D. V. Tsu, G. Lucovsky, M. J. Mantini, Phys. Rev. B 33 (1986) 7069-7076.
  • [9] J. A. Diniz, P. J. Tatsch, M. A. A. Pudenzi, Appl. Phys. Lett. 69 (1996) 2214-2215.
  • [10] T. Maruyma, T. Shirai, Appl. Phys. Lett. 63 (1993) 611-613.
  • [11] V. P. Tolstoy, I. V. Chernyshova, V. A. Skryshevsky, Hand book of infrared spectroscopy of ultra thin films, A John , Wiley and Sons, Inc., (2003).
  • [12] W. L. Scopel, M. C. A. Fantini, M. I. Alayo, I. Pereyra, Thin Solid Films 413 (2002) 59-64.
  • [13] F. Giorgis, C. F. Pirri, E. Tresso, Thin Solid Films 307 (1997) 298-305.
  • [14] R. K. Pandey, L. S. Patil, J. P. Bange, D. R. Patil, A. M. Ahajan, D. S. Patil, D. K. Gautam, Opt. Mater. 25 (2004) 1-7.
  • [15] L. S. Patil, R. K. Pandey, J. P. Bange, S. A. Gaikwad, D. K. Gautam, Opt. Mater. 27 (2005) 663-670.
  • [16] H. J. Schliwinski, U. Schnakenberg, W. Windbrache, H. Neff, P. Lange, J. Electrochem. Soc. 139 (1992) 1730-1735.
  • [17] J. X. Zhang, H. Cheng, Y. Z. Chen, A. Uddin, Shu Yuan, S. J. Geng, S. Zhang, Surface and coating technology 198 (2005) 68-73.
  • [18] D. K. Schroder, Semiconductor Material and Device Characterization, John-Wiley & Sons, Inc. (NJ, USA) (2006), Ch.6, 328.
  • [19] S. M. Sze, K. K. Ng, Physics of Semiconductor Devices, 3rd ed., John Willy Sons Inc., (2007).
  • [20] E. H. Nicollian, J. R. Brews, MOS (Metal Oxide Semiconductor) Physics and Technology, John Wiley and Sons, (2003).
  • [21] M. M. Ismael, Characteristics of SiOxNy Thin Films Prepared by CO2 Laser, Msc. Thesis, Salahaddin University-Erbil, (2010).
  • [22] S. M. Sze, Physics of Semiconductor Devices, second ed.,Wiley/Interscience, New York, (1981)
Typ dokumentu
Bibliografia
Identyfikator YADDA
bwmeta1.element.baztech-7f6c119c-7831-4304-9816-b5769f4d4de9
JavaScript jest wyłączony w Twojej przeglądarce internetowej. Włącz go, a następnie odśwież stronę, aby móc w pełni z niej korzystać.