Experimental investigations into foaming of biodegradable polymers using scCO2

Wybrane pełne teksty z tego czasopisma
Identyfikatory
Warianty tytułu
PL
Badania doświadczalne spieniania biodegradowalnych polimerów przy użyciu CO2 w stanie nadkrytycznym
Języki publikacji
EN
Abstrakty
EN
Results of experimental investigations of batch foaming of poly(ε-caprolactone) using scCO2 are presented in the paper. The high pressure system consisting of CO2 cylinder, scCO2 pump, high pressure cell, pressure and temperature gauge and back pressure regulator was applied in the experiments. The porous three-dimensional solid-gas structures were prepared for the following range of process parameters: temperature 298+373 K, pressure 8+18 MPa, time 1+4 h and depressurization rate 0.007+4 MPa/s. The significant influence of process parameters on the obtained foams morphology was identified.
PL
W pracy przedstawiono wyniki badań doświadczalnych procesu spieniania polikaprolaktonu (PCL) przy użyciu CO2 w stanie nadkrytycznym. Badania przeprowadzono w instalacji złożonej z butli CO2, pompy do płynów nadkrytycznych, komory wysokociśnieniowej, miernika ciśnienia i temperatury oraz regulatora ciśnienia wstecznego. Badania wykonano dla zakresu zmienności parametrów operacyjnych: temperatura: 398÷373 K, ciśnienie: 8÷18 MPa, czas nasycania: 1÷4 h, szybkość dekompresji: 0,007÷4 MPa/s. Wykazano silny wpływ warunków realizacji procesu spieniania na strukturę wytwarzanych pian.
Rocznik
Tom
Strony
40--41
Opis fizyczny
Bibliogr. 5 poz., rys., tab.
Twórcy
autor
  • Faculty of Chemical and Process Engineering, Warsaw University of Technology, Warsaw
autor
  • Faculty of Chemical and Process Engineering, Warsaw University of Technology, Warsaw
Bibliografia
  • 1. Duarte A.R.C., Mano J.F., Reis R.L., (2009). Perspectives on: Supercritical fluid technology for 3D tissue engineering scaffold applications. J. Bioactive Comp. Polym., 24, 385-400, DOI: 10.1177/0883911509105796
  • 2. Gloria A., Causa F., Russo T., Battista E., Della Moglie R., Zeppetelli S., De Santis R., Netti P.A., Ambrosio L., (2012). Three-dimensional poly(ε-caprolactone) bioactive scaffolds with controlled structural and surface properties. Biomacromolecules, 13(11), 3510-3521. DOI:10.1021/bm300818y
  • 3. Jenkins M.J., Harrison K.L., Silva M.M.C.G., Whitaker M.J., Shakesheff K.M., Howdle S.M., (2006). Characterisation of microcellular foams produced from semi-crystalline PCL using supercritical carbon dioxide. Eur. Polymer J., 42, 3145-3151. DOI:10.1016/j.eurpolymj.2006.07.022
  • 4. Karimi M., Heuchel M., Weigel T., Schossig M., Hofmann D., Lendlein A., (2012). Formation and size distribution of pores in poly(ε-caprolactone) foams prepared by pressure quenching using supercritical CO2. J. Supercrit. Fluids, 61, 175-190, DOI:10.1016/j.supflu.2011.09.022
  • 5. Salerno A., Di Maio E., Iannace S., Netti P.A., (2011), Solid-state supercritical CO2 foaming of PCL and PCL-HA nano-composite: Effect of composition, thermal history and foaming process on foam pore structure. J. Supercrit. Fluids, 58, 158-167. DOI:10.1016/j.supflu.2011.05.009
Uwagi
Opracowanie ze środków MNiSW w ramach umowy 812/P-DUN/2016 na działalność upowszechniającą naukę (zadania 2017).
Typ dokumentu
Bibliografia
Identyfikator YADDA
bwmeta1.element.baztech-7ec5ebe4-b9ac-4467-9ad2-858523920766
JavaScript jest wyłączony w Twojej przeglądarce internetowej. Włącz go, a następnie odśwież stronę, aby móc w pełni z niej korzystać.