Diffusion and laser boriding of Hardox 450 steel

• Autorzy: Kapcińska-Popowska D. , Pertek-Owsianna A. , Bartkowska A.

Warianty tytułu

PL

Borowanie dyfuzyjne i laserowe stali Hardox 450

• Języki publikacji: EN

Abstrakty

EN

The effect of diffusion and laser boriding on the microstructure, microhardness and wear resistance of Hardox 450 steel compared to initial state is the subject of this article. After the boron modification process of Hardox 450 steel microhard-ness and wear resistance increased. After the diffusion boriding a needle-like microstructure of microhardness about 1800-1500 HV0.1 was obtained. As a result of laser boronizing the microstructure consisted of a remelted zone (MZ), heat-affected zone (HAZ) and core. In the remelted zone enriched of boron microhardness was about 1500-1600 HV0.1 The wear resistance tests showed the higher wear resistance of the diffusion borided layers, whereas the lower were in initial state but the lowest was for laser borided layer.

PL

W pracy przedstawiono wpływ borowania dyfuzyjnego i laserowego na mikrostrukturę, mikrotwardość oraz odporność na zużycie przez tarcie stali Hardox 450 w porównaniu do stali w stanie wyjściowym. Po procesie modyfikacji stali Hardox 450 borem uzyskano zwiększenie mikrotwardości i odporności na zużycie przez tarcie. W wyniku procesu borowania dyfuzyjnego warstwa miała iglastą strukturę o mikrotwardości ok. 1800-1500 HV0,1. Natomiast w wyniku borowania laserowe-go uzyskano budowę strefową składającą się ze strefy przetopionej, strefy wpływu ciepła oraz rdzenia. W strefie przetopionej wzbogaconej w bor mikrotwardość wynosiła ok. 1500-1600 HV0,1. Badania odporności na zużycie przez tarcie wykazały, że najlepszą odporność posiada warstwa borowana dyfuzyjnie, natomiast mniejszą stal w stanie wyjściowym a najmniejszą warstwa borowana laserowo.

Słowa kluczowe

EN

diffusion boriding; laser boriding; microstructure; microhardness; wear resistance

PL

borowanie dyfuzyjne; borowanie laserowe; mikrostruktura; mikrotwardość; odporność; zużycie przez tarcie

• Wydawca: Sieć Badawcza Łukasiewicz - Poznański Instytut Technologiczny
• Czasopismo: Journal of Research and Applications in Agricultural Engineering
• Rocznik: 2015
• Tom: Vol. 60, nr 2
• Strony: 40--42
• Opis fizyczny: Bibliogr. 9 poz., rys., wykr.

Twórcy

autor

Kapcińska-Popowska D.

• Industrial Institute of Agricultural Engineering, ul. Starołęcka 31, 60-963 Poznań, Poland

autor

Pertek-Owsianna A.

• Poznan University of Technology, Institute of Materials Science and Engineering, Poznań, Poland

autor

Bartkowska A.

• Poznan University of Technology, Institute of Materials Science and Engineering, Poznań, Poland

Bibliografia

• [1] Kula P.: Inżynieria warstwy wierzchniej. Łódź: Wydawnictwo Politechniki Łódzkiej, 2000.
• [2] Bartkowska A., Pertek-Owsianna A., Przestacki D.: Hartowanie i borowanie laserowe stali konstrukcyjnej C45. Inżynieria Materiałowa, 2013, nr 6, 610-614.
• [3] Wiśniewski K., Pertek-Owsianna A.: Struktura i właściwości stali konstrukcyjnej borowanej laserowo. Inżynieria Powierzchni, 2009, nr 2, 84-88.
• [4] Pertek-Owsianna A., Wiśniewski K.: Właściwości konstrukcyjne borowanej stali konstrukcyjnej. Inżynieria Powierzchni, 2007, nr 3, 75-78.
• [5] Pertek-Owsianna A., Kulka M., Jankowiak M.: Badania struktury i właściwości borowanej stali konstrukcyjnej 41Cr4 i narzędziowej 102Cr6. Archiwum Technologii Maszyn i Automatyzacji, 2006, vol. 26, nr 1, 167-176.
• [6] Pertek-Owsianna A.: Borowanie dyfuzyjne i laserowe części maszyn i narzędzi. Inżynieria Powierzchni, 2010, nr 4, 28-34.
• [7] Kusiński J.: Lasery i ich zastosowanie w inżynierii materiałowej. Kraków: Wydawnictwo Naukowe „Akapit”, 2000.
• [8] Pertek-Owsianna A., Kapcińska-Popowska D., Bartkowska A., Wiśniewski K.: Wpływ borowania dyfuzyjnego i laserowego na mikrostrukturę i wybrane właściwości stali Hardox 450. Inżynieria Materiałowa, 2013, nr 5(195), 530-533.
• [9] Kapcińska-Popowska D., Pertek-Owsianna A., Bartkowska A., Bartkowski D., Przestacki D.: Influence of diffusion boriding and laser boriding on corrosion resistance Hardox 450 steel. Journal of Research and Applications in Agricultural Engineering, 2014, vol. 59(2), 40-45.