Szerardyzacja, jako zabezpieczenie antykorozyjne części złącznych : badania wstępne

Wybrane pełne teksty z tego czasopisma
Identyfikatory
Warianty tytułu
EN
Sherardizing as the anticorrosion protection of fasteners : preliminary research
Języki publikacji
EN PL
Abstrakty
EN
In the paper the corrosion resistance of the fasteners - M10 screws and flat samples made of 23MnB4 steel were compared after hot-dip and thermal diffusion galvanizing (sherardizing). Corrosion examinations were conducted in a salt spray chamber, in the neutral NaCl fog (according to PN-EN ISO 9227). The achieved results were compared to these which was determinated in analogous conditions for the samples after galvanizing and protected by lamellar zinc coating. In order to explain the diversity of determined and literature corrosion resistance of thermal diffusion coating, on the cross section and the outside surface of the thermal diffusion coating (and hot-dip galvanizing – for comparison) microscopic observation was conducted using the scanning microscope and EDS analysis. The performed examinations showed, that fasteners after sherardizing reveal the lowest corrosion resistance amongst compared methods inside the examined environment. Achieved results are a consequence of both the too small thickness, and the improper structure of the coating and to its improvement an optimization of process parameters is necessary.
PL
W pracy porównano odporność korozyjną części złącznych – śrub M10 oraz próbek płaskich, wykonanych ze stali 23MnB4, cynkowanych ogniowo oraz termodyfuzyjnie (szerardyzacja). Badania korozyjne prowadzono w komorze solnej, w obojętnej mgle NaCl (wg PN-EN ISO 9227). Uzyskane wyniki porównano do tych, jakie otrzymano w analogicznych warunkach dla części zabezpieczanych antykorozyjnie poprzez cynkowanie galwaniczne i naniesienie lamelowej warstwy cynku. W celu wyjaśnienia zróżnicowania wyznaczonej i literaturowej odporności korozyjnej powłoki termodyfuzyjnej, na przekroju i powierzchni zewnętrznej powłoki termodyfuzyjnej (oraz ogniowej – dla porównania) przeprowadzono obserwacje mikroskopowe przy zastosowaniu mikroskopu skaningowego oraz analizę EDS. Wykonane badania wykazały, że szerardyzowane części złączne charakteryzują się najmniejszą wśród porównywanych metod odpornością korozyjną w badanym środowisku. Otrzymane wyniki są konsekwencją zarówno zbyt małej grubości, jak i niewłaściwej struktury naniesionej powłoki i w celu ich poprawy niezbędna jest optymalizacja parametrów procesu cynkowania.
Rocznik
Tom
Strony
59--64
Opis fizyczny
Bibliogr. 12 poz., rys., tab., wykr.
Twórcy
  • Akademia Techniczno-Humanistyczna
autor
  • Akademia Techniczno-Humanistyczna
Bibliografia
  • [1] Alvey C.E. 2002. “Evaluation of Distek Thermodiffusion Coating”. Corrosion Advisory Technical Services.
  • [2] Evans D.W. 2014. “Next generation technology for corrosion protection in ground support elements”. Coal Operators’ Conference, 12-14 February 2014, The University of Wollongong, Northfields Ave, Australia.
  • [3] Jeffrey R. 2010. “Evaluation of Corrosion Resistance of Mining Products”. Pacific Testing.
  • [4] Jiang J.H., A.B. Ma, X.D. Fan, M.Z. Gong, L.Y. Zhang. 2010. “Sherardizing and Characteristic of Zinc Protective Coating on High-Strength Steel Bridge Cable Wires”. Advanced Materials Research 97 (101) : 1368–1372.
  • [5] Kenhong T., G. Lothongkum, Y. Boonyongmaneerat. 2014. “Influence of Hot-dip Coatings on Mechanical and Corrosion Behaviors of Steel Bolts 2”. Journal of Metals, Materials and Minerals 24 (2) : 49–53.
  • [6] PN-EN ISO 17668:2016-04 – wersja angielska Cynkowe powłoki dyfuzyjne na wyrobach stalowych – Szerardyzacja – Specyfikacja.
  • [7] Praca zbiorowa. 2000. “Zinc coatings. Microstructures of various zinc coatings”. Englewood: American Galvanizers Association.
  • [8] Raport firmy HILTI. 2010. Corrosion aspects of fastening systems.
  • [9] Surowska B. 2002. Wybrane zagadnienia z korozji i ochrony przed korozją. Lublin.
  • [10] Szłapa I.: „Wpływ korozji na wybrane właściwości mechaniczne elementow złącznych – porownanie antykorozyjnych właściwości powłok cynkowych”. Praca Doktorska, WBMiI ATH Bielsko-Biała, w przygotowaniu.
  • [11] Tatarek A., P. Liberski, H. Kania. 2008. „Porownawcze badania odporności korozyjnej powłok cynkowych otrzymywanych rożnymi metodami”. Ochrona przed Korozją 51 (4–5) : 131–134.
  • [12] Wienstroer S., M. Fransen, H. Mittelstadt, M. Nazikkol, M. Volker. 2003. “Zinc/iron phase transformation studies on galvannealed steel coatings by X-ray diffraction”. Advance in X-ray Analysis 46 : 291–296.
Uwagi
Opracowanie ze środków MNiSW w ramach umowy 812/P-DUN/2016 na działalność upowszechniającą naukę (zadania 2017).
Typ dokumentu
Bibliografia
Identyfikator YADDA
bwmeta1.element.baztech-7c8e4ca6-5718-42ce-b456-f8e2bbc790c4
JavaScript jest wyłączony w Twojej przeglądarce internetowej. Włącz go, a następnie odśwież stronę, aby móc w pełni z niej korzystać.