Copper Leaching from Chalcopyrite: Mechanochemical Approach

• Autorzy: Tesinsky M. , Balaz P.

Warianty tytułu

EN

Ługowanie miedz z chalkopirytu – aspekt mechaniczny i chemiczny

• Języki publikacji: EN

Abstrakty

EN

In the presented work, possibilities of intensification of copper leaching from chalcopyrite CuFeS2 induced by mechanical activation was studied. In this article, the influence of mechanical activation time on copper leaching efficiency is compared. This study also shows how mechanical activation time influences selectivity of copper and iron leaching. For mechanical activation, planetary mill Fritsch Pulverisette 6 at 400 rpm and room temperature was used. Grinding chamber (250 cm3 in volume) and 50 balls (10 mm in diameter) made of tungsten carbide were used. Specifically, the effect of mechanical activation time (4, 20, 30 minutes), the effect of temperature (40, 60, 80°C) on the copper recovery by leaching and the effect of the leaching atmosphere (air, argon) were examined. The results showed that the highest possible recovery of copper from chalcopyrite was obtained after 20 minutes of milling and leached in hydrochloric acid at 80°C, with air atmosphere without any oxidizing reagents.

PL

W artykule przedstawiono możliwości intensyfikacji procesu ługowania miedzi z chalkopirytu CuFeS2 za pomocą aktywacji mechanicznej. Zbadano wpływ czasu aktywacji mechanicznej na efektywność ługowania miedzi. Wyniki badań pokazały również wpływ czasu na selektywność rozdziału miedzi i żelaza. Do aktywacji mechanicznej wykorzystani młyn planetarny Fritsch Pulverisette 6, aktywację prowadzono przy obrotach 400 rpm, w temperaturze pokojowej. Do badan wykorzystano komorę mielenia o objętości 250 cm3 i 50 kul o średnicy 10 mm wykonanych z węglika wolframu. Określono wpływ czasu aktywacji mechanicznej (4, 20, 30 minut), wpływ temperatury (40, 60, 80°C) na odzysk miedzi w procesie lugowania w atmosferze powietrza i argonu. Wyniki wskazują, że najwyższy możliwy odzysk miedzi z chalkopirytu uzyskano po 20 minutach mielenia i ługowaniu w kwasie solnym w temperaturze 80°C, w atmosferze powietrza, bez jakichkolwiek czynników utleniających.

Słowa kluczowe

EN

milling; mechanical activation; leaching; chalcopyrite

PL

mielenie; aktywacja mechaniczna; ługowanie; chalkopiryt

• Wydawca: Polskie Towarzystwo Przeróbki Kopalin
• Czasopismo: Inżynieria Mineralna
• Rocznik: 2017
• Tom: R. 18, nr 1
• Strony: 1--5
• Opis fizyczny: Bibliogr. 13 poz., tab.

Twórcy

autor

Tesinsky M.

• Institute of Geotechnics of SAS, Watsonova 45, 04353 Košice, Slovak Republic

autor

Balaz P.

• Institute of Geotechnics of SAS, Watsonova 45, 04353 Košice, Slovak Republic

Bibliografia

• 1. Balaz P., 2000. Extractive metallurgy of activated minerals. Elsevier, Amsterdam
• 2. Habashi F., 1978. Chalcopyrite : Its chemistry and metallurgy. Mc Graw Hill, New York
• 3. Kawashima Y.,Li J.,Chandra A.P.,Gerson, A.R.,2013.A review of the structure, and fundamental mechanisms and kinetics of leaching of chalcopyrite. Advances in Colloid and Interface Science 197-198,1-32
• 4. Cordoba E.M., Munoz J.A., Blazquez M.L., Gonzalez F., Baller A., 2008. Leaching of chalcopyrite with ferric ion. Part 1 : General aspects. Hydrometallurgy 93, 81-87
• 5. Dreisinger, D., 2006. Copper leaching from primary sulphides ; options for biological and chemical extraction of copper. Hydrometallurgy 83, 10-20
• 6. Lu J., Dreisinger, D.,2013. Copper leaching from chalcopyrite concentrate in Cu(II)/Fe(III) chloride system. Minerals Engineering 45,185-190
• 7. Havlik T., 1997. Non-traditional ways and innovation technologies in hydrometallurgy. Acta Montanistica Slovaca, 2,247-251
• 8. Dutrizac J.E., 1992. The leaching of sulphide minerals in chloride media. Hydrometallurgy 29, 1-45
• 9. Turan,M.D.2014. Direct selective leaching of chalcopyrite concentrate. Canadian Metallurgical Quarterly 53,444-449
• 10. Garlapalli R., Cho E., Ray Y., 2010. Leaching of Chalcopyrite with Sodium Hypochlorite. Metallurgical & Materials Transactions B, 41, 308-317
• 11. Balaz P., 2008. Mechanochemistry in Nanoscience and Minerals Engineering. Springer, Berlin Heidelberg
• 12. Chagas Almeida T., Marsalha Garcia E., Alves da Silva H.W., Matencio T.,Cunha Lins V.F., 2016. Electrochemical study of chalcopyrite dissolution in sulfuric, nitric and hydrochloric acid solutions. International Journal of Mineral Processing, 149, 25-33
• 13. Tkacova K., Balaz P., 1988. Structural and temperature sensitivity of leaching of chalcopyrite with iron(III) sulphate. Hydrometallurgy 21, 103-1127.

Uwagi

Opracowanie ze środków MNiSW w ramach umowy 812/P-DUN/2016 na działalność upowszechniającą naukę (zadania 2017).