Evaluation of micro-geometry changes on surfaces after chemical pretreatment

• Autorzy: Draganovská D. , Tomáš M. , Ižol P

Warianty tytułu

PL

Ocena zmian mikrogeometrii powierzchni po obróbce chemicznej

• Języki publikacji: EN

Abstrakty

EN

The paper discusses the evaluation of the surface quality in terms of microgeometry. For the experiment, samples of S235JRG2 steel were used. The surface of the steel was chemically pretreated prior to the tests. Thefocus of the research was on the surfaces of steel sheets in states such as an initial state surface, degreased surface, galvanized surface, a surface after galvanizing and chromatizing, degreased and phosphated, and a surface pretreated with degreasing and phosphating with RAL coating. The measurement of microgeometry parameters on the samples was evaluated by a profilometric device Surftest SJ – 201, Mitutoyo, Japan. The roughness parameters Ra, Rz, RSm, and RPc, were measured on evaluated surfaces and compared. Profilographs, as well as Abbot Fireston curves were also evaluated.

PL

W artykule oceniono jakość powierzchni z punktu widzenia mikrogeometrii. W badaniach wykorzystano próbki ze stali S235JRG2. Powierzchnie badanych próbek poddano różnym zabiegom obróbki chemicznej. W badaniach przeanalizowano próbki w stanie początkowym oraz po procesach: odtłuszczania, galwanizacji, galwanizacji i chromowania, odtłuszczania i galwanizacj odtłuszczania i galwanizacji z powłoką RAL. Parametry mikrogeometrii powierzchni zmierzono za pomocą stykowego profilografometru Surftest SJ-201 Mitutoyo. Na podstawie pomiarów wyznaczono parametry chropowatości powierzchni Ra, Rz, RSm i RPc badanych próbek, a następni dokonano ich porównania. Analizie poddano również profilogramy i krzywe Abbotta-Firestone’a.

Słowa kluczowe

EN

galvanized surfaces; roughness parameters; chemical pretreatment

PL

powierzchnie galwanizowane; parametry chropowatości; obróbka chemiczna

• Wydawca: Wydawnictwo Politechniki Poznańskiej
• Czasopismo: Archives of Mechanical Technology and Automation
• Rocznik: 2014
• Tom: Vol. 34, no. 2
• Strony: 17--24
• Opis fizyczny: Bibliogr. 12 poz., rys.

Twórcy

autor

Draganovská D.

• Faculty of Mechanical Engineering, Technical University in Košice, Slovakia

autor

Tomáš M.

• Faculty of Mechanical Engineering, Technical University in Košice, Slovakia

autor

Ižol P

• Faculty of Mechanical Engineering, Technical University in Košice, Slovakia

Bibliografia

• [1] Autengruber R. et al., Surface and eoating analysis of press-hardened hot-dip galvanized teel sheet, Steel Research International, 2012, vol. 83, no. 11, p. 1005-1011.
• [2] Bumbálek B., Odvody V., Ostadal B., Drsnost povrchu. 1. vyd., Praha 1989.
• [3] Cabanelas I. et al., Influence of galvanised surface state on the duplex systems behaviour, Corrosion Science, 2007, vol. 49, no. 4, p. 1816-1832.
• [4] Draganovská D., Analýza procesu tvorby a vlastností nových povrchov, získaných technológiou tryskania, DDP, TU Košice 2005.
• [5] Królczyk G., Raos P., Legutko S., Experimental analysis of surface roughness and surface texture, Technički vjesnik, 2014, vol. 21, no. 1, p. 217-221.
• [6] Lajmert P., Ležanski P., Monitoring of the cylindrical plunge grinding process, Archives of Mechanical Technology and Automation, 2013, vol. 33, no. 3, p. 3-15.
• [7] Lu L. et al., Relationship between distinctness of image of organic coatings and texture of substrate sheets, Surface Engineering, 2011, vol. 27, no. 7, p. 515-518.
• [8] Payen G.R. et al., Influence of contact pressure and boundary films on the frictional behaviour and on the roughness changes of galvanized Steel sheets, Wear, 2012, vol. 276-277, p. 48-52.
• [9] Sedláček V., Povrchy a povlaky kovu, Praha, ČVUT 1992.
• [10] STN EN ISO 4287:1999 Geometrické špecifikácie výrobkov (GPS) Charakter povrchu: Profilová metóda - Termíny, defimcie a parametre charakteru povrchu.
• [11] Wichern C.M., de Cooman B.C., van Tyne C.J., Surface roughness changes on a ho -dipped galvanized sheet Steel during deformation at Iow strain levels, Acta Materialia, 200-vol. 52, no. l,p. 1211-1222.
• [12] Wichern C.M., de Cooman B.C., van Tyne C.J., Surface roughness of a hot-dipped galvanized sheet Steel as a function of deformation mode, Journal of Materials Processir Technology, 2005, vol. 160, no. 3, p. 278-288.