The influence of silica module of the soluble sodium silicate hardened by ester on the residual strenght of molding sand

• Autorzy: Baliński A.
• Języki publikacji: EN

Abstrakty

EN

Describes how to obtain a soluble sodium silicate with a density of 1.40 g/cm3, 1.45 g/cm3, 1.50 g/cm3, and silica module M = 2.1 obtained from the silica- sodium glass with module M = 3.3 and M = 2.1. Residual (final) strength of molding samples made with these binders, were determined at temperatures corresponding to the characteristic temperatures of phase and temperature transitions of silica gel. Indicated the type of soluble sodium silicate capable of obtain the smallest value of the final strength of molding sand in the specified range of temperatures.

Słowa kluczowe

EN

soluble sodium silicate; silica gel; residual strength

PL

uwodniony krzemian sodu; żel krzemionkowy; wytrzymałość resztkowa

• Wydawca: Komisja Odlewnictwa Polskiej Akademii Nauk Oddział w Katowicach
• Czasopismo: Archives of Foundry Engineering
• Rocznik: 2013
• Tom: Vol. 13, iss. 1
• Strony: 131--133
• Opis fizyczny: Bibliogr. 12 poz., tab., wykr.

Twórcy

autor

Baliński A.

• Foundry Research Institute, ul. Zakopiańska 73, 30-418 Kraków, Poland

Bibliografia

• [1] Lewandowski, J.L. (1997). Tworzywa na formy odlewnicze. Kraków: Akapit.
• [2] Żukovski, S.S. (1985). Probliemy procznosti formovocznych smesi. Lit. Proizv. nr 5, s. 5-7.
• [3] Iler, R.K. (1968). The Chemistry of Silica. New York – Chichester- Brisbane – Toronto: John Wiley.
• [4] Iler, R.K. (1959). Kolloidnaja chimia kremniezjema i silikatov, Moskwa: Gostrojizdat.
• [5] Jelinek, P. (1998). Vytvrzovaci procesy smesi s alkalickymi silikaty. In International Conference – Ecological production of castings in the waterglass mixtures, 7 – 10 May 1998 (pp 99 – 102). Zlin, Czechy: VSB.
• [6] Liass, A.M. (1965). Bystrotvierdujussczije formovocznyje smesi. Moskwa: Maszinostrojenije.
• [7] Franek, B., Humpola, J., Burian, A., Kajzarova, M., Jelinek, P., Miksovsky, F. (1998), Vlasnosti smesi s novymi pojivovymi systemy na bazi alkalickych kremicitane a jejich regenerovatelnost. In International Conference – Ecological production of castings in the waterglass mixtures, , 7 – 10 May 1998 (pp 108 – 112). Zlin, Czechy: VSB.
• [8] Schneider, H., Dopp, R. (1991). Einige chemische und strukturelle Untersuchungen zum Wasser-glass – CO2 – Verfahren – Teil 1. Schrifttumsubersicht und ergebnisse struktureller Untersuchungen, Gissereiforschung, no. 1-2, pp.10 - 14.
• [9] Baliński, A., Izdebska-Szanda, I. (2006). The Economical and Ecological Aspects of Using the Modified Water-glass and Fly Ash as an Additive to Green Sands. In 46 Foundry Conference, 7 – 11 September 2006 (pp. 39 – 42). Portoroż, Słowenia: Slovenian Foundrymen Society.
• [10] Baliński, A. (2006). Nanostruktura uwodnionego krzemianu sodu w aspekcie kondycjonowania szkliwa krzemianowo-sodowego. In Komitet Metalurgii PAN (Eds.), Polska Metalurgia w Latach 2002 – 2006, (pp. 281 – 285). Kraków: Akapit.
• [11] Izdebska-Szanda, I., Baliński, A. (2005). Badanie właściwości kohezyjno-adhezyjnych modyfikowanych chemicznie krzemianów sodu. Odlewnictwo – Nauka i Praktyka. Nr 2, s.12 - 14.
• [12] Korzeniowska, M. (2009). Wpływ struktury uwodnionego krzemianu sodu jako spoiwa mas formierskich na właściwości żelu krzemionkowego w wysokich temperaturach. Unpublished doctoral dissertation, AGH University of Science and Technology, Kraków, Poland.