Tribological studies of monolithic drawing dies for the production of reinforcing wires used in construction

• Autorzy: Náprstková Nataša , Kruzel Robert , Dembiczak Tomasz

Identyfikatory

DOI

10.17512/bozpe.2022.11.03

• Języki publikacji: EN

Abstrakty

EN

Cold drawn products are widely used in the construction industry. Drawn products are obtained by a drawing process in which the most important tool is the drawing tool. Drawn products include wire, bar and pipe. The material used in this study was a drawing die mesh made of sintered carbide, grade H10S. The abrasive wear analysis of prepared samples was carried out using the ball on disc method with a ZrO2 ceramic ball. Hardness measurements were carried out using the Vickers method in accordance with the PN-EN 23878:1996 standard. The resistance to brittle fracture was determined based on the length of the measurement of cracks formed at the corners of the impression.

Słowa kluczowe

EN

rebar wires; drawing diesfor; abrasive wear

PL

drut zbrojeniowy; ciągarki; zużycie ścierne

• Wydawca: Wydawnictwo Politechniki Częstochowskiej
• Czasopismo: Budownictwo o Zoptymalizowanym Potencjale Energetycznym
• Rocznik: 2022
• Tom: Vol. 11
• Strony: 23--30
• Opis fizyczny: Bibliogr. 18 poz., rys., tab.

Twórcy

autor

Náprstková Nataša

• University of Jan Evangelista in Ústí nad Labem, Czech Republic

• https://orcid.org/0000-0003-4433-0581

autor

Kruzel Robert

• Czestochowa University of Technology, Poland

• https://orcid.org/0000-0002-8534-7286

autor

Dembiczak Tomasz

• Jan Dlugosz University in Czestochowa, Poland

• https://orcid.org/0000-0003-2751-3749

Bibliografia

• 1.Arato, P., Bartha, R. Berger, S. & Rosen A. (1998) Solid or liquid phase sintering of nanocrystalline WC/Co hardmetals. Nanostructured Materials, 10, 245-255.
• 2.Bao, R.J. & Yi, J. (2013) Effect of sintering atmosphere on microwawve prepared WC-8Wt.%Co cemented carbide. International Journal of Refractory Metals and Hard Materials, 41, 315-321.
• 3.Bao, R.J., Yi, Y., Peng, H. & Zhang, A.L. (2012) Decarburization and improvement of ultra fine straight WC-8Co sintered microwave sintering. Transaction of Nonferrous Metal Socienty of China, 22, 853-857.
• 4.Blikharskyy, Y. & Selejdak, J. (2021) Influence of the percentage of reinforcement damage on the bearing capacity of RC beams. Construction of Optimized Energy Potential, 10, 1, 145-150.
• 5.Cichosz, P. (2006) Narzędzia skrawające. Warszawa, Wydawnictwo Naukowo-Techniczne.
• 6.Dembiczak, T., Balaga, Z., Opydo, M., Kruzel, R., Garbiec, D. & Dyner, M. (2021) The effect of the binder phase and sintering temperature on the properties of spark plasma sintering WC-Co cemented carbid. Manufacturing Technology, 21, 45-50.
• 7.Jia, Ch., L., Sun, H. & Tang, X. (2007) Hot pressing of nanometer WC-Co powder. International Journal of Refractory Metals and Hard Materials, 25, 53-56.
• 8.Kim, H.D. & Oh, I.S. (2004) Sintering of nanophase WC-15vol.%Co hard metals by rapid sintering process. International Journal of Refractory Metals and Hard Materials, 22, 197-203.
• 9.Kim, H.D., Oh, J. & Guojian, I.S. (2004) Synthesis of WC and dense WC-5vol.%Co hard materials by high-frequency induction heated combustion. Materials Science and Engineering, A368, 10-17.
• 10.Knap, F., Kruzel, R. & Cieślak, Ł. (2004) Ciągnienie drutów, prętów i rur. Seria Metalurgia nr 36, Politechnika Częstochowska, Częstochowa.
• 11.Łuksza, J., Skołyszewski, A., Witek, F. & Zachariasz, W. (2006) Druty ze stali i stopów specjalnych.Warszawa, Wydawnictwo Naukowo-Techniczne.
• 12.Náprstková, N., Šramhauser, K., Cais, J. & Stančeková, D. (2018) Using of the electron microscope to evaluate the tool wear for a selected cutting insert. Manufacturing Technology, 18, 4, 635-640.
• 13.Náprstková, N., Cais, J., Kraus, P. & Tavodova, M. (2017) Using of electron microscopy for tool wear evaluation. Engineering for Rural Development.
• 14.Nowacki, J. (2004) Spiekane metale i kompozyty z osnową metaliczną. Warszawa, Wydawnictwo Naukowo-Techniczne.
• 15.Piekarczyk, A. (2021) Zginanie muru w płaszczyźnie prostopadłej do powierzchni ściany - obciążenia i mechanizmy zniszczenia. Materiały Budowlane, 582, (2), 27-29.
• 16.Wachowicz, J., Dembiczak, T., Stradomski, G., Bałaga, Z. & Dyner, M. (2021) Properties of WCCo composites produced by SPS method intended for cutting tools for machining of wood-based materials. Materials, 14, 2618, 1-15.
• 17.Wei, Ch.X., Song, S., Zhao, L. & Zhang, W. (2010) In-situ synthesis of WC-Co composite powder and densification by sinter-HIP. International Journal of Refractory Metals and Hard Materials, 28, 567-571.
• 18.Zapolski, P. (2021) Jak uniknąć błędów w ocenie i weryfikacji stałości właściwości użytkowych płyt warstwowych. Materiały Budowlane, 582, (2), 2-4.

Uwagi

Opracowanie rekordu ze środków MEiN, umowa nr SONP/SP/546092/2022 w ramach programu "Społeczna odpowiedzialność nauki" - moduł: Popularyzacja nauki i promocja sportu (2022-2023).