Research on the properties of high chromium cast iron overlay welds deposited by tubular electrodes

• Autorzy: Szymura M. , Czupryński A. , Różański M.

Identyfikatory

DOI

10.26628/ps.v90i10.947

Warianty tytułu

PL

Badanie własności warstw napawanych żeliwem chromowym elektrodami otulonymi rurkowymi

• Języki publikacji: EN

Abstrakty

EN

In the paper, there were shown the results of research on the properties of overlay welds consisted of one and three layers deposited by three types of tubular electrodes of the Fe-Cr-C alloy, Fe-Cr-C-Nb-Mo-W-V alloy and composite consist of tungsten carbide particles in the Fe-Cr-C alloy matrix. The study of hardfacing deposits included: test of metal-mineral abrasion resistance, metallographic examinations, analysis of chemical composition, and hardness tests. The test of abrasive usage in metal-mineral friction was made according to the procedure A of the ASTM G 65 standard.

PL

W artykule przedstawiono wyniki badania własności napoin jedno- i trójwarstwowych wykonanych trzema rodzajami elektrod rurkowych ze stopów Fe-Cr-C, Fe-Cr-C-Nb-Mo-W-V oraz kompozytu składającego się z cząstek węglika wolframu w osnowie ze stopu Fe-Cr-C. Badania napoin obejmowały: badania odporności na zużycie ścierne typu metal-minerał, badania metalograficzne, analizę składu chemicznego oraz pomiar twardości. Badanie odporności na zużycie ścierne typu metal-minerał przeprowadzono zgodnie z normą ASTM G 65, procedura A.

Słowa kluczowe

EN

hardfacing; tubular electrode; covered electrode; abrasion; chromium cast iron

PL

napawanie; elektroda rurkowa; elektroda otulona; ścieranie; żeliwo chromowe

• Wydawca: Stowarzyszenie Inżynierów i Techników Mechaników Polskich
• Czasopismo: Welding Technology Review
• Rocznik: 2018
• Tom: R. 90, nr 10
• Strony: 26--30
• Opis fizyczny: Bibliogr. 11 poz., il., tab.

Twórcy

autor

Szymura M.

• Silesian University of Technology, Poland

autor

Czupryński A.

• Silesian University of Technology, Poland

autor

Różański M.

• Institute of Welding, Gliwice, Poland

Bibliografia

• [1] V. Lazic, D. Arsic, R. Nikolic, M. Mutavzic, B. Hadzima, Revitalization of the damaged machine parts by hard facing as a way of saving funds, Production Engineering Archives (2016), vol. 12 (3), 9-13.
• [2] D. Womersley, Hardfacing: not merely a reclamation process, Surface Engineering (1995), vol. 11 (1), 43-46.
• [3] A. Klimpel, Napawanie i natryskiwanie cieplne. Technologie, WNT (2000), Warszawa, 92.
• [4] A.K. Mangla, S. Singh, J.S. Grewal, V. Chawla, Improvement in abrasive wear resistance by hardfacing: a review, National Conference on Advancements and Futuristic Trends in Mechanical and Materials Engineering (2010), 90-95.
• [5] J. Węgrzyn, Elektrody kompozytowe z węglikiem wolframu w otulinie, Welding Technology Review (1995), vol. 47 (12), 5-9.
• [6] A. Gruszczyk, Kształtowanie struktury napoin żeliwnych przez podwyższenie ich zdolności do grafityzacji, Welding Technology Review (2011), vol. 83 (10), 61-66.
• [7] A. Klimpel, A. Gruszczyk, K. Luksa, A. Szymański, Otulone elektrody rurkowe do napawania, Welding Technology Review (1995), vol. 47 (4), 1-4.
• [8] A. Cruz-Crespo, A. Scotti, M. Rodriguez-Perez, Operational behavior assesment of coated tubular electrodes for SMAW hardfacing, Journal of Materials Processing Technology (2008), vol. 199, 265-273.
• [9] Katalog firmy Welding Alloys Polska Sp. z o.o., Elektrody rurkowe WA do napawania, 2017.
• [10] Norma PN-EN 14700:2014-06 Materiały dodatkowe do spawania – Materiały dodatkowe do napawania utwardzającego.
• [11] Norma ASTM G 65-00 Standard Test Method for Measuring Abrasion Using the Dry Sand/Rubber Wheel Apparatus.

Uwagi

Opracowanie rekordu w ramach umowy 509/P-DUN/2018 ze środków MNiSW przeznaczonych na działalność upowszechniającą naukę (2019).