Laser cladding of Stellite 6 on low carbon steel for repairing components in automotive applications using disk laser

• Autorzy: Piasecki A. , Bartkowski D. , Młynarczyk A. , Dudziak A. , Gościański M. , Kasprowiak M.

Warianty tytułu

PL

Laserowe napawanie stopu stellite 6 na stal niskowęglową z użyciem lasera dyskowego w celu naprawy części stosowanych w przemyśle samochodywm

• Języki publikacji: EN

Abstrakty

EN

This paper describes results of a repair process of crankshaft pulley hub made of low-carbon steel using laser cladding method. Widely used Co-based alloy powder (Stellite 6) was applied as cladding material. After laser cladding process crankshaft pulley hub has been subjected to grinding to nominal size. Non-destructive testing (dye penetrant inspection) as well as microscopic and chemical composition examination of surface layer and substrate were performed on the cross-section of a control specimen, cut from pulley hub. Produced layer was non-porous and metallurgically bonded with steel substrate. On the cladding weld a much higher micro- hardness relatively to substrate material has been measured.

PL

W artykule opisano proces regeneracji piasty koła pasowego wału korbowego wykonanej ze stali niskowęglowej. Wykorzystano do tego celu metodę laser cladding. Jako materiał napawany zastosowano proszek stopu na bazie kobaltu (stellit 6). Po napawaniu piastę koła pasowego poddano szlifowaniu aż do uzyskania nominalnych wymiarów. Próbkę wyciętą z piasty poddano nieniszczącym badaniom penetracyjnym, badaniom mikroskopowym i składu chemicznego warstw powierzchniowych, a także badaniom mikrotwardości. Wytworzone warstwy napawane zbadano pod względem porowatości i jakości metalurgicznego związania ze stalowym podłożem. Wykonano również pomiary mikrotwardości wytworzonych warstw i podłoża. Na napoinach stwierdzono znacznie większą mikrotwardość niż na materiale podłoża.

Słowa kluczowe

EN

laser cladding; Stellite 6; automotive; microhardness; parts regeneration

PL

laser cladding; stellite 6; przemysł samochodowy; mikrotwardość; regeneracja części

• Wydawca: Wydawnictwo Politechniki Poznańskiej
• Czasopismo: Archives of Mechanical Technology and Automation
• Rocznik: 2013
• Tom: Vol. 33, no. 2
• Strony: 25--34
• Opis fizyczny: Bibliogr. 8 poz., fig.

Twórcy

autor

Piasecki A.

• Institute of Materials Science and Engineering, Poznan University of Technology

autor

Bartkowski D.

• Institute of Materials Science and Engineering, Poznan University of Technology

autor

Młynarczyk A.

• Institute of Materials Science and Engineering, Poznan University of Technology

autor

Dudziak A.

• Industrial Institute of Agricultural Engineering, Poznan

autor

Gościański M.

• Industrial Institute of Agricultural Engineering, Poznan

autor

Kasprowiak M.

• Institute of Materials Science and Engineering, Poznan University of Technology

Bibliografia

• 1. Burakowski T., Wierzchoń T., Inżynieria powierzchni metali, Warszawa, WNT 1995.
• 2. Cui C., Guo Z., Liu Y., Xie Q., Wang Z., Hu J., Yao Y., Characteristics of cobalt-based alloy coating on tool steel prepared by powder feeding laser cladding, Optics & Laser Tech¬nology, 2007, 39, p. 1544-1550.
• 3. Díaz E., Amado J.M., Montero J., Tobar M.J., Yáňez A., Comparative study of Co-based alloys in repairing low Cr-Mo steel components by laser cladding, Physics Procedia, 2012, 39, p. 368-375.
• 4. Gholipour A., Shamanian M., Ashrafizadeh F., Microstructure and wear behavior of stellite 6 cladding on 17-4 PH stainless steel, Journal of Alloys and Compounds, 2011, 509, p. 4905-4909.
• 5. Jakubowski J., Młynarczak A., Obróbka powierzchniowa i powłoki ochronne, Poznań, Wydawnictwo Politechniki Poznańskiej 1998.
• 6. Kathuria Y.P., Laser-cladding process: a study using stationary and scanning CO2 laser beams, Surface and Coatings Technology, 1997, 97, p. 442-447.
• 7. Lin W.C., Chen C., Characteristics of thin surface layers of cobalt-based alloys deposited by laser cladding, Surface & Coatings Technology, 2006, 200, p. 4557-4563.
• 8. Otterloo J.L., J Hossont Th.M., Microstructural features and mechanical properties of a cobalt-based laser coating, Acta Materialia, 1997, 45, p. 1225-1236.