The effect of curing temperature on the properties of different types of refractory concrete

• Autorzy: Boris R. , Antonovič V. , Stonys R. , Valochka A. , Belov I.

Warianty tytułu

PL

Wpływ temperatury twardnienia na właściwosci różnych typów betonu ogniotrwałego

• Języki publikacji: EN

Abstrakty

EN

At different curing temperatures, in alumina cement-based concrete, various crystalline hydrates are formed such as CAH10, C2AH8, C3AH6, AH3.While developing or modifying compositions of refractory concrete, it is necessary to take into consideration the impact of curing temperature on the process of formation of the structure and operating characteristics of concrete. This study investigates the properties of the following refractory concretes: the conventional concrete, the concrete modified by microsilica additive and the medium-cement concrete based on chamotte filler with alumina cement, of the grade Gorkal 70, at the curing temperatures of 10 ºC, 20 ºC and 30 ºC. Using the ultrasonic method of investigation, the differences were revealed in formation of the structure of concrete at its hardening in the course of 48 hours. It was established that the differences formed in the structure at hardening of concrete exert influence on properties of concrete after its firing at temperatures of 1100 ºC and 1200 ºC.

PL

W różnych temperaturach twardnienia w betonie opartym na cemencie glinowym tworzą się różne krystaliczne wodziany, takie jak CAH10, C2AH8, C3AH6, AH3. Podczas opracowywania i modyfikowania składów betonu ogniotrwałego konieczne jest wzięcie pod uwagę wpływu temperatury twardnienia na proces formowania struktury i charakterystyk pracy betonu. W niniejszej pracy zbadano właściwości następujących betonów ogniotrwałych: beton tradycyjny, beton modyfikowany dodatkiem mikrokrzemionki i średniocementowy beton oparty na wypełniaczu szamotowym z cementem glinowym w gatunku Gorkal 70, przy temperaturach twardnienia wynoszących 10 ºC, 20 ºC i 30 ºC. Wykorzystując metodę ultradźwiękową w badaniach, ujawniono różnice w tworzeniu się struktury betonu podczas jego twardnienia w ciągu 48 h. Ustalono, że różnice powstałe w strukturze podczas twardnienia betonu wywierają wpływ na właściwości betonu po jego wypaleniu w temperaturach 1100 ºC i 1200 ºC.

Słowa kluczowe

EN

refractory concrete; alumina cement; hydration; curing temperature; properties of concrete

PL

beton ogniotrwały; cement glinowy; hydratacja; temperatura twardnienia; właściwości betonu

• Wydawca: Polskie Towarzystwo Ceramiczne
• Czasopismo: Materiały Ceramiczne
• Rocznik: 2013
• Tom: T. 65, nr 3
• Strony: 267--271
• Opis fizyczny: Bibliogr. 8 poz.

Twórcy

autor

Boris R.

• Vilnius Gediminas Technical University Institute of Thermal Insulation, Linkmenų str. 28, LT-08217 Vilnius, Lithuania

autor

Antonovič V.

• Vilnius Gediminas Technical University Institute of Thermal Insulation, Linkmenų str. 28, LT-08217 Vilnius, Lithuania

autor

Stonys R.

• Vilnius Gediminas Technical University Institute of Thermal Insulation, Linkmenų str. 28, LT-08217 Vilnius, Lithuania

autor

Valochka A.

• National Academy of Sciences of Byelorussia, Kuprevichia 10, 220141 Minsk, Belarus

autor

Belov I.

• Institute NIISM, Minina 23, 220014 Minsk, Belarus

Bibliografia

• [1] UOP standart specification 3-24-4, Vibracast refractory linning.
• [2] Majumdar, S.D., Sarkar, R., Vajifdar, P.P., Narayanan, S., Cursetji, R.M., Chatterjee, A.K.: User friendly high refractory calcium aluminate cement, Proceedings of the International conference of Calcium Aluminate Cements, (2001), 467–476.
• [3] Goberis, S., Antonovič, V.: Kaitrai atsparūs šamotbetoniai: monogafija (Goberis S., Antonovič V.: Refractory fireclay castables), Vilnius: Technika, (2007), 360.
• [4] Plibrico Japan Comp.: Technology of monolithic refractories, Tokyo, Plibrico Japan Comp. Ltd, (1999), 598.
• [5] Cardoso, F. A., Innocentini, M. D. M., Akiyoshi, M. M., Pandolfelli, V. C.: ,Effect of curing conditions on the properties of ultra-low cement refractory castables‘, Refractories Applications and News, 9, 2, (2004), 12–16.
• [6] Heikal, M., Radwan, M. M., Morsy, M. S.: Influence of curing temperature on the physical-mechanical, characteristics of calcium aluminate cement with air-cooled slag or water-cooled slag‘, Ceramics – Silikaty, 4, (2004), 185–196.
• [7] Cardoso, F. A., Innocentini, M. D. M., Akiyoshi, M. M., Pandolfelli, V. C.: Effect of curing time on the properties of CAC bonded refractory castables, J. Eur. Ceram. Soc., 24, (2004), 2073–2078.
• [8] www. schleibinger.com