Changes in poplar (Populus trichocarpa) wood porous structure after liquid hot water (LHW) pretreatment

• Autorzy: Akus-Szylberg Florentyna , Szadkowski Jan , Antczak Andrzej , Zawadzki Janusz

Identyfikatory

DOI

10.5604/01.3001.0014.8861

• Języki publikacji: EN

Abstrakty

EN

Changes in poplar (Populus trichocarpa) wood porous structure after liquid hot water (LHW) pretreatment. The aim of this research was to investigate the effect of applying different hydrothermal pretreatment conditions on the porous structure of poplar wood. Porosity is recognised as an important factor considering efficiency of an enzymatic hydrolysis as a step of bioethanol production. Native poplar wood as well as solid fractions after pretreatment performed at different temperatures (160 °C, 175 °C and 190 °C) were analysed. Porous structure was examined with an inverse size-exclusion chromatography (ISEC) method. Results indicated a significant development of the porous structure of the biomass with increasing porosity along with the growing temperature of the LHW process. The temperature of 190 °C was chosen as the most promising condition of poplar wood LHW pretreatment in terms of the efficiency of the subsequent steps of bioethanol production. The obtained results were consistent with the previous experimental data procured during analysis of the LHW pretreated poplar wood and its subsequent enzymatic hydrolysis yield.

PL

Zmiany w strukturze porowatej drewna topoli po obróbce gorącą wodą (LHW). Celem badań było zbadanie wpływu zastosowania różnych warunków hydrotermalnej obróbki wstępnej na porowatą strukturę drewna topolowego. Porowatość jest uznawana za ważny czynnik, biorąc pod uwagę efektywność hydrolizy enzymatycznej, jako etapu produkcji bioetanolu. W pracy przedstawiono analizę porowatości biomasy po procesie obróbki wstępnej gorącą wodą przeprowadzonym w różnych temperaturach (160 °C, 175 °C i 190 °C). W celu zbadania struktury porowatej materiału zastosowano odwrotną chromatografię wykluczenia przestrzennego (ISEC). W efekcie przeprowadzonych badań stwierdzono znaczące zwiększanie się porowatości materiału wraz z rosnącą temperaturą obróbki LHW oraz określono 190 °C, jako optymalną temperaturę obróbki wstępnej LHW drewna topoli. Uzyskane wyniki znajdują potwierdzenie we wcześniej prowadzonych badaniach dotyczących hydrolizy enzymatycznej drewna topoli poddanej obróbce wstępnej LHW.

Słowa kluczowe

EN

liquid hot water; porosity; poplar wood; bioethanol production

• Wydawca: Wydawnictwo Szkoły Głównej Gospodarstwa Wiejskiego w Warszawie
• Czasopismo: Annals of Warsaw University of Life Sciences - SGGW. Forestry and Wood Technology
• Rocznik: 2020
• Tom: No. 112
• Strony: 71--78
• Opis fizyczny: Bibliogr. 18 poz., rys.

Twórcy

autor

Akus-Szylberg Florentyna

• Warsaw University of Life Sciences-SGGW, Department of Wood Science and Wood Preservation, Institute of Wood Sciences and Furniture, Poland

autor

Szadkowski Jan

• Warsaw University of Life Sciences-SGGW, Department of Wood Science and Wood Preservation, Institute of Wood Sciences and Furniture, Poland

autor

Antczak Andrzej

• Warsaw University of Life Sciences-SGGW, Department of Wood Science and Wood Preservation, Institute of Wood Sciences and Furniture, Poland

autor

Zawadzki Janusz

• Warsaw University of Life Sciences-SGGW, Department of Wood Science and Wood Preservation, Institute of Wood Sciences and Furniture, Poland

Bibliografia

• 1. AKUS-SZYLBERG F., ANTCZAK A., ZAWADZKI J., 2020: Hydrothermal pretreatment of poplar (Populus trichocarpa) wood and its impact on chemical composition and enzymatic hydrolysis yield. Drewno-Wood DOI: 10.12841/wood.1644-3985.367.09.
• 2. CHUNDAWAT S.P., DONOHOE B.S., DA COSTA SOUSA L., ELDER T., AGARWAL U.P., LU F., RALPH J,. HIMMEL M.E., BALAN V., DALE B.E., 2011: Multi-scale visualization and characterization of lignocellulosic plant cell wall deconstruction during thermochemical pretreatment. Energy Environ Sci4(3); 973-984.
• 3. GRETHLEIN H.E., 1985: The effect of pore size distribution on the rate of enzymatic hydrolysis of cellulose substrates. Bio/Technol 3; 155–160.
• 4. ISHIZAWA C.I., DAVIS M.F., SCHELL D.F., JOHNSON D.K., 2007: Porosity and its effect on the digestibility of dilute sulfuric acid pretreated corn stover. J. Agric. Food Chem. 55(7); 2575–2581.
• 5. IUPAC, 1994: Recommendations for the characterization of porous solids, Technical Report of International Union of Pure and Applied Chemistry, Physical Chemistry Division, Commission on Colloid and Surface Chemistry, Subcommittee on Characterization of Porous Solids, Pure and Applied Chemistry 66 (8); 1739-1758.
• 6. LAWRENCE M., JIANG Y., 2017: Porosity, Pore Size Distribution, Micro-structure. Bio-aggregates Based Building Materials23; 39-71.
• 7. LI X., LU J., ZHAO J., QU Y., 2014: Characteristics of corn stover pretreated with liquid hot water and fed–batch semi-simultaneous saccharification and fermentation for bioethanol production.PLoS One 9: e95455.
• 8. LIN K.W, LADISCH M.R, VOLOCH M, PATTERSON J.A, NOLLER C.H, 1985: Effect of pretreatments and fermentation on pore size in cellulosic materials. Biotechnol. Bioeng. 27(10); 1427–1433.
• 9. LYND L.R., 1996: Overview and evaluation of fuel ethanol from cellulosic biomass : technology, economics, the environment, and policy. Ann. Rev. Energ. Environ. 21; 403–465.
• 10. RADOMSKI A., 2015: Zastosowanie odwrotnej chromatografii wykluczenia przestrzennego do badania struktury porowatej materiałów lignocelulozowych. Wyd. SGGW, Warszawa.
• 11. SANNIGRAHI P., MILLER S.J., RAGAUSKAS A.J., 2010: Effects of organosolv pretreatment and enzymatic hydrolysis on cellulose structure and crystallinity in Loblolly pine. Carbohydr. Res. 345; 965-970.
• 12. SZADKOWSKI J., 2019: Changes of porous structure and chemical composition of poplar wood (Populus sp.) after physicochemical treatment. Doctoral thesis, Szkoła Główna Gospodarstwa Wiejskiego, Warszawa.
• 13. TAN Y., HU J., CHANG S. WEI Y., LIU G., WANG Q., LIU Y., 2020: Relationship between pore structure and gas permeability in poplar (Populus deltoides CL.’55/65’) tension wood. Annals of Forest Science 77; 88. doi.org/10.1007/s13595-020-00994-6.
• 14. YANG B., DAI Z., DING S.Y., WYMAN C. E., 2011: Enzymatic hydrolysis of cellulosic biomass.Biofuels 2; 421-450.
• 15. YIN J., SONG K., LU Y., ZHAO G., Yin Y., 2015: Comparison of Changes in Micropores and Mesopores in the Wood Cell Walls of Sapwood and Heartwood.Wood Sci. Technol. 49; 987–1001.
• 16. ZAWADZKI J., RADOMSKI A., ANTCZAK A., KUPCZYK A., 2016: Nowoczesne aspekty badawcze związane z otrzymywaniem bioetanolu z biomasy lignocelulozowej” in: Wyniki wybranych badań przeprowadzonych w ramach projektu WOODTECH [red. Stanisław Karpiński]. Oficyna Wydawniczo-Poligraficzna ADAM, Warszawa.
• 17. ZENG M., MOSIER N.S., HUANG C.P., SHERMAN D.M., LADISCH M.R., 2007: Microscopic examination of changes of plant cell structure in corn stover due to hot water pretreatment and enzymatic hydrolysis. Biotechnol. Bioeng. 97(2); 265–278.
• 18. ZHANG Y., LYND L.R., 2004: Toward an aggregated understanding of enzymatic hydrolysis of cellulose: noncomplexed cellulase systems. Biotechnol. Bioeng. 88(7); 797–824.

Uwagi

Opracowanie rekordu ze środków MEiN, umowa nr SONP/SP/546092/2022 w ramach programu "Społeczna odpowiedzialność nauki" - moduł: Popularyzacja nauki i promocja sportu (2022-2023).