Corrosion Resistance of Some Stainless Steels in Chloride Solutions

• Autorzy: Kasprzyk D. , Stypuła B.

Identyfikatory

DOI

10.1515/amm-2017-0107

• Języki publikacji: EN

Abstrakty

EN

The present work compares corrosion behaviour of four types of S30403, S31603, S32615 austenitic and S32404 austeniticferritic stainless steels in chloride solutions (1%, 3% NaCl) and in Ringer solution, at 37°C temperature. Corrosion resistance was determined by potentiodynamic polarization measurements and a thirty day immersion test conducted in Ringer solution. The immersion test was performed in term of biomedical application. These alloy were spontaneously passivated in all electrolytes, wherein S30403, S31603 and S32404 undergo pitting corrosion. Only S32615 containing 5.5% Si shows resistance to pitting corrosion.

Słowa kluczowe

EN

stainless steel; chemical composition; corrosion; Ringer solution

• Wydawca: Institute of Metallurgy and Materials Science of Polish Academy of Sciences ; Committee of Materials Engineering and Metallurgy of Polish Academy of Sciences
• Czasopismo: Archives of Metallurgy and Materials
• Rocznik: 2017
• Tom: Vol. 62, iss. 2A
• Strony: 711--714
• Opis fizyczny: Bibliogr. 19 poz., rys., tab.

Twórcy

autor

Kasprzyk D.

• AGH University of Science and Technology, Faculty of Foundry, Department of Chemistry and Corrosion of Metals, 23 Reymonta Str., 30-059 Kraków Poland

autor

Stypuła B.

• AGH University of Science and Technology, Faculty of Foundry, Department of Chemistry and Corrosion of Metals, 23 Reymonta Str., 30-059 Kraków Poland

Bibliografia

• [1] S. Ahmad, A. U. Malik, J. Appl. Electrochem. 31, 1009 (2001).
• [2] A. U. Malik, S. Ahmad, I. Andijani, Desalination 123, 205 (1999).
• [3] A. A. Hermas, J. Mat. Sci. 36, 3415 (2001).
• [4] D. Kasprzyk, B. Stypuła, Corrosion Protection 55, 508 (2012).
• [5] I. Milosev, H.H. Strehblow, J. Biomed. Res. 52, 404 (2000).
• [6] A. Kocijan, D.K. Merl, M. Jenko, Corros. Sci. 53, 776 (2011).
• [7] J. A. Platt, A. Guzman, A. Zuccari, et al., Am. J. Orthod. Dentofac. Orthop. 112, 69 (1997).
• [8] A.U. Malik, N.A. Siddiqi, et al., Corros. Sci. 37, 1521 (1995).
• [9] H. C. Brookes, F.J. Graham, Corrosion 45, 287 (1989).
• [10] R. Perren, T. Suter, P. Uggowitzer, et al., Corros. Sci. 43, 707 (2001).
• [11] K. Sieradzki, R.C. Newman, J. Electrochem. Soc. 133, 1979 (1986).
• [12] K. Asami, K. Hashimoto, S. Shimodaira, Corros. Sci. 18, 151 (1978).
• [13] D. Kasprzyk, B. Stypuła, P. Kuśtrowski, M. Drozdek, Arch. Of Metall. Mater. 58, 1169 (2013).
• [14] Y. Okazaki, E. Gotoh, Corros. Sci. 50, 3429 (2008).
• [15] G. Herting, I. Odnevall Wallinder, C. Leygraf, Corros. Sci. 49, 103 (2007).
• [16] J. Horvath, H.H. Uhlig, J. Electrochem. Soc. 115, 791 (1968).
• [17] K. Lorenz, G. Medawar, Thyssen Forsch. 1, 97 (1969).
• [18] B. Stypula, D. Kasprzyk, M. Hajos , Archiv of Metallurgy and Matter. 54, 305 (2009).
• [19] M. Holtzer, Werkstoffe und Korrosion 41, 25 (1990).

Uwagi

PL

Opracowanie ze środków MNiSW w ramach umowy 812/P-DUN/2016 na działalność upowszechniającą naukę (zadania 2017).