Determination Of Power Loss In Fe-Based Soft Magnetic Composites

• Autorzy: Jankowski B. , Kapelski D. , Ślusarek B. , Szczygłowski J.

Warianty tytułu

PL

Wyznaczanie strat mocy w kompozytach magnetyczne miękkich na bazie żelaza

• Języki publikacji: EN

Abstrakty

EN

The magnetic properties of Fe-based composite materials with different particle sizes were investigated. The results of energy loss density were obtained from measurements of the static (DC) hysteresis cycles ranging from 0,2 to 1,4 T. In turn, the results of power loss density were obtained from measurements of the dynamic (AC) hysteresis cycles ranging from 20 to 400 Hz and at the maximum flux density 0,3; 0,9 and 1,3 T. Two sets of specimens was analyzed in the investigation: the specimens compacted under pressure of 800 MPa and hardened at 500°C and the specimens compacted under different pressure and hardened at 500°C. Specimens of the second set had the same density. The study confirmed the influence of particle size distribution on magnetic properties of Fe-based soft magnetic composites.

Słowa kluczowe

EN

magnetic materials; power losses; soft magnetic composites

PL

materiały magnetyczne; straty mocy; miękkie kompozyty magnetyczne

• Wydawca: Institute of Metallurgy and Materials Science of Polish Academy of Sciences ; Committee of Materials Engineering and Metallurgy of Polish Academy of Sciences
• Czasopismo: Archives of Metallurgy and Materials
• Rocznik: 2015
• Tom: Vol. 60, iss. 2B
• Strony: 1411--1415
• Opis fizyczny: Bibliogr. 9 poz., rys.

Twórcy

autor

Jankowski B.

• Tele and Radio Research Institute, 11 Ratuszowa Str., 03-450, Warszawa, Poland

autor

Kapelski D.

• Tele and Radio Research Institute, 11 Ratuszowa Str., 03-450, Warszawa, Poland

autor

Ślusarek B.

• Tele and Radio Research Institute, 11 Ratuszowa Str., 03-450, Warszawa, Poland

autor

Szczygłowski J.

• Czestochowa University of Technology, 17 Armii Krajowej Av, 42-200, Częstochowa, Poland

Bibliografia

• [1] J. A. Bas, J. A. Calero, M. J. Dougan, J Magn Magn Mater 254, 391-398 (2003).
• [2] B. Ślusarek, Prz Elektrotechniczn 86(4), 16-19 (2010).
• [3] A. Kordecki, B. Węglinski, J. Kaczmar, Powder Metall 25(4), 201-208 (1982).
• [4] H. Shokrollahi, K. Janghorban, J Mater Process Tech 189(1-3), 1-12 (2007).
• [5] I. Hemmati, H. R. M. Hosseini, S. Miraghaei, Powder Metall 50(1), 86-90 (2007).
• [6] G. Bertotti, IEEE T Magn 24(1), 621-630 (1988).
• [7] G. Bertotti, F. Fiorillo, G. P. Soardo, J Phys-Paris 49(C-8), 1915-1919 (1988).
• [8] P. Kollár, Z. Birčáková, J. Füzer, R. Bureš, M. Fáberová, J Magn Magn Mater 327, 146-150 (2013).
• [9] A. Kordecki, Dielektromagnetyki magnetowodów maszyn elektrycznych; 1994, Wrocław, Oficyna Wydawnicza Politechniki Wrocławskiej, (in Polish).

Uwagi

PL

Opracowanie ze środków MNiSW w ramach umowy 812/P-DUN/2016 na działalność upowszechniającą naukę.