Thermal, Structural and Electrical Properties of Some Bi-Cu-Ni Alloys

• Autorzy: Marković B. , Živković D. , Manasijeyić D. , Sokić M. , Minić D. , Talijan N. , Stajić-Trošić J.

Identyfikatory

DOI

10.2478/amm-2014-0018

Warianty tytułu

PL

Struktura, właściwości termiczne i elektryczne wybranych stopów Bi-Cu-Ni

• Języki publikacji: EN

Abstrakty

EN

The Bi-Cu-Ni ternary system belongs to the group of potential Cu-Ni-based advanced lead-free solder materials for high temperature application. In this study microstructure investigation of the slow-cooled Bi-Cu-Ni samples was done using SEM-EDS analysis. The samples compositions were chosen along three cross-sections with molar ratio Cu:Ni=1:3, 1:1 and 3:1. The experimentally obtained phase structure was compared with the results of thermodynamic calculation according to CALPHAD method. Also, new results regarding thermal and electrical properties investigations of these alloys are presented in this paper, based on DSC and electroconductivity measurements.

PL

Trójskładnikowe stopy Bi-Cu-Ni należą do grupy potencjalnych zaawansowanych bezołowiowych materiałów do lutowania w wysokiej temperaturze opartych na stopach Cu-Ni. Analizę mikrostruktury wolno schłodzonych próbek Bi-Cu-Ni wykonano za pomocą technik SEM-EDS. Do badań wybrano próbki charakteryzujące się stałym molowym stosunkiem Cu:Ni=1:3, 1:1 i 3:1. Doświadczalnie otrzymaną strukturę faz porównano z wynikami obliczeń termodynamicznych metodą CALPHAD. Ponadto, nowe wyniki dotyczące badań właściwości cieplnych i elektrycznych stopów zostały przedstawione w tym artykule, na podstawie pomiarów DSC i przewodności elektrycznej.

Słowa kluczowe

EN

Bi-Cu-Ni alloys; lead-free solders; characterization

PL

stopy Bi-Cu-Ni; luty bezołowiowe; charakterystyka

• Wydawca: Institute of Metallurgy and Materials Science of Polish Academy of Sciences ; Committee of Materials Engineering and Metallurgy of Polish Academy of Sciences
• Czasopismo: Archives of Metallurgy and Materials
• Rocznik: 2014
• Tom: Vol. 59, iss. 1
• Strony: 117--120
• Opis fizyczny: Bibliogr. 8 poz., rys., tab.

Twórcy

autor

Marković B.

• Institute for Technology of Nuclear and Other Mineral Raw Materials, Belgrade, Serbia

autor

Živković D.

• University of Belgrade, Technical Faculty, Bor, Serbia

autor

Manasijeyić D.

• University of Belgrade, Technical Faculty, Bor, Serbia

autor

Sokić M.

• Institute for Technology of Nuclear and Other Mineral Raw Materials, Belgrade, Serbia

autor

Minić D.

• University of Priština, Faculty of Technical Sciences, Kosovska Mitrovica, Serbia

autor

Talijan N.

• University of Belgrade, Institute of Chemistry, Technology and Metallurgy, Belgrade, Serbia

autor

Stajić-Trošić J.

• University of Belgrade, Institute of Chemistry, Technology and Metallurgy, Belgrade, Serbia

Bibliografia

• [1] http://cost602.ipm.cz/
• [2] F. Gao, X. Liu, Y. Takaku, I. Ohnuma, K. Ishida, J. Mater. Res. 24 (8), 2644-2653 (2009).
• [3] B. Marković, D. Živkovic, J. Vřeštál, D. Manasijević, D. Minić, J. Stajić - Trošić, R. Todorović, CALPHAD 34 (3), 294-300 (2010).
• [4] J. Romanowska, Arch. Metall. Mater. 56 (1), 87-91 (2011).
• [5] G. Wnuk, Arch. Metall. Mater. 56 (2), 305-310 (2011).
• [6] D. Živković, D. Manasijević, Lj. Balanović, D. Minić, V. Cosović, A. Kostov, Ž. Živković, J. Min. Metall. Sect. B-Metall. 48 (3)B, 375-382 (2012).
• [7] www.chemicool.com
• [8] www.webelements.com

Uwagi

This paper was done in the frame of project OI 172037 financed by Ministry of Science and Technological Development of the Republic of Serbia and the COST Action MP 0602 “Advanced Solder Materials for High Temperature Application”.