The effect of simulated climatic conditions of ageing on properties of selected polymer composites

• Autorzy: Dulebova L. , Krzyżak A. , Dulebova M.

Warianty tytułu

PL

Wpływ symulowanych warunków klimatycznych na proces starzenia właściwości wybranych polimerów kompozytowych

• Języki publikacji: EN

Abstrakty

EN

Nowadays designers and engineers readily turn to plastics because they offer combinations of properties not available in any other materials. Plastics offer advantages such as lightness, resilience, resistance to corrosion, colour fastness, transparency, ease of processing, etc., and although they have their limitations, their exploitation is limited only by the ingenuity of the designer. Degradation of the polymers under the influence of temperature, light, humidity and oxygen leads to changes in structures such as the increase in crosslinking, reducing the degree of polymerization, oxidation or recrystallization of the molecular chains. The result of the ageing process are reversibly or irreversibly a deterioration of processing and changing of properties. The aim of this paper was the comparison of change of selected properties of polymer composites used for the production of parts in the electrical industry in changing the thermal conditions. Materials ABS, PA6 and PBT were tested and the samples were exposed to different climatic conditions. Static tensile test and 3- point bend test were used for testing and samples were used by injection molding.

PL

Obecnie projektanci i inżynierowie chętnie sięgają po tworzywa sztuczne ze względu na kombinacje właściwości, które oferują, nieosiągalne w przypadku innych materiałów. Tworzywa mają liczne zalety, takie jak: lekkość, sprężystość, odporność na korozję, trwałość koloru, przejrzystość, łatwość obróbki, itd. i mimo swoich ograniczeń, ich zastosowanie jest ograniczone tylko poprzez pomysłowość lub jej brak u projektanta. Degradacja polimerów pod wpływem temperatury, światła, wilgotności i tlenu prowadzi do zmian w strukturze, takich jak wzrost sieciowania, redukcja stopnia polimeryzacji, utlenianie czy też rekrystalizacja łańcuchów molekularnych. Skutki procesu starzenia to odwracalne bądź nieodwracalne pogorszenie przetwarzania i zmiana właściwości. Celem niniejszej pracy było porównanie zmian wybranych właściwości kompozytów polimerowych stosowanych w produkcji części w przemyśle elektrycznym przy zmieniających się warunkach termicznych. Badano materiały ABS, PA6 PBT, których próbki poddani działaniu różnych warunków klimatycznych. W badaniach wykorzystano statyczne próby rozciągania oraz 3-punktowy test giętkości, natomiast próbki były wykorzystane w procesie formowania wtryskowego.

Słowa kluczowe

EN

polymer composites; simulated climatic condition; ageing; polymer properties

PL

kompozyty polimerowe; symulowane warunki klimatyczne; starzenie; właściwości polimerów

• Wydawca: Wydawnictwo Lotniczej Akademii Wojskowej
• Czasopismo: Zeszyty Naukowe / Wyższa Szkoła Oficerska Sił Powietrznych
• Rocznik: 2015
• Tom: Nr 3
• Strony: 71--79
• Opis fizyczny: Bibliogr. 12 poz., fig.

Twórcy

autor

Dulebova L.

• Faculty of Mechanical Engineering, Technical University of Kosice

autor

Krzyżak A.

• Faculty of Areonautics, Polish Air Force Academy

autor

Dulebova M.

• Faculty of Mechanical Engineering, Technical University of Kosice

Bibliografia

• 1. Dobránsky J., Baron P., Kočiško M., Vojnová E., Monitoring of the influence of moisture content in thermoplastic granulate on rheological properties of material, Applied Mechanics and Materials 2014.
• 2. Boxhammer J., Acceleration by increased irradiance and temperature in artificial weathering tests, Polymer Testing 2001.
• 3. Dulebová Ľ, Tor- Swiatek A., Duleba B., Study of selected properties of thermoplastics after ageing, Transfer inovacii. 2014.
• 4. Sobotová L. et al., The experimental verification of the impact of regrind on mechanical properties of thermoplastics, Advanced Materials Research 2013.
• 5. Garbacz T., Tor A.: Wpływ zawartości środka porującego na właściwości użytkowe zewnętrznych powłok kabli, Polimery 2007.
• 6. Encyclopedia of polymer science and technology/ Degradation to magnetic polymers. Vol. 6, 3rd ed. Hoboken: Wiley-Inter Science, 2003.
• 7. Niewczas A.M., Pieniak D., Kordos P., Krzyżak A., Influence of simulated thermal conditions of the oral cavity environment on composite fillings, Polish Journal of Environment Study 2010.
• 8. Dulebová Ľ., Krasinskyi V., Qualitative evaluation of selected mechanical properties of composites produced by injection molding after degradation, In: Technological and design aspects of extrusion and injection moulding of thermoplastic polymer composites and nanocomposites: Volume 2. Košice: TU, 2014.
• 9. Tavares A.C., Gulmine J.V., Lepienski C.M., Akcelrud L., The effect of accelerated ageing on the surface mechanical properties of polyethylene, Polymer Degradation and Stability 2003.
• 10. Jachowicz T., Krzyżak A., Wpływ starzenia naturalnego na wybrane właściwości rur z polietylenu, MOTROL 2009.
• 11. Sobków D., Chana K., Wpływ warunków przyspieszonego starzenia na proces degradacji poliolefin, Polimery 2003.
• 12. Kahlen S., Wallner G.M., Lang R.W., Ageing behaviour of polymeric solar absorber materials – Part 1, Engineering plastics. Solar Energy, 2010.