Structure and Soft Magnetic Properties of the Amorphous Alloys: Fe61Co10Ti3-xY6+xB20 (x = 0,1)

• Autorzy: Błoch K.

Identyfikatory

DOI

10.1515/amm-2016-0080

• Języki publikacji: EN

Abstrakty

EN

This paper presents studies relating to the structure, soft magnetic properties and thermal stability of the following bulk amorphous alloys: Fe₆₁Co₁₀Ti_3-xY_6+xB₂₀ (x = 0, 1). On the basis of the performed X-ray diffraction studies and Mössbauer spectroscopy, it was found that investigated samples were amorphous in the as-cast state. The DSC curve obtained for Fe₆₁Co₁₀Ti₂Y₇B₂₀ alloy exhibited one exothermic peak, while for the Fe₆₁Co₁₀Ti₃Y₆B₂₀ sample, two peaks were distinguishable. The change in the chemical structure of the investigated alloys has a major effect on their soft magnetic properties; especially on coercivity and saturation magnetization. On the basis of the magnetization curves analysis, the spin wave stiffness parameter D_sp were determined for the investigated alloys.

Słowa kluczowe

EN

structure; soft magnetic properties; amorphous alloys

• Wydawca: Institute of Metallurgy and Materials Science of Polish Academy of Sciences ; Committee of Materials Engineering and Metallurgy of Polish Academy of Sciences
• Czasopismo: Archives of Metallurgy and Materials
• Rocznik: 2016
• Tom: Vol. 61, iss. 1
• Strony: 445--450
• Opis fizyczny: Bibliogr. 21 poz., rys., tab., wykr., wzory

Twórcy

autor

Błoch K.

• Czestochowa University of Technology, Institute of Physics, 19 Armii Krajowej Av., 42-200 Czestochowa, Poland

Bibliografia

• [1] P. Duwez, R. H. Willens, T. Metall. Soc. Aime. 227, 362-365 (1963).
• [2] M. Nabiałek, J. Zbroszczyk, J. Olszewski, M. Hasiak, W. Ciurzyńska, K. Sobczyk, J. Świerczek, J. Kaleta, A. Łukiewska, J. Magn. Magn. Mater. 324, 787-791 (2008).
• [3] J. Garus, S. Garus, M. Nabiałek, M. Szota, Acta Phys.Pol. A 126, 954-956 (2014).
• [4] J. Gondro, K. Błoch, M. Nabiałek, K. Waltters, M. Szota, Arch. Metall. Mater. 60, 1071-1074 (2015).
• [5] M. Dospial, J. Olszewski, M. Nabialek, P. Pietrusiewicz, T. Kaczmarzyk, Nukleonika 60, 15-18 (2015).
• [6] M. Nabiałek., P. Pietrusiewicz, M. Szota, M. Dośpiał, J. Jędryka, K. Szota, S. Lesz, Arch. Metall. Mater. 57, 223-227 (2012).
• [7] J. Gondro, J. Świerczek, J. Olszewski, J. Zbroszczyk, K. Sobczyk, W. Ciurzyńska, J. Rzącki, M. Nabiałek, J. Magn. Magn. Mater. 324, 1360-1364 (2012).
• [8] K. Błoch, J. Magn. Magn. Mater. 390, 118-122 (2015).
• [9] J. Gondro, J. Świerczek, K. Błoch, J. Zbroszczyk, W. Ciurzyńska, J. Olszewski, Physica B. 445, 37-41 (2014).
• [10] S. Lesz, R. Babilas, M. Nabialek, M. Szota, M. Dospial, R. Nowosielski, J. All. Compd. 509, 197-201 (2010).
• [11] W. H. Wang, C. Dong, C. H. Shek, Mater. Sci. Eng. 44, 45-89 (2004).
• [12] H. W. Chang, Y. C. Huang, C. W. Chang, C. H. Chiu, W. C. Chang, J. All. Compd. 462, 68-72 (2008).
• [13] H. Kronmüller, J. Appl. Phys. 52 (3), 1859 - 1864 (1981).
• [14] H. Kronmüller, IEEE Trans. Magn., MAG -15, 5, 1218-1225 (1979).
• [15] N. Lenge, H. Kronmüller, Phys. Stat. Sol. (a), 95, 621-633 (1986).
• [16] P. Pietrusiewicz, M. Nabiałek, M. Dośpiał, K. Gruszka, K. Błoch, J. Gondro, P. Brągiel, M. Szota, Z. Stradomski, J. All. Compd. 615, Suppt 1, 5, S67-S70 (2014).
• [17] K. Gruszka, M. Nabiałek, K. Błoch S. Walters, Int. J. Mater. Res. 106, 689-696 (2015).
• [18] Z. P. Lu, C. T. Liu, J. Mat. Sci. 39, 3965-3974 (2004).
• [19] K. Gruszka, M. Nabiałek, K. Błoch, J. Olszewski, Nukleonika 60, No.1, 23-27 (2015).
• [20] M. Nabiałek., J. Alloys and Compd. 642, 98-103 (2015).
• [21] Z. Long, Y. Shao, F. Xu, H. Wei, Z. Zhang, P. Zhang, X. Su, Mater. Sci. Eng. 164, 1-5 (2009).

Uwagi

PL

Opracowanie ze środków MNiSW w ramach umowy 812/P-DUN/2016 na działalność upowszechniającą naukę