Aging behavior of the three-proof polyurethane coating under UV radiation

• Autorzy: Wang Jianfa , Gu Zheng , Zhao Jie , Zhang Susu , Li Peiyao , Meng Chao , Sui Jinyong , Zhang Xiaoyi , Hu Shaokai , Pan Jiaying , Li Junyi

Identyfikatory

DOI

10.14314/polimery.2022.9.4

Warianty tytułu

PL

Wpływ promieniowania UV na starzenie trójwarstwowej powłoki poliuretanowej

• Języki publikacji: EN

Abstrakty

EN

The influence of UV radiation on the gloss, structure (SEM, FTIR), thermal (TGA, DTG) and mechanical properties of polyurethane resins and the three-layer protective coating made of them was investigated. The gloss of the resins was greater than that of the protective coating. UV radiation has been proven to reduce gloss (at 1,200 hours irradiation, 81.3° to 8.9° for resins, and 61.1° to 2.8° for coating).The tensile strength of the resins decreased during aging, and the relative elongation at break after reaching the minimum was increased (at the irradiation time of 100 h). In the case of coating, both the tensile strength and elongation decreased during aging and, after reaching the minimum they increased (at the irradiation time of 800 h), reaching the maximum (at the irradiation time of 1000 h), and then decreased.

PL

Zbadano wpływ promieniowania UV na połysk, strukturę (SEM, FTIR), właściwości termiczne (TGA, DTG) i mechaniczne żywic poliuretanowych oraz wykonanej z nich trójwarstwowej powłoki ochronnej. Połysk żywic był większy niż powłoki ochronnej. Potwierdzono, że promieniowanie UV zmniejsza połysk (przy naświetlaniu przez 1200 godzin, w przypadku żywic z 81,3° do 8,9°, a w przypadku powłok z 61,1° do 2,8°). Wytrzymałość na rozciąganie żywic zmniejszała się w trakcie starzenia, a wydłużenie względne przy zerwaniu po osiągnięciu minimum zwiększało (przy czasie naświetlania 100 h). W przypadku powłoki zarówno wytrzymałość na rozciąganie, jak i wydłużenie zmniejszały się w trakcie starzenia i po osiągnięciu minimum zwiększały (przy czasie naświetlania 800 h), osiągając maksimum (przy czasie naświetlania 1000 h), a następnie zmniejszały.

Słowa kluczowe

EN

polyurethane; ultraviolet; coating; resin

PL

poliuretan; ultrafiolet; powłoka; żywica

• Wydawca: Sieć Badawcza Łukasiewicz – Instytut Chemii Przemysłowej
• Czasopismo: Polimery
• Rocznik: 2022
• Tom: Vol. 67, nr 9
• Strony: 433--437
• Opis fizyczny: Bibliogr. 15 poz., rys., wykr.

Twórcy

autor

Wang Jianfa

• College of Chemistry and Chemical Engineering, Qingdao University, China 266071.

• https://orcid.org/0000-0002-1242-3794

autor

Gu Zheng

• College of Chemistry and Chemical Engineering, Qingdao University, China 266071.
• Weihai Innovation Institute, Qingdao University, China 264200.

• https://orcid.org/0000-0001-9521-2863

autor

Zhao Jie

• College of Chemistry and Chemical Engineering, Qingdao University, China 266071.

autor

Zhang Susu

• College of Chemistry and Chemical Engineering, Qingdao University, China 266071.

• https://orcid.org/0000-0003-3620-0816

autor

Li Peiyao

• College of Materials Science and Engineering, Qingdao University, China 266071.

• https://orcid.org/0000-0002-4713-1599

autor

Meng Chao

• College of Chemistry and Chemical Engineering, Qingdao University, China 266071.

• https://orcid.org/0000-0001-6603-2273

autor

Sui Jinyong

• College of Chemistry and Chemical Engineering, Qingdao University, China 266071

• https://orcid.org/0000-0002-4232-3540

autor

Zhang Xiaoyi

• College of Chemistry and Chemical Engineering, Qingdao University, China 266071

• https://orcid.org/0000-0003-4047-5046

autor

Hu Shaokai

• College of Chemistry and Chemical Engineering, Qingdao University, China 266071

• https://orcid.org/0000-0002-2049-3135

autor

Pan Jiaying

• College of Materials Science and Engineering, Qingdao University, China 266071.

• https://orcid.org/0000-0002-1609-7869

autor

Li Junyi

• College of Materials Science and Engineering, Qingdao University, China 266071.

• https://orcid.org/0000-0001-8110-6496

Bibliografia

• [1] Yang F., Lv Y.B., Yang X. et al.: Comprehensive Corrosion Control 2016, 5, 78. https://doi.org /10.13726/j.cnki.11-2706/tq.2016.05.078.03
• [2] Li Q., Li H., Li C. et al.: Coating Industry 2018, 48(09), 46.
• [3] Zhang Y., Cheng Z., Liu H.: Equipment Environmental Engineering 2018, 15(2), 97.
• [4] Luo L., Xiao Y., Su Y. et al.: Equipment Environmental Engineering 2015, 12(6), 42.
• [5] Yang X.F., Tallman D.E., Bierwagen G.P. et al.: Polymer Degradation and Stability 2002, 77, 103. https://doi.org/10.1016/S0141-3910(02)00085-X
• [6] Yang X.F., Li J., Croll S.G. et al.: Polymer Degradation and Stability 2003, 80, 51. https://doi.org/10.1016/S0141-3910(02)00382-8
• [7] Xu Y., Yan C., Ding J. et al.: Chinese Journal of Corrosion and Protection 2004, 24(3), 168.
• [8] Yang H., Wang X., Zheng J. et al.: Journal of Xiamen University (Natural Science Edition) 2017, 56(03), 370.
• [9] Zhang H., Xin L., Hong L.: China Adhesive 2018, 27(03), 51. https://doi.org/ 10.13416/j.ca.2018.03.013
• [10] Xu X., Zou B., Lin Z.: China Adhesives 2016, 25(11), 37 + 59. https://doi.org/10.13416/j.ca.2016.11.010
• [11] Zhang H., Xin C., Li S. et al.: Polyurethane Industry 2016, 31(05), 14.
• [12] Pan Y., Wen Q., Zhu J.: Surface Technology 2020, 49(06), 305-313+344.https://doi.org/1016490/j.cnki.issn.1001-3660.2020.06.037
• [13] Pat. GB / T 23987-2009.
• [14] Pat. GB / T 1766-1995.
• [15] Civancik-Uslu D., Ferrer L., Puig R. et al.: Science of the Total Environment 2018, 626, 927. https://doi.org/10.1016/j.scitotenv.2018.01.149

Uwagi

Opracowanie rekordu ze środków MEiN, umowa nr SONP/SP/546092/2022 w ramach programu "Społeczna odpowiedzialność nauki" - moduł: Popularyzacja nauki i promocja sportu (2022-2023).