Influence of the corrosive environment on the Portevin–Le Chatelier plastic instability phenomenon in Al–1Mg and Al–3Mg model alloys

• Autorzy: Towarek A. , Zdunek J. , Mizera J. , Dobkowska A. , Molak R.

Identyfikatory

DOI

10.15199/28.2016.3.1

Warianty tytułu

PL

Wpływ środowiska korozyjnego na niestabilność odkształcenia plastycznego Portevin–Le Chatelier w modelowych stopach Al–1Mg i Al–3Mg

• Języki publikacji: EN

Abstrakty

EN

The aim of this work was to indicate the influence of changes on the surface of materials caused by the corrosive medium (3.5% NaCl solution) on the intensity and character of the Portevin–Le Chatelier effect in model aluminium alloys. For this purpose, two Al alloys, containing 1% and 3% of magnesium, were subjected to tensile testing in the as-cast state and after the exposition in NaCl solution for various time. Several electrochemical measurements were held to determine materials’ corrosive behaviour and microscopic observations to evaluate the surface character of the samples. High corrosion resistance of the materials resulted in a very slight alteration of their surface development, which didn’t lead into any significant variations in the plastic instability phenomenon PLC.

PL

Efekt Portevin–Le Chatelier jest dobrze znanym i szeroko opisanym zjawiskiem pojawiającym się w wielu stopach aluminium. Objawia się on podczas odkształcania w postaci charakterystycznych ząbków na krzywej rozciągania wywołanych gwałtownymi zmianami naprężenia przy niewielkim odkształceniu. Wpływ na to zjawisko jest przypisywany głównie czynnikom wewnętrznym, wynikającym ze struktury materiału, takim jak: wielkość ziarna, obecność wydzieleń czy tekstury. Istotne mogą być jednak również czynniki zewnętrzne, m.in. szybkość odkształcania, środowisko czy stopień rozwinięcia powierzchni próbki. Celem pracy było zbadanie, jak zmiany na powierzchni materiału wywołane przez ekspozycję w środowisku korozyjnym (3,5% roztworze NaCl) wpłyną na intensywność i charakter zjawiska Portevin–Le Chatelier w dwóch modelowych stopach aluminium, Al–1Mg oraz Al–3Mg.

Słowa kluczowe

EN

Portevin-Le Chatelier effect; aluminium alloys; plastic instability; corrosion

PL

zjawisko Portevin-Le Chatelier; stopy aluminium; niestabilność odkształcenia plastycznego; korozja

• Wydawca: Wydawnictwo SIGMA-NOT
• Czasopismo: Inżynieria Materiałowa
• Rocznik: 2016
• Tom: Vol. 37, nr 3
• Strony: 98--103
• Opis fizyczny: Bibliogr. 11 poz., fig., tab.

Twórcy

autor

Towarek A.

• Materials Science and Engineering Faculty, Warsaw University of Technology, Warsaw

autor

Zdunek J.

• Materials Science and Engineering Faculty, Warsaw University of Technology, Warsaw

autor

Mizera J.

• Materials Science and Engineering Faculty, Warsaw University of Technology, Warsaw

autor

Dobkowska A.

• Materials Science and Engineering Faculty, Warsaw University of Technology, Warsaw

autor

Molak R.

• Materials Science and Engineering Faculty, Warsaw University of Technology, Warsaw

Bibliografia

• [1] Kuo C. M., Tso C. H., Lin C. H.: Plastic instability of Al–Mg alloys during stress rate change test. Mater. Sci. Eng. A 519 (1-2) (2009) 32÷37.
• [2] Rizzi E., Hähner P.: On the Portevin–Le Chatelier effect: theoretical modeling and numerical results. Scr. Metall. 20 (2004) 121÷165.
• [3] Zdunek J.: Badania ilościowe niestabilności odkształcenia plastycznego Portevin–Le Chatelier w stopach na osnowie aluminium. Politechnika Warszawska (2008).
• [4] Abduluyahed A. A., Rożniatowski K., Kurzydłowski K. J.: The effect of test environment on tensile properties of 316L austenitic stainless steel part I: Serrated flow characteristics. Scripta Metallurgica et Materialia 33(9) (1995) 1489÷1492.
• [5] Abduluyahed A., Kurzydłowski K. J.: Tensile properties of a type 316 stainless steel strained in air and vacuum. Mater. Sci. Eng. A 256 (1-2)(1998) 34÷38.
• [6] Yilmaz A.: Temperature and surface potential correlations with serrated flow of low carbon steel. J. Mater. Sci. 46 (11) (2011) 3766÷3776.
• [7] Abbadi M., Hähner P., Zeghloul A.: On the characteristics of Portevin–Le Chatelier bands in aluminum alloy 5182 under stress-controlled and strain controlled tensile testing. Mater. Sci. Eng. A 337 (1-2) (2002) 194÷201.
• [8] Ezuber H., El-Houd A., El-Shawesh F.: A study on the corrosion behavior of aluminum alloys in seawater. Mater. Des. 29 (4) (2008) 801÷805.
• [9] Wang B., Zhang L., Su Y., Xiao Y., Liu J.: Corrosion behavior of 5A05 aluminum alloy in NaCl solution. Acta Metall. Sin. (English Lett.) 26 (5)(2013) 581÷587.
• [10] [10] M. Popovicand E. Romhanji, “Stress corrosion cracking susceptibility of Al–Mg alloy sheet with high Mg content,” J. Mater. Process. Technol., vol. 125–126,pp. 275–280, 2002.
• [11] Mizera J., Kurzydlowski K. J.: On the anisotropy of the Portevin–Le Chatelierplastic instabilities in Al–Li–Cu–Zr alloy. Scr. Mater. 45 (7) (2001)801÷806.

Uwagi

Opracowanie ze środków MNiSW w ramach umowy 812/P-DUN/2016 na działalność upowszechniającą naukę.