Assessment of the tribological properties of hardfacing welding alloy Fe-Mn-C-B-Si-Ni-Cr in dry friction conditions

• Autorzy: Pashechko M. , Dziedzic K. , Dziubińska A , Barszcz M.

Warianty tytułu

PL

Badania właściwości tribologicznych powłok napawanych Fe-Mn-C-B-Si-Ni-Cr w warunkach tarcia suchego

• Języki publikacji: EN

Abstrakty

EN

The paper assesses the tribological properties of hardfacing coatings produced by gas metal arc welding. Flux-cored wires were used as a welding material. The core mixture was based on the Fe Mn-C-B-Si-Ni-Cr alloy. Seven types of flux-cored wires with different compositions were prepared. The flux-cored wires had a diameter of 2.4 mm. The tribological assessment was performer with an Amsler tribotester under dry friction conditions at different unit pressures: 3, 7, and 10 MPa. The results demonstrate that the coating L-6 has good tribological properties. The overlay weld had a hardness of 49 HRC. Following friction testing, the coatings were also examined with respect to their microhardness and microstructure.

PL

Praca przedstawia badania właściwości tribologicznych powłok otrzymanych metodą napawania łukowego w osłonie gazowej GMA. Jako materiał spawalniczy wykorzystano druty proszkowe (rdzeniowe). Mieszankę rdzeniową wykonano na podstawie stopu Fe-Mn-C-B-Si-Ni-Cr. Opracowano siedem rodzajów drutów proszkowych o różnych składach. Średnica drutów proszkowych wynosiła 2,4 mm. Badania tribologiczne przeprowadzono na tribotesterze Amslera w warunkach tarcia suchego przy różnych naciskach jednostkowych 3, 7 i 10 MPa. Wykazały one, że dobrymi właściwościami tribologicznymi cechowała się powłoka L-6 o twardości napoiny 49 HRC. Powłoki po tarciu poddano również badaniom mikrotwardości oraz mikrostrukturalnym.

Słowa kluczowe

EN

coatings; hardfacing by arc welding; flux-cored wire; wear

PL

powłoki; napawanie; drut proszkowy; zużycie

• Wydawca: Stowarzyszenie Inżynierów i Techników Mechaników Polskich
• Czasopismo: Tribologia
• Rocznik: 2016
• Tom: nr 2
• Strony: 101--110
• Opis fizyczny: Bibliogr. 9 poz., tys., tab.

Twórcy

autor

Pashechko M.

• Department of Fundamental of Technology, Fundamentals of Technology Faculty, Lublin University of Technology, ul. Nadbystrzycka 38, 20-618 Lublin, Poland

autor

Dziedzic K.

• Department of Fundamental of Technology, Fundamentals of Technology Faculty, Lublin University of Technology, ul. Nadbystrzycka 38, 20-618 Lublin, Poland

autor

Dziubińska A

• Department of Computer Modelling and Metal Forming Technologies, Mechanical Engineering Faculty, Lublin University of Technology, ul. Nadbystrzycka 38, 20-618 Lublin, Poland

autor

Barszcz M.

• Department of Fundamental of Technology, Fundamentals of Technology Faculty, Lublin University of Technology, ul. Nadbystrzycka 38, 20-618 Lublin, Poland

Bibliografia

• 1. Gidikova N., Ciaś A., Petkov V., Madej M., Sułowski M., Valov R.: Wear resistant chromium coatings modified with diamond nanoparticles, Archives of metallurgy and materials, Vol. 52, 2014, p. 1513–1516.
• 2. Adamiec P., Dziubiński J.: Wytwarzanie i właściwości warstw wierzchnich elementów maszyn transportowych, Wyd. Politechniki Śląskiej, Gliwice 2005.
• 3. Granat K.: Wieloskładnikowe stopy Fe-C-Cr-Si odporne na zużycie przeznaczone na odlewy i warstwy napawane, Oficyna Wydawnicza Politechniki Wrocławskiej, Wrocław 2005.
• 4. Badisch E., Katsich C., Winkelmann H., Franek F., Manish Roy: Wear behavior of hardfaced Fe-Cr-C alloy and austenitic steel under 2-body and 3-body conditions at elevated temperature, Tribology International, 2010, p.1234–1244.
• 5. Napiórkowski J., Pękalski G., Kołakowski K.: Badanie struktur i zużywania powłok napawanych w glebowej masie ściernej, Tribologia, tarcie, zużycie, smarowanie, Nr 3, 2012, p. 111–117.
• 6. Pashechko M., Lenik K.: Segregation of atoms of the eutectic alloys Fe-Mn-C-B-Si-Ni-Cr at friction wear, Wear, Vol. 267, 2009, p. 1301–1304.
• 7. Pashechko M., Dziedzic K., Barszcz M.: Study of the structure and properties of wear-resistant eutectic Fe-Mn-C-B-Si-Ni-Cr coatings, Powder metallurgy and metal ceramics, nr 7-8, Vol. 52, 2013, p. 469–476.
• 8. Pashechko M., Dziedzic K., Barszcz M.: Badania struktury i właściwości warstw wierzchnich powłok ze stopów eutektycznych Fe-Mn-C-B, Inżynieria Materiałowa, nr 2, Vol. 33, 2012, p. 82–85.
• 9. Pashechko M., Dziedzic K., Barszcz M.: Właściwości tribologiczne powłoki eutektycznej Fe-Mn-C-B-Si-Ni-Cr, Inżynieria powierzchni, nr 1, 2011, p. 40–45.

Uwagi

PL

Opracowanie ze środków MNiSW w ramach umowy 812/P-DUN/2016 na działalność upowszechniającą naukę.