Manganese influence on chromium distribution in high-chromium cast irons

• Autorzy: Byelikov S , Volchok I. , Netrebko V

Warianty tytułu

PL

Wpływ manganu na rozkład stężenia chromu w żeliwie wysokochromowym

• Konferencja: International Conference Development Trends in Mechanization of Foundry Process (6 ; 5-7.09.2013 ; Inwałd, Poland)
• Języki publikacji: EN

Abstrakty

EN

It is shown that chromium distribution in the metal base of high-chromium cast irons depends on manganese content. According to the X-ray micro-spectral analysis data with the increase of manganese content from 0.72 to 6.49% chromium content decreased in the near-carbide zones. At the same time chromium content in carbides increased. This process obtained particularly strong development inside eutectic colonies of carbides. As a result of it, when total chromium content in the alloy has been 23%, its concentration in the local zones was 12,3%, thus the necessary level of corrosion resistance has not been provided. The minimal chromium content has to amount 23.2%, at 6.49% Mn and 2.2...2.5% C in order to provide corrosion resistance of high-chromium cast irons.

PL

Pokazano, że rozkład chromu w osnowie metalowej żeliwa o wysokiej zawartości chromu zależy od zawartości manganu. Zgodnie z wynikami spektralnej mikroanalizy rentgenowskiej zwiększenie stężenie manganu z 0,72 do 6,49% powoduje zmniejszenie stężenia chromu w osnowie metalowej na granicy z węglikami. Równocześnie wzrasta zawartość chromu w węglikach. Zjawisko to występuje z większą intensywnością w osnowie metalowej ziaren eutektycznych, pomiędzy eutektycznymi węglikami. W wyniku redystrybucji chromu w żeliwie o zawartości 23% chromu występują lokalne strefy o stężeniu tego pierwiastku obniżonym do 12,3%, co skutkuje niedopuszczalnym obniżeniem odporności przeciwko korozji. Dla zapewnienia odporności korozyjnej wysokochromowego żeliwa, zawierającego od 2,2 do 2,5% C i 6,49% Mn, stop ten powinien zawierać powyżej 23,2% Cr.

Słowa kluczowe

EN

cast iron; chromium; manganese; distribution; microstructure

PL

żeliwo; chrom; mangan; rozkład; mikrostruktura

• Wydawca: Institute of Metallurgy and Materials Science of Polish Academy of Sciences ; Committee of Materials Engineering and Metallurgy of Polish Academy of Sciences
• Czasopismo: Archives of Metallurgy and Materials
• Rocznik: 2013
• Tom: Vol. 58, iss. 3
• Strony: 895--897
• Opis fizyczny: Bibliogr. 7 poz., rys., tab.

Twórcy

autor

Byelikov S

• Metal Technology Department, Zaporizhzhya National Technical University 64 Zhukovskogo St., 69063, Zaporizhzhya, Ukraine

autor

Volchok I.

• Metal Technology Department, Zaporizhzhya National Technical University 64 Zhukovskogo St., 69063, Zaporizhzhya, Ukraine

autor

Netrebko V

• Metal Technology Department, Zaporizhzhya National Technical University 64 Zhukovskogo St., 69063, Zaporizhzhya, Ukraine

Bibliografia

• [1] M. E. Garber, Castings from white wear-resistant cast irons. - M.: Mashinostroenie, 1972. - 112 p. (in Russian).
• [2] I. I. Tsypin, White wear-resistant cast irons. - M.: Metallurgiya, 1983. -176 p. (in Russian).
• [3] A. Gierek, L. Bajka, Zeliwo stopowe jako tworzyvo konstrukcyjne. - Katowice: Slask, 1976. - 230 p. (in Polish).
• [4] A. P. Chelyah, Economically alloyed metastable alloys and strengthening technologies. - Kharkov: NNC KHFTI, 2003. -212 p. (in Russian).
• [5] Structurally and non-structurally sensitive properties of chromium cast irons / A. A. Kirillov [and oth.] // Chernyemetally. -2007. - September. - P. 7-13. (in Russian).
• [6] I. P. Volchok, V. V. Netrebko, Manganese influence on the structure formation processes of wear-resistant cast irons // Stroitelstvo, materialovedenie, mashinostroenie: Compilation of scientific works. Vol. 64 - Dnepropetrovsk, PGASA, 2012. - P. 301-304. (in Russian).
• [7] A. P. Gulyaev, Metal Science. - M.: Metallurgiya, 1978. -647 p. (in Russian).