Why are you still using magnesium anodes?

• Autorzy: Gummow R. A.

Warianty tytułu

PL

Czy warto zawsze stosować anody magnezowe?

• Języki publikacji: EN

Abstrakty

EN

The service life of magnesium anode cathodic protection systems have been in many instances, less than design calculations would predict. Testing of high potential magnesium alloys from various suppliers using the ASTM G97-89 test method indicates that efficiencies are widely variable. The literature shows that various factors such as anode current density, anode oxidation reaction, anolyte chemistry, alloy chemical composition, and alloy microstructure can affect anode efficiency. Utilities are advised to conduct tests for alloy composition, microstructure, and backfill composition on anodes from industry suppliers in order to ensure anode quality and to maximize system life. But even with constant quality control efforts the efficiency can still be low owing to operating factors. From an efficiency perspective packaged zinc anodes would be a better option under some application conditions.

PL

Czas pracy systemów ochrony katodowej z anodami magnezowymi jest w wielu przypadkach krótszy niż wskazują na to obliczenia. Testy wysokopotencjałowych stopów magnezu, pochodzących od różnych dostawców, wykonane zgodnie z ASTM G97-89, wskazują na bardzo zróżnicowaną efektywność. Zgodnie z literaturą, na wydajność anody ma wpływ szereg czynników, takich jak: gęstość prądu, anodowa reakcja utleniania, charakterystyka środowiska anodowego oraz skład chemiczny i mikrostruktura stopu. Dla zapewnienia odpowiedniej jakości i maksymalizacji czasu pracy, zaleca się wykonywanie badań składu i mikrostruktury stopu anody oraz składu zasypki. Jednak nawet przy ciągłej kontroli jakości wydajność może być niska z uwagi na czynniki zewnętrzne. Z perspektywy efektywności anody cynkowe w zasypce byłyby lepszym wyborem w niektórych aplikacjach.

Słowa kluczowe

EN

magnesium anodes; efficiency; current density; oxidation reaction; chemical composition; microstructure; heat treatment; ASTM G97-89; backfill

PL

anody magnezowe; wydajność; gęstość prądu; reakcja utleniania; skład chemiczny; mikrostruktura; obróbka cieplna; ASTM G97-89; zasypka

• Wydawca: Wydawnictwo SIGMA-NOT
• Czasopismo: Ochrona przed Korozją
• Rocznik: 2013
• Tom: nr 2
• Strony: 39--43
• Opis fizyczny: Bibliogr. 11 poz., rys., tab., wykr.

Twórcy

autor

Gummow R. A.

• CORRENG Consulting Service Inc., Markham, Canada

Bibliografia

• 1. N ACE International, CP3-Cathodic Protection Technologist Course, p. 2-51
• 2. ASTM G97-89 ‘Standard Test Method for Laboratory Evaluation of Magnesium Sacrifi cial Anode Test Specimens for Underground Applications’, West Conshohocken, PA, ASTM, 1989
• 3. Gummow, R.A., Performance Effi ciency of High Potential Mg Anodes for Cathodically Protecting Iron Water Mains, Materials Performance, May 2004, p. 28-33
• 4. G. Song, A. Atrens, D.St. John, X. Wu, J. Nairn, The Anode Dissolution of Magnesium in Chloride and Sulphate Solutions, Corrosion Science 39, 10-11(1997), 2003
• 5. A. Antonyra, C.O Augustin, Anomolous Behaviour of Magnesium Anodes in Different Electrolytes at High Concentrations, Corrosion Reviews Special Issue: Corrosion Resistance of Magnesium Alloys, M.Schorr ed., Freund Publishing House Ltd 16,1- 2(1998) p. 136
• 6. H .A. Robinson, Fundamental Characteristics of Magnesium Galvanic Anodes, Cathodic Protection – A Symposium, Houston, TX, NACE, 1949
• 7. M ilitary Handbook-Electrical Engineering Cathodic Protection, USA Department of Defense, MIL-HDBK-1004/10, Jan 31, 1990, p. 118
• 8. Brian A. Martin, Magnesium Anode Performance, Materials Performance, August 1987, p. 16
• 9. H.A. Robinson, P.F. George, Effect of Alloying and Impurity Elements in Magnesium Alloy Cast Anodes, Corrosion, June 1954, p. 182-188
• 10. J. Genesca, C. Rodriguez, J. Juarez, B. Campillo and L. Martinez, Assessing and Improving Current Effi ciency in Magnesium Base Sacrifi cial Anodes by Micro-structure Control, Corrosion Reviews, Special Issue: Corrosion Resistance of Magnesium Alloys, Edited by M. Schorr, Freund Publishing House Ltd., Vol. 16, Nos. 1-2, 1998, p. 95-125.
• 11. N .G. Thompson and T. Barlo, Fundamental Process of Cathodically Protecting Steel Pipe Lines, Gas Research conference Proceedings presented 1983 at Rockville, MD: Government Institutes Inc.