Assessment of the fatigue life of machine components under service loading – a review of selected problems

Będkowski, W.

Artykuł - szczegóły

Tytuł artykułu

Assessment of the fatigue life of machine components under service loading – a review of selected problems

Autorzy

Będkowski W.

Treść / Zawartość

Pełne teksty:

Pobierz

Identyfikatory

Warianty tytułu

Języki publikacji

Abstrakty

Based on a literature review, the author provides a historical outline of the fatigue analysis and describes the current trends aiming at comprehension of the fatigue life of engineering structures under service loading. Next, an algorithm for multiaxial fatigue life prediction is identified, describing steps of calculation. Classification criteria of fatigue failure and components of the stress state in multiaxial loading conditions are also presented, recognising the importance of the so-called Standarised Load Histories (SLH) used in the comparative analysis of fatigue life of finished products.

Słowa kluczowe

fatigue life prediction multiaxial fatigue service loading

Wydawca

Polskie Towarzystwo Mechaniki Teoretycznej i Stosowanej

Czasopismo

Journal of Theoretical and Applied Mechanics

Rocznik

2014

Tom

Vol. 52 nr 2

Strony

443--458

Opis fizyczny

Bibliogr. 78 poz., rys., tab.

Twórcy

autor

Będkowski W.

w.bedkowski@po.opole.pl

Opole University of Technology, Opole, Poland

Bibliografia

1. Achtelik H., Macha E., Jakubowska I., 1983, Actual and estimated directions of fatigue fracture plane in zl250 cast iron under combined alternating bending and torsion, Studia Geotechnica et Mechanica, N, 2, 9-30
2. AFNOR A03-406, 1993, Fatigue of metals under variable amplitude loads – rainflow cycle counting method (in French), AFNOR
3. Bächström M., Koski K., Siljander A., Liukkonen S., Tikka J., Marquis G., 2004, Fatigue assessment of an aging aircraft’s wing under complex multiaxial spectrum loading, Proceedings of 7th International Conference on Biaxial/Multiaxial Fatigue and Fracture, ICBMFF, Berlin, 595-600
4. Bagci C., 1980, Fatigue design of machine elements using the “Bagci line” defining the fatigue failure surface line (mean stress diagram), Mechanical Engineering, 17, 2, 22-34
5. Bardenheier R., Rogers G., 2004, Experimental simulation of multiaxial stress states in material testing, Proceedings of 7th International Conference on Biaxial/Multiaxial Fatigue and Fracture, ICBMFF, Berlin, 527-534
6. BędkowskiW. Macha E., Ohnami M., Sakane M., 1995, Fracture plane of cruciform specimen in biaxial low cycle fatigue – estimate by varinace metod and experimental verification, Journal of Engineering Materials and Technology, Transaction ASME, 117, 2, 183-190
7. Będkowski W., 2005a, Fatigue tests of materials under biaxial loading, test stands and methodology, [In:] New Results in Fatigue and Fracture, Vol. 2, Zeszyty Naukowe Politechniki Opolskiej, 306, Mechanika, 84, 9-30
8. Będkowski W., 2005b, Model for fatigue life estimation under multiaxial random loading and its verification based on fatigue tests results, Zeszyty Naukowe Politechniki Opolskiej, 304, Mechanika, 82, 1, 21-28
9. Będkowski W., Lachowicz C., Macha E., 1988, Predicted fatigue fracture planes according to variance of shear stress under random triaxial stress state, Proceedings of the 9th Biennial European Conference on Fracture, E. Czoboly (Edit), I, 281-283
10. Będkowski W., Lachowicz C., Macha E., 1989, The variance method of predicting the fatigue fracture plane under multiaxial random loadings, Proceedings of 3rd International Conference on Biaxial/Multiaxial Fatigue, Stuttgart, 1, 7.1-7.18
11. Będkowski W., Łagoda T., Słowik J., 2007, Strain controlled tests for determining the change of the material fatigue parameters, Materials Science, 43, 4, 492-498
12. Będkowski W., Macha E., 1986, The expected position of fatigue fracture plane according to variance of the reduced stress, Proceedings of the 6th Biennial European Conference on Fracture, Amsterdam, 2, 1345-1352
13. Będkowski W., Macha E., 1987a, Computational – experimental methods to assess the fatigue life of machine components under multiaxial random loads (in Polish), Prace Naukowe Instytutu Konstrukcji i Eksploatacji Maszyn Politechniki Wrocławskiej, 50, Konferencje, 13, 163-170
14. Będkowski W., Macha E., 1987b, Methods for assessing the fatigue life of machine components under service loads (in Polish), Przegląd Mechaniczny, 21, 87, 5-7
15. Będkowski W., Macha.E., 1989, Methods for estimating the position of the expected fatigue fracture plane under complex random stress state, Prace Naukowe, Politechnika Warszawska, Mechanika, 121, 27-35
16. Będkowski W., Macha E., 1992, Fatigue tests of cruciform specimens under random loadings, construction of the stand and preliminary results, Reliability and Structural Integrity of Advanced Materials, Proceedings of the 9th Biennial European Conference on Fracture, Varna, I, 371-376
17. Będkowski W., Macha E., Niesłony A., 2004, Verification of the spectral method determining the fatigue life on the basis of steel 10HNAP (in Polish), Przegląd Mechaniczny, 12, 13-1618.
18. Będkowski W., Weber B., Macha E., Robert J.-L., 1999, Comparison of variance method and damage indicator methods for prediction of the fracture plane orientation in multiaxial fatigue, [In:] Multiaxial Fatigue and Fracture, E.Macha,W. Będkowski, T. Łagoda (Edit,), ESIS Publication 25, ELSEVIER, 147-165
19. Billy M., 1988, Fatigue Life under Stochastic Loads (in Czech), Slovenska Akademia Ved, Ustav Materialov a Mechaniky Strojov, Bratislava
20. British Standard BS 5400: 1980, Part10: Appendix B, 29
21. Brown M.W., Miller K.J., 1992, Two decades of progress in the assesment of multiaxial lowcycle fatigue, [In:] Low Cycle Fatigue and Life Prediction, ASTM STP 770, C. Amzallag, B.N. Leis and P. Rabbe (Edit,), 482-499
22. Cabralles J.S., Diez P.C.G., 1990, A new facility for aircraft structural testing, Closed Loop MTS, 17, 3, 2-10
23. Chen C.-S., Krause R., Petit R.G., Banks-Sills L., Ingraffea A.R., 2001, Numerical assessment of t-stress computation using a p-version finite element method, International Journal of Fracture, 107, 177-199
24. Cheng X., Ohkawa I., Misumi M., 2004, Mean stress efect on cyclic deformation and short crack growth behaviour in torsional fatigue of steels, Proceedings of 7th International Conference on Biaxial/Multiaxial Fatigue and Fracture, ICBMFF, Berlin, 259-264
25. Corten H.T., Dolan T.I., 1956, Cumulative fatigue damage, International Conference on Fatigue of Metals, London
26. Dannbauer H., Gaier C., Steinbatz M., 2004, A statistical measure of non-proportionality of stresses investigations and applications, Proceedings of 7th International Conference on Biaxial/Multiaxial Fatigue and Fracture, ICBMFF, Berlin, 623-628
27. Dietman H., Bhonghibhat T., Schmid A., 1989, Multiaxial fatigue behavior of steels under in-phase and out-of-phase loading including different wave form and frequencies, Proceedings of 3rd International Conference on Biaxial/Multiaxial Fatigue and Fracture, ICBMFF, Stuttgart, 61.1-61.17
28. Dmitricenko S.S., 1967, Modern methods of accelerated tests of machines for fatigue strength (in Russian), Vestnik Masinostrojenija, 2
29. Dowling N.E., 1972, Fatigue failure prediction for complicated stress-strain histories, Journal of Materials, ASTM, 7, 71-87
30. Downing S.D., Socie D.F., 1982, Simple rain flow counting algorithms, International Journal of Fatigue, 5, 31-44
31. E 1049-85, in: Annular Book of ASTM Standards, 1991, Section 3, Vol.03.01
32. Fatemi A., Yang L., 1998, Cumulative fatigue damage and life prediction theories: a survey of the state-of-the-art for homogeneous materials, International Journal of Fatigue, 20, 1, 9-34
33. Marquis G., Solin J., edit., 1997, Fatigue Design of Components, ESIS Publication 22, Elsevier
34. Garud Y.S., 1981, Multiaxial fatigue: a survey of the state-of-the-art, Journal of Testing and Evaluation, 9, 3, 165-178
35. Grinienko N.I., Szefer L.A., 1976, Spectral method for evaluating the fatigue life under random loadings (in Russian), Problemy Prochnosti, 1, 9-22
36. Haibach E., 1970, Modified linear damage accumulation hypothesis to account the progress of damage for fatigue strength (in German), Laboratorium fur Betriebsfestigkait, Darmstadt, Technische Mitteilungen TM, 50/70
37. Heuler P., Kl¨atschke H., 2003, Generation and use of standardised load spectra and load-time histories, Proceedigs of Conference on Fatigue Damage, Seville, 175-185
38. Jakubczak H., Sobczykiewicz W., 1999, Valuing hydraulic excavator attachments, the concept of quality (in Polish), Materiały XII Konferencji Naukowej Problemy Rozwoju Maszyn Roboczych, Zakopane, 1, 111-118
39. Jono M., 2003, fatigue damage and crack growth under variable amplitude loading and counting method of stress strain ranges, Proceedigs of Conference on Fatigue Damage, Seville, 54-62
40. Kanazawa K., Miller K.J., Brown M.W., 1977, Low cycle fatigue under out-of-phase loading condition, Journal of Engineering Materials and Technology, 9, 222-228
41. Kocańda D., Kocańda S., Torzewski J., 2004, The speed of fatigue cracks in aerospace aluminum alloy with a programmable load spectrum, Materiały XX Sympozjum Zmęczenie i Mechanika Pękania, Bydgoszcz, 179-186
42. Kocańda S., 1985, Fatigue Failure of Metals (in Polish), WNT, Warszawa
43. Kocańda S., Szala J., 1985, Fundamentals of Calculations of Fatigue (in Polish), PWN, Warszawa
44. Kuropatnicki A., Jakubczak H., 2004, Evaluating in designing the supporting structures of machines - nominal stress concept (in Polish), Materiały XX Sympozjum Zmęczenie i Mechanika Pękania, Bydgoszcz, 209-216
45. Lachowicz C., Łagoda T., Macha E., 1996, Comparison of analitical and algorithmical methods for life time estimation of 10hnap steel under random loadings, Fatigue’96, G. Lutjering and H. Nowack (Edit.), vol. I, Berlin, 595-600
46. Leese G.E., Mullin R.L., 1991, The role of fatigue analysis in the vehicle test simulation laboratory, SAE Technical Papers 910166, Detroit, 12
47. Macha E., Stężała H., 1985, Modelling of stress random histories by sinusoidal histories of real time when fatigue life of machine or constructure elements is determined, [In:] System Analyssis and Simulation, 2nd ed., A. Sydow et al., Akad-Verlag Berlin, 385-388
48. Manson S.S., 1960, Thermal stress in design. Part 19, Cyclic life of ductile materials, Machine Design, 139-144
49. Marin J., 1956, Interpretation of fatigue Strengths for Combined Stresses, Proceedigs of International Conference on Fatigue of Metals, London, 184-194
50. McDiarmid D.L., 1985, Fatigue under out-of phase biaxial stresses of different frequencies, multiaxial fatigue, ASTM STP 853, K.M. Miller and W.M. Brown (Edit.), Philadelphia, 606-621
51. Miner M.A., 1945, Cumulative damage in fatigue, Journal of Applied Mechanics, 12, 159-164
52. Morill J.H., Achatz T., Khosrovaneh A., 1998, An application for fatigue damage analysis using power spectral density from road durability events, SEA Technical Papers 980689, Warrendale, 55-62
53. Morrow J., 1965, Cyclic plastic strain energy and fatigue of metals, [In:] Internal Friction, Damping and Cyclic Plasticity, ASTM STP 378, 45-87
54. Nishihara T., Kawamoto M., 1945, The strength of metals under combined alternating Bendig and torsion with phase difference, Memoirs of the College on Engineering, Kyoto Imperial University, 11, 5, 85-112
55. Okamura H., Sakai S., Sususki I., 1979, Cumulative fatigue damage under random loadings, Fatigue of Engineering of Material and Structure, I, 409-419
56. Palin-Luc T., Banvillet A., Lasserre S., Vittori J.-F., 2004, A technique to reduce the duration of multiaxial fatigue tests under service loadings, Proceedings of 7th International Conference on Biaxial/Multiaxial Fatigue and Fracture, ICBMFF, Berlin, 421-426
57. Palmgren A., 1924, Die Lebensdauer von Kugellagen, VDI-Z, 68, 41, 339-341
58. Pawliczek R., 2004, The sensitivity of the material on load average in the fatigue (in Polish), Materiały XX Sympozjum Zmęczenie i Mechanika Pękania, Bydgoszcz, 311-318
59. Rotvel F., 1970, Biaxial fatigue tests with zero mean stresses using tubular specimens, International Journal of Mechanical Sciences, 12, 597-613
60. Saathoff A., Stolze F.-J., Zenner H., 2004, Creation of a synthetic road for multiaxial fatigue limit simulation on automobiles, Proceedings of 7th International Conference on Biaxial/Multiaxial Fatigue and Fracture, ICBMFF, Berlin, 541-546
61. Serensen S.V., Kogaev V.P., Snajdorovic R.M., 1975, The bearing capacity and strength calculations of machine parts (in Russian), Mashinostroenie, 3 62.
62. Simburger A., 1975, Strength behavior of tough materials with a phase-shifted multi-axis vibration stress with body-fixed and variable principal stress directions, LBF Bericht, Nr FB-121, Darmstadt
63. Sines G., Ohgi G., 1981, Fatigue criteria under combined stresses or strains, Journal of Engineering Materials and Technology, 103, 82-92
64. Sobczykiewicz W., 1994, Dimensioning of welded construction machine bearing in fatigue life (in Polish), Prace Naukowe Politechniki Warszawskiej, Mechanika, 157, Warszawa
65. Sonsino C.M., 2003, Structural durability of cast aluminium gearbox housing of underground vehicles under variable amplitude loading, Proceedigs of Conference on Fatigue Damage, Seville, 134-142
66. Sonsino C.M., Zenner H., Yousefi-Hashtyani F., K¨uppers M., 2004, Present limitation in the assesment of components under multiaxial service loading, Proceedings of 7th International Conference on Biaxial/Multiaxial Fatigue and Fracture, ICBMFF, Berlin, 17-25
67. Stephens R.L., Fatemi A., Stephens R.R., Fuchs H.O., 2000, Metal Fatigue in Engineering, John Wiley & Sons Inc., 2nd ed.
68. Susmel L., Tovo R., Lazzarin P., 2003, The mean stress influence on fatigue under multiaxial out-of-phase loading, Proceedigs of Conference on Fatigue Damage, Seville, 103
69. Szala J., 1975, The problem of approximation of load random variations on programmable fatigue life tests (in Polish), Akademia Techniczno-Rolnicza w Bydgoszczy, Zeszyty Naukowe, 26, Mechanika, 11, Bydgoszcz
70. Szala J., 1979, Research and Fatigue Calculations of Machine Components under Random and Programmed Loads (in Polish), IPPT PAN, Warszawa
71. Troschenko V.T., Sestopal L.F., 1975, Criteria of fatigue strength of metals in torsion (in Russian), Problemy Prochnosti, 2, 3-7
72. Wirshing P.H., Haugen E.B., 1974, A general statistical model for random fatigue, Transactions ASME, Series H, 96, 1, 34-40
73. Wirshing P.H., Light M.C., 1980, Fatigue under wide band random stresses, Journal of the Structural Division, July, 1593-1607
74. Wirshing P.H., Shekata A.M., 1977, Fatigue under wide band random stresses using the rainflow method, Transactions ASME, Series H, Journal of Engineering Materials and Technology, 205-211
75. Xie M., Hobbs R.E., 1999, A computer simulation approach for fatigue life prediction of engineering structure under random loading, [In:] Engineering Against Fatigue, J.H. Beynon,M.W. Brown et al. (Edit.), A. Balkema, 447-452
76. You B.R., Lee S.B., 1989, A critical review on multiaxial fatigue assesment of metals, International Journal of Fatigue, 11, 353-359
77. Zamrik S.Y., Frishmuth R.E., 1973, The effects of out-of-phase biaxial strain cycling on lowcycle fatigue, Experimental Mechanics, 204-208
78. Zenner H., 2004, Multiaxial fatigue – methods, hypotheses and applications an overview, Proceedings of 7th International Conference on Biaxial/Multiaxial Fatigue and Fracture, ICBMFF, Berlin, 3-16

Typ dokumentu

Bibliografia

Identyfikator YADDA

bwmeta1.element.baztech-5c3e4c7f-584a-49b6-bf24-a17487f9f54b