Dependence of the Structure And Magnetic Properties of Cast Plate-Shaped Nd60Fe30Al10 Samples on Their Thickness

• Autorzy: Michalski B. , Kaszuwara W. , Latuch J. , Pawlik P.

Identyfikatory

DOI

10.1515/amm-2015-0283

Warianty tytułu

PL

Zależność mikrostruktury i właściwości magnetycznych od grubości magnesów Nd60Fe30Al10 odlewanych w postaci płytek

• Języki publikacji: EN

Abstrakty

EN

The hard magnetic Nd-Fe-Al alloys are inferior to Nd-Fe-B magnets as far as the magnetic properties are concerned, but their great advantage is that they need no additional annealing to achieve good magnetic properties. These properties depend on the cooling rate from the melting state, and on the thickness of the sample - the best values are achieved at the quenching rates at which the samples have a thickness of 0.3-2 mm. The present study is concerned with the correlation between the magnetic properties of the plate-shaped Nd₆₀Fe₃₀Al₁₀ samples and their size - thickness. Two casting ways: with the melt stream perpendicular direction and parallel to the surface of the plates were used. The plates were produced by pressure casting and suction casting. The studies have shown that the cooling rates depends on local propagation on liquid metal in the mold resulting in heterogeneity of structure and properties.

PL

Stopy Nd-Fe-Al nie posiadają tak wysokich właściwości magnetycznych jak Nd-Fe-B. Ich dużą zaletą jest natomiast możliwość otrzymywania bezpośrednio poprzez odlewanie. Właściwości magnetyczne zależą od szybkości chłodzenia ciekłego stopu, co w praktyce określa się rozmiarem odlewanej próbki. Przy odlewaniu do form metalowych optymalny zakres wymiaru w kierunku odprowadzania ciepła to 0,3-2 mm. W niniejszej pracy zbadano zależność właściwości magnetycznych stopu Nd₆₀Fe₃₀Al₁₀ od grubości próbek w postaci płytek w zależności od sposobu odlewania (wtryskiwanie cieczy pod ciśnieniem i odlewanie z zasysaniem) oraz kierunku strumienia cieczy (prostopadle lub równolegle do powierzchni płytki). Badania wykazały, że szybkość chłodzenia zależy lokalnie od sposobu rozchodzenia się cieczy w formie, co skutkuje niejednorodnością mikrostruktury i właściwości.

Słowa kluczowe

EN

hard magnetic materials; Nd-Fe-Al alloys; rapid quenching

PL

twarde materiały magnetyczne; Nd-Fe-Al alloys; szybkie hartowanie

• Wydawca: Institute of Metallurgy and Materials Science of Polish Academy of Sciences ; Committee of Materials Engineering and Metallurgy of Polish Academy of Sciences
• Czasopismo: Archives of Metallurgy and Materials
• Rocznik: 2015
• Tom: Vol. 60, iss. 3A
• Strony: 1623--1627
• Opis fizyczny: Bibliogr. 9 poz., rys., tab., wykr.

Twórcy

autor

Michalski B.

• Warsaw University Of Technology, Faculty Of Materials Science And Engineering, 141 Wołoska Str., 02-507 Warszawa, Poland

autor

Kaszuwara W.

• Warsaw University Of Technology, Faculty Of Materials Science And Engineering, 141 Wołoska Str., 02-507 Warszawa, Poland

autor

Latuch J.

• Warsaw University Of Technology, Faculty Of Materials Science And Engineering, 141 Wołoska Str., 02-507 Warszawa, Poland

autor

Pawlik P.

• Czestochowa University Of Technology, Institute Of Physics, Czestochowa, 19 Armii Krajowej Av., 42-200 Czestochowa, Poland

Bibliografia

• [1] M. Mabiałek, P. Pietrusiewicz, M. Szota, A. Dobrzańska-Danikiewicz, S. Lesz, M. Dospiał, K. Błoch, K. Ozga, Archives of Metallurgy and Materials 59, 259-262 (2014).
• [2] A. Ceglarek, D. Płusa, P. Pawlik, M. Dospiał, Archives of Metallurgy and Materials 57, 229-232 (2012).
• [3] W. Kaszuwara, B. Michalski, P. Pawlik, J. Latuch, in: AIP Conf. Proc. 1347, 95, Internacional Conference on Magnetic Materials, Kolkata, (2011). AIP Conf. Proc. 1347 95 (2011).
• [4] Y. Li, J. Ding, S. C. Ng, X. Z. Wang, J. Magn. Magn. Mater., 187, L273 (1998).
• [5] L. Wang, J. Ding, Y. Li, Y. P. Feng, X. Z. Wang, N. X. Phuc, N. H. Dan, J. Magn. Magn. Mater. 224, 143 (2001).
• [6] W. T. Kim, B. Cantor, Scripta Metallurgia et Materialia 24, 4, 633 (1990).
• [7] A. Inoue, T. Z hang, A. Takeuchi, IEEE Trans. Magn. 33, 5, 3814 (1997).
• [8] B. Michalski, E. Jezierska, W. Kaszuwara, P. Pawlik, J. of Alloys and Compounds 509, 1, S423 (2011).
• [9] W. Kaszuwara, B. Michalski, J. Latuch, M. Leonowicz, J. Magn. Magn. Mater. 320, 14, e54 (2008).

Uwagi

EN

This work was supported by The National Centre for Research and Development, project no. N R15 0022 06 and by the Polish Ministry of Science and Higher Education, project no. N N507 450739