Evaluation of Cracking Causes of AlSi5Cu3 Alloy Castings

• Autorzy: Eperješi Š. , Matvija M. , Eperješi Ľ. , Vojtko M.

Identyfikatory

DOI

10.2478/amm-2014-0187

Warianty tytułu

PL

Określenie przyczyn pękania odlewów ze stopu AlSi5Cu3

• Języki publikacji: EN

Abstrakty

EN

Recently, the castings made from aluminum-silicon alloys by pressure die casting are increasingly used in the automotive industry. In practice, on these castings are high demands, mainly demands on quality of their structure, operating life and safety ensuring of their utilization. The AlSi5Cu3 alloy castings are widely used for production of car components. After the prescribed tests, the cracks and low mechanical properties have been identified for several castings of this alloy, which were produced by low pressure casting into a metal mould and subsequent they were heat treated. Therefore, analyses of the castings were realized to determine the causes of these defects. Evaluation of structure of the AlSi5Cu3 alloy and causes of failure were the subjects of investigation presented in this article.

PL

Zastosowanie odlewów ciśnieniowych ze stopów Al-Si ustawicznie wzrasta w przemyśle samochodowym, gdzie stopy te muszą spełniać wysokie wymagania odnośnie do jakości ich struktury, żywotności i bezpiecznego użytkowania. Odlewy ze stopu AlSi5Cu3 są szeroko stosowane w produkcji części samochodów. Wg pracy wady pęknięć wewnętrznych i niskie właściwości mechaniczne posiada część odlewów obrabianych cieplnie, odlanych do form metalowych pod niskim ciśnieniem. Praca poświęcona jest ocenie struktury i przyczynom pękania odlewów ze stopu AlSi5Cu3.

Słowa kluczowe

EN

AlSi5Cu3 alloy; microstructure; cracks; hardness

PL

stop AlSi5Su3; mikrostruktura; pękanie; twardość

• Wydawca: Institute of Metallurgy and Materials Science of Polish Academy of Sciences ; Committee of Materials Engineering and Metallurgy of Polish Academy of Sciences
• Czasopismo: Archives of Metallurgy and Materials
• Rocznik: 2014
• Tom: Vol. 59, iss. 3
• Strony: 1089--1092
• Opis fizyczny: Bibliogr. 11 poz., rys., tab.

Twórcy

autor

Eperješi Š.

• Faculty of Metallurgy, Technical University of Kosice, Letna 9, 040 01 Kosice, Slovakia

autor

Matvija M.

• Faculty of Metallurgy, Technical University of Kosice, Letna 9, 040 01 Kosice, Slovakia

autor

Eperješi Ľ.

• CČZ, A. S., Tovarni 202, 386 15 Strakonice, Czech Republic

autor

Vojtko M.

• Faculty of Metallurgy, Technical University of Kosice, Letna 9, 040 01 Kosice, Slovakia

Bibliografia

• [1] J. Malik, Technológia liatia zliatin hlinika, Kosice, 2013.
• [2] R. Kantorik, D. Bolibruchova, International Foundry Reseach 63, 2, 18-23 (2011).
• [3] T. Gŕigerova, R. Koreny, I. Lukač, Zlievarenstvo nezeleznych kovov, Bratislava, 1988.
• [4] W. K. Krajewski, J. Lelito, J. S. Suchy, P. Schumacher, Computed tomography - a new tool in structural examinations of castings, Archives of Metallurgy and Materials 54, 2, 335-338 (2009).
• [5] K. Haberl, W. K. Krajewski, P. Schumacher, Microstructural features of the grain-refined sand cast AlZn20 alloy, Archives of Metallurgy and Materials 55, 3, 837-841 (2010).
• [6] W. K. Krajewski, A. L. Greer, P. K. Krajewski, Trends in developments of high-aluminium zinc alloys of stable structure and properties, Archives of Metallurgy and Materials 58, 3, 859-861 (2013).
• [7] E. Tillová, M. Chalupová, L. Hurtalová, M. Bonek, L.A. Dobrzański, Journal of Achievements in Materials and Manufacturing Engineering 47, 1, 19-25 (2011).
• [8] R. Colás, E. Velasco, S. Valtierra, Castings, In: G. E. Totten, D. C. MacKenzie (Ed.), Handbook of Aluminum, Physical Metallurgy and Processes, Boca Raton, 591-641 (2003).
• [9] M. Fujda, O. Milkovič, M. Vojtko, T. Kvačkaj, T. Donič, Metallurgical Journal 62, 1, 14-19 (2009).
• [10] M. Matvija, M. Fujda, M. Vojtko, R. Kočiško, Acta Metallurgica Slovaca – Conference 3, 75-81 (2013).
• [11] E. Sjölander, S. Seifeddine, Journal of Materials Processing Technology 210, 1249-1259 (2010).