Zmęczenie kompozytów polimerowych podczas ustalonego i nieustalonego samorozgrzania
Języki publikacji
Abstrakty
The self-heating effect occurring during the cyclic loading of materials that exhibit thermoviscoelastic properties, depending on the loading conditions, may develop according to two possible scenarios: stationary and non-stationary. Since stationary self-heating has not been not previously studied in terms of the criticality of the self-heating effect, it is essential to perform such a study to better understand the degradation processes in this scenario and to confront the results with the criticality of non-stationary self-heating. In the present study, the experimental results on fatigue testing following the stationary self-heating scenario are presented and discussed. In order to characterize the degradation process, both self-heating temperature distributions and their evolution as well as acoustic emission measured at various self-heating temperature ranges were analyzed. The obtained results allow the influence of the self-heating effect on the residual life of composite structures under the stationary self-heating scenario to be estimated.
Efekt samorozgrzania, powstający podczas cyklicznych obciążeń materiałów, wykazujących właściwości termolepkosprężyste, w zależności od warunków obciążenia, może rozwinąć się według dwóch możliwych scenariuszy: ustalonego i nieustalonego. Ze względu na to, że samorozgrzanie ustalone nie było wcześniej badane pod względem krytyczności efektu samorozgrzania, istotne jest przeprowadzenie takich badań w celu lepszego zrozumienia procesów degradacji przy takim scenariuszu i skonfrontowania wyników z krytycznością dla nieustalonego samorozgrzania. W niniejszej pracy zostały przeanalizowane i opisane wyniki dotyczące badań eksperymentalnych zmęczenia według scenariusza ustalonego samorozgrzania. W celu scharakteryzowania procesu degradacji przeanalizowano zarówno rozkłady temperatury samorozgrzania i ich zmienność, jak i emisji akustycznej zmierzonej dla różnych zakresów temperatury samorozgrzania. Otrzymane wyniki pozwoliły na oszacowanie wpływu efektu samorozgrzania na trwałość resztkową struktur kompozytowych podczas występowania scenariusza ustalonego samorozgrzania.
Czasopismo
Rocznik
Tom
Strony
19--24
Opis fizyczny
Bibliogr. 15 poz., rys., tab.
Twórcy
autor
- Silesian University of Technology, Institute of Fundamentals of Machinery Design, ul. S. Konarskiego 18A, 44-100 Gliwice, Poland
Bibliografia
- [1] Katunin A., Domination of self-heating effect during fatigue of polymeric composites, Procedia Structural Integrity 2017, 5, 93-98.
- [2] Ferreira J.A.M., Costa J.D.M., Reis P.N.B., Richardson O.W., Analysis of fatigue and damage in glass-fibrereinforced polypropylene composite materials, Composites Science and Technology 1999, 59, 1461-1467.
- [3] Toubal L., Karama M., Lorrain B., Damage evolution and infrared thermography in woven composite laminates under fatigue loading, International Journal of Fatigue 2006, 28, 1867-1872.
- [4] Naderi M., Khonsari M.M., Thermodynamic analysis of fatigue failure in a composite laminate, Mechanics of Materials 2012, 46, 113-122.
- [5] Katunin A., Thermal fatigue of polymeric composites under repeated loading, Journal of Reinforced Plastics and Composites 2012, 31, 1037-1044.
- [6] Liu Z.Y., Beniwal S., Jenkins C.H.M., Winter R.M., The coupled thermal and mechanical influence on a glassy thermoplastic polyamide: Nylon 6,6 under vibro-creep, Mechanics of Time-Dependent Materials 2004, 8, 235-253.
- [7] Moisa S., Landsberg G., Rittel D., Halary J.L., Hysteretic thermal behavior of amorphous semi-aromatic polyamides, Polymer 2005, 46, 11870-11875.
- [8] Karama M., Determination of the fatigue limit of carbon/epoxy composite using thermographic analysis, Structural Control and Health Monitoring 2011, 18, 781-789.
- [9] Naderi M., Kahirdeh A., Khonsari M.M., Dissipated thermal energy and damage evolution of glass/epoxy using infrared thermography and acoustic emission, Composites: Part B 2012, 43, 1613-1620.
- [10] Kahirdeh A., Khonsari M.M., Criticality of degradation in composite materials subjected to cyclic loading, Composites: Part B 2014, 61, 375-382.
- [11] Katunin A., Gnatowski A., Influence of heating rate on evolution of dynamic properties of polymeric laminates, Plastics, Rubber and Composites 2012, 41, 233-239.
- [12] Katunin A., Critical self-heating temperature during fatigue of polymeric composites under cyclic loading, Composites Theory and Practice 2012, 12, 72-76.
- [13] Katunin A., Wronkowicz A., Bilewicz M., Wachla D., Criticality of self-heating in degradation processes of polymeric composites subjected to cyclic loading: A multiphysical approach, Archives of Civil and Mechanical Engineering 2017, 17, 806-815.
- [14] Ratner S.B., Korobov V.I., Self-heating of plastics during cyclic deformation, Polymer Mechanics 1965, 1, 63-68.
- [15] Wronkowicz A., Katunin A., Detection of damage initiation in composite structures subjected to self-heating based on acoustic emission, Modelling in Engineering 2017, 33, 114-119.
Uwagi
Opracowanie rekordu w ramach umowy 509/P-DUN/2018 ze środków MNiSW przeznaczonych na działalność upowszechniającą naukę (2018).
Typ dokumentu
Bibliografia
Identyfikator YADDA
bwmeta1.element.baztech-5972722f-9e01-4d47-9cb2-0efef6cb5cf1