Comparative analysis of welded and adhesive joints strength made of acid-resistant stainless steel sheets

• Autorzy: Rudawska A. , Pawlak P. , Miturska I. , Stančeková D. , Chyra M.

Identyfikatory

DOI

10.12913/22998624/78165

• Języki publikacji: EN

Abstrakty

EN

The article presents the selected results of strength tests on the effectiveness of bonding high-alloy steel 1.4310. Sheet steel is one of the materials that are difficult to activate energy. Effective joining of it is difficult, requires selection of the appropriate bonding technology. The paper focuses on the comparative tests of shear strength of one-single lap welded and bonded joints. The welding process was performed on 3 groups of samples TIG welding and argon, where the variable value of the welding process was current: 60A, 70A, 80A. The adhesion process was performed in 6 groups of samples which differed in the method of surface preparation and the type of the adhesive. Adhesive joints were made by using adhesive of epoxy resin and a hardener: Epidian 61/TFF at a mass ratio of 100:22 and Epidian 61/IDA at a mass ratio of 100:40. As a way of surface preparation applied 3 different, but simplified and environmentally friendly methods of surface preparation: degreasing with using cleaner Loctite 7061, abrasive machining with P320 and degreasing and grinding with abrasive T800 and degreasing were used. Make joints and curing the adhesive joints were carried out at ambient temperature. Analyzed the joints were tested destructive – which set out the shear strength, in accordance with DIN EN 1465 on the testing machine Zwick / Roell Z150. Based on the results of the research it was found that better results were obtained for the maximum welded joints, but this result was similar to the maximum value of the strength of the adhesive bond.

Słowa kluczowe

EN

adhesive joints; welded joints; strength; acid resistant steel

• Wydawca: Lublin University of Technology ; Polish Society of Ecological Engineering (PTIE), Branch of PTIE in Lublin
• Czasopismo: Advances in Science and Technology. Research Journal
• Rocznik: 2017
• Tom: Vol. 11, no 4
• Strony: 97--102
• Opis fizyczny: Bibliogr. 16 poz., fig., tab.

Twórcy

autor

Rudawska A.

• Department of Production Engineering of Lublin University of Technology, address: ul. Nadbystrzycka 36, 20-618 Lublin

autor

Pawlak P.

• Mechanical Engineering Faculty of Lublin University of Technology

autor

Miturska I.

• Department of Production Engineering of Lublin University of Technology, address: ul. Nadbystrzycka 36, 20-618 Lublin

autor

Stančeková D.

• Faculty of Mechanical Engineering, Univerzitna of University of Žilina, address: Univerzitna 1, 010 26, Žilina, SK

autor

Chyra M.

• Institute of Mechanical Technologies, Faculty of Mechanical Engineering and Computer Science, Czestochowa University of Technology, st. Armii Krajowej 19C, 42-201 Częstochowa

Bibliografia

• 1.Czaplicki J., Ćwikliński J., Godzimirski J., Konar P.: Klejenie tworzyw konstrukcyjnych. WKŁ, Warszawa 1987.
• 2.da Silva L.F.M., Carbas R.J.C., Critchlow G.W., Figueiredo M.A.V., Brown K., Effect of material, geometry, surface treatment and environment on the shear strength of single lap joints, International Journal of Adhesion and Adhesives, 2009, 29, 621–632.
• 3.DIN EN 1465. Adhesives. Determination of tensile lap-shear strength of bonded joints.
• 4.Ferenc K.: Spawalnictwo.WNT, Warszawa 2007.
• 5.Godzimirski J., Komorek A.: Trwałość zmęczeniowa zakładkowych i czołowych połączeń klejowych. Przegląd Mechaniczny, 12/2008, 40–44.
• 6.Godzimirski J., Kozakiewicz J., Łunarski J., Zielecki W.: Konstrukcyjne połączenia klejowe elementów metalowych w budowie maszyn. Oficyna Wydawnicza Politechniki Rzeszowskiej, Rzeszów 1997.
• 7.Kaliszewski E., Czyżowicz S.: Podstawowe wiadomości o stalach odpornych na korozję. Homepage: http://www.n-s.pl/betolit/betolit/porady/stal.pdf, z dnia 23.11.2016.
• 8.Kuczmaszewski J.: Fundamentals of metal-metal adhesive joint design. Politechnika Lubelska, Oddział PAN w Lublinie, 2006.
• 9.Mistur L., Czuchryj J.: Metody spawania oraz sposoby oceny jakości złączy spawanych. KaBe, Krosno 2005.
• 10.Penkała P., Płowaś B.,: The influence of currant mma welding on the tensile strenght of joint. Advances in Science and Technology Research Journal, 8/2014, 43–48.
• 11.PN-EN 10088–1:2014–12 – Stale odporne na korozję – Część 1: Wykaz stali odpornych na korozję
• 12.Rotella G., Alfano M., Schiefer T., Jansen I., Evaluation of mechanical and laser surface pre-treatments on the strength of adhesive bonded steel joints for automotive industry, Journal of Adhesion Science and Technology, 2016, 30,747–758.
• 13.Rudawska A., Dzwonkowski Ł. Przyrząd do ustalania próbek połączeń klejowych, zwłaszcza powierzchni płaskich. Zgłoszenie patentowe P403112.
• 14.Rudawska A., Łukasiewicz M.: Wpływ obróbki mechanicznej na wytrzymałość połączeń klejowych wybranych materiałów konstrukcyjnych. Przegląd Spawalnictwa, 8/2008.
• 15.Rudawska A.: Wybrane zagadnienia konstytuowania połączeń adhezyjnych jednorodnych i hybrydowych. Politechnika Lubelska, Lublin 2013.
• 16.Urbański T.: The influence of welding deformation types of hybrid node on assembly suitability. Advances in Science and Technology Research Journal, 6/2012, 42–47.

Uwagi

Opracowanie ze środków MNiSW w ramach umowy 812/P-DUN/2016 na działalność upowszechniającą naukę (zadania 2017)