Selected problems of formability of aluminised steel plates

• Autorzy: Żaba K.
• Języki publikacji: EN

Abstrakty

EN

The paper presents the results testing of the influence of heat treatment on formability of aluminised steel sheets. Tests have been conducted on samples of DX52D+AS120 aluminised steel sheet with the surface coating thickness of ca. 20 μm, before and after heat treatment in temperature range 300–1000 °C within 3–150 min and after deep drawing. Tests of thickness, roughness, structure and plasticity of coating before and after heat treatment and deep drawing have been conducted. Special equipment for non-destructive and destructive measurements has been used in these tests. A digital camera, an optical microscope and a scanning electron microscope have been used to show changes of coating surface and structure at the cross-section after tests.

Słowa kluczowe

EN

aluminised steel plate; heat treatment; deep drawing

PL

blacha stalowa; obróbka cieplna; głębokie tłoczenie

• Wydawca: Springer ; Wrocław University of Science and Technology
• Czasopismo: Archives of Civil and Mechanical Engineering
• Rocznik: 2012
• Tom: Vol. 12, no. 2
• Strony: 163--170
• Opis fizyczny: Bibliogr. 20 poz., rys., wykr.

Twórcy

autor

Żaba K.

• University of Science and Technology, Al. Mickiewicza 30, 30-059 Kraków, Poland

Bibliografia

• [1] S. Kobayashi, T. Yakou, Control of intermetallic compound layers at interface between steel and aluminum by diffusion treatment, Materials Science and Engineering: A 338 (1–2) (2002) 44–53.
• [2] N.A. El-Mahallawy, M.A. Taha, M.A. Shady, A.R. El-Sissi, A.N. Attia, W. Rief, Analysis of coating layer formed on steel strips during aluminising by hot dipping in Al–Si baths, Materials Science and Technology 13 (10) (1997) 832–840.
• [3] H. Glasbrenner, E. Nolde, Z. Voss, The influence of alloying elements on the hot-dip aluminizing process and on the subsequent high-temperature oxidation, Journal of Nuclear Materials 249 (1) (1997) 39–45.
• [4] S.H. Hwang, J.H. Song, Y.S. Kim, Effects of carbon content of carbon steel on its dissolution into a molten aluminum alloy, Materials Science and Engineering: A 390 (1–2) (2005) 437–443.
• [5] M.A. Shady, A.R. El-Sissi, A.M. Attia, N.A. El-Mahallawy, M.A. Taha, W. Reif, On the technological properties of steel strips aluminized in Al–Si baths, Journal of Materials Science 15 (12) (1996) 1032–1036.
• [6] G. Eggeler, W. Auer, H. Kaesche, On the influence of silicon on the growth of the alloy layer during hot dip aluminizing, Journal of Materials Science 21 (9) (1986) 3348–3350.
• [7] M.V. Akdeniz, A.O. Mekhrabov, T. Yilmaz, The role of Si addition on the interfacial interaction in Fe–Al diffusion layer, Scripta Metallurgica et Materialia 31 (12) (1994) 1723–1728.
• [8] ASTM A463/A463M 06, Standard Specification for Steel Sheet, Aluminum-Coated, by the Hot-Dip Process.
• [9] AK Steel, Technical Bulletin on Aluminized Steel Type 2, AK Steel Corporation, 703, Curtis Street, Middle Town, OH.
• [10] AK Steel, Production Data Bulletin on Aluminized Steel Type 1, AK Steel Corporation, 703, Curtis Street, Middle Town, OH.
• [11] DIN EN ISO 4287 1998 A1:2009, Geometrical Product Specifications (GPS) – Surface Texture: Profile Method – Terms, Definitions and Surface Texture Parameters.
• [12] ASME B46.1 2009, Surface Texture (Surface Roughness, Waviness, and Lay).
• [13] G.H. Awan, F. Hasan, The morphology of coating/substrate interface in hot-dip-aluminized steels, Materials Science and Engineering A 472 (1–2) (2008) 157–165.
• [14] H. Kawase, A. Takezoe, Peeling of coated metal due to severe press-forming in aluminized steel sheet, Transactions of the Iron and Steel Institute of Japan 22 (5) (1982) 371–376.
• [15] W. Deqing, Phase evolution of an aluminized steel by oxidation treatment, Applied Surface Science 254 (10) (2008) 3026–3032.
• [16] M. Suehiro, J. Maki, K. Kusumi, M. Ohgami, T. Miyakoshi, Properties of Aluminum-Coated Steels for Hot-Forming, Nippon Steel Technical Report 88, 2003, pp. 16–21.
• [17] K. Żaba, The influence of temperature and time of exhibition on a change of Al–Si coating thickness and surface texture on the steel plates, Archives of Metallurgy and Materials 55 (1) (2010) 151–162.
• [18] K. Żaba, The influence of heat treatment on selected physical properties of aluminized steel strips, Archives of Civil and Mechanical Engineering 10 (4) (2010) 107–118.
• [19] K. Żaba, M. Madej, Selected problems of abrasion resistance of aluminized steel tubes, Archives of Metallurgy and Materials 56 (4) (2011) 860–869.
• [20] K. Żaba, Wear resistance of aluminized steel plates, Archives of Metallurgy and Materials 56 (4) (2011) 871–882.