Tests of damage to Inconel 718 alloy used in aviation

• Autorzy: Krysztofik J. , Socha G.

Warianty tytułu

PL

Badania uszkodzeń stopu Inconel 718 stosowanego w lotnictwie

• Języki publikacji: EN

Abstrakty

EN

Inconel 718 alloy was tested. A new type of specimens of variable cross-sectional area measuring part was used for the tests. This provided a continuous distribution of plastic strain in that part of the sample. The proposed method enables to replace a series of specimens by one specimen. The degradation of the material u:as obtained by static tensile test and the creep test. The permanent deformation that varies along the specimen axis allows for an analysis of damage induced by a plastic deformation. The degradation of the alloy corresponds with the changes of acoustics properties of the material - attenuation of ultrasonic waves. It allows to determine the degree of damage to the material using a non-invasive - ultrasonic method. Using the damage parameter proposed by Johnson allows to obtain correlation between the non-destructive results and a damage degree of the material. The presented testing method delivers information about changes in the material structure caused by permanent deformation.

PL

Badaniom materiałowym poddano stop Inconel 718. Do badań użyto nowy rodzaj próbki o zmiennym polu przekroju części pomiarowej. Dzięki temu uzyskano ciągły rozkład odkształceń plastycznych w tej części próbki. Zaproponowana metoda badania uszkodzenia struktury prowadzi do zastąpienia w badaniach serii próbek jedną próbką. Degradację materiału zadano poprzez statyczną próbę rozciągania i próbę pełzania. Deformacja trwała, która zmienia się wzdłuż osi próbek, umożliwia analizę uszkodzenia wywołanego odkształceniem plastycznym. Z degradacją badanego stopu wiążą się zmiany jego właściwości akustycznych -współczynnika tłumienia materiału. Pozwala to na określenie stopnia uszkodzenia materiału za pomocą bezinwazyjnej metody nieniszczącej -metody ultradźwiękowej. Stosując parametr uszkodzenia zaproponowany przez Johnsona uzyskano korelację pomiędzy wynikami pomiarów nieniszczących a stopniem uszkodzenia materiału. Zastosowana w przedstawionym artykule metoda badawcza dostarcza informacji na temat zmian struktury materiału wywołanych deformacją trwałą.

Słowa kluczowe

EN

material degradation; ultrasonic wave attenuation factor; damage parameter; non-destructive testing

PL

parametr uszkodzenia; współczynnik tłumienia fali ultradźwiękowej; degradacja materiału; badania nieniszczące

• Wydawca: Wydawnictwa Naukowe Instytutu Lotnictwa
• Czasopismo: Prace Instytutu Lotnictwa
• Rocznik: 2017
• Tom: Nr 1 (246)
• Strony: 104--116
• Opis fizyczny: Bibliogr. 9 poz., diagr., rys., wykr.

Twórcy

autor

Krysztofik J.

• Materials & Structures Research Center, Institute of Aviation, Al. Krakowska 110/114, Warsaw

autor

Socha G.

• Institute of Aviation, Al. Krakowska 110/114, Warsaw

Bibliografia

• [1] Kachanov L. M.: 1986, „Introduction to Continuum Damage Mechanics", Martinus Nijhoff, The Netherlands.
• [2] Holler P. & Dobmann G., 1989, NDT-Techniques for monitoring material degradation. Mat Res. Soc. Symp. Proc. 142, pp. 105-118.
• [3] 2013, „Materials Degradation and Detection (MD2): Deep Dive Final Report", U.S. Department of Energy.
• [4] Deputat J.,1997, nieniszczące metody badania własności materiałów" [''Non-destructive methods for testing material properties "J, Biuro Gamma [Gamma Office], Warsaw.
• [5] Pawłowski Z., 1998, gadania nieniszczące" ["Non-destructive tests"]. Polish Society of Mechanical Engineers and Technicians, Ośrodek Doskonalenia Kadr SIMP w* Warszawie [SIMP Human Resources Traning Centre in Warsaw].
• [6] Socha G., Madejski B.. Krysztofik J. i Czarnewicz S., 2014, „Sposób badania uszkodzenia struktury materiału wywołanego deformacją trwałą próbki poddanej rozciąganiu i próbka do badania uszkodzenia struktury materiału" ["Test method of the material structure damage caused by permanent deformation of a specimen subjected to tension and a sample for testing the material structure damage"], Application to the Patent Office of the Republic of Poland No. p_409294. of27.08.2014.
• [7] Johnson G. R.,1980, „Materials characterization for computations involving severe dynamie loading", Proc. Army Symp. of Solid Mechanics, Cape Cod. Mass, pp. 62-67.
• [8] Krysztofik J., Socha G. and Kukla D., 2015, „Ocena stopnia uszkodzenia stopu Inconel 718 z zastosowaniem prądów wirowych" ["Assessment of Inconel 718 alloy damage degree with the use of eddy currents'1]. Przegląd Spawalnictwa [Welding Review], 87(12), pp. 24-26.
• [9] Krysztofik J., Malicki M., Madejski B., Czarnewicz S., Socha G., 2015, „Wczesne wykrywanie uszkodzeń superstopów na bazie niklu metodami nieniszczącymi" ["Early detection of damage to the nickel-based alloys using nondestructive methods "J: Institute of Aviation, Warsaw, (unpublished report)

Uwagi

PL

Opracowanie ze środków MNiSW w ramach umowy 812/P-DUN/2016 na działalność upowszechniającą naukę (zadania 2017).