Influence of elevated temperature on low cycle properties of WCLV/1.2344 steel

• Autorzy: Mroziński S. , Dolny A. , Hawryluk M. , Jakubik J.

Warianty tytułu

PL

Wpływ podwyższonej temperatury na właściwości niskocyklowe stali WCLV/1.2344

• Języki publikacji: EN

Abstrakty

EN

In this paper the results of low cycle fatigue tests of hot-work tool WCLV (1.2344) steel carried out at the temperatures of 20ºC and 600°C were presented. These results are used for numerical modelling of the wearing course of forging tools. This analysis was performed by means of hysteresis loop parameters recorded during tests. It was stated that the elevated temperature influences fatigue life and changes of hysteresis loop parameters in the function of loading cycles. At the temperature of 600°C, changes in the parameters were significantly higher than at 20°C. It make mare difficult to calculate the fatigue life of objects operating at elevated temperatures, because materiał data determined during tests reflects only the momentary properties of steel.

PL

W pracy zamieszczono wyniki niskocyklowych badań zmęczeniowych stali WCL V 1.2344 w temperaturze 20°C oraz 600°C. Analizę wyników prowadzono przy wykorzystaniu parametrów pętli histerezy rejestrowanych w trakcie badań. W pracy stwierdzono, że podwyższona temperatura ma wpływ na trwałość zmęczeniową oraz zmiany parametrów pętli w funkcji liczby cykli obciążenia. W temperaturze 600°C zmiany parametrów są zdecydowanie większe niż w temperaturze 20°C. Utrudnia to prowadzenie obliczeń trwałości obiektów poddanych eksploatacji w temperaturze podwyższonej. Wyznaczone podczas badań dane materiałowe odzwierciedlają bowiem jedynie chwilowe właściwości stali.

Słowa kluczowe

EN

low cycle fatigue; cyclic softening; fatigue life

PL

zmęczenie niskocyklowe; osłabienie cykliczne; trwałość zmęczeniowa

• Wydawca: Wydawnictwo Naukowe Instytutu Technologii Eksploatacji - Państwowego Instytutu Badawczego
• Czasopismo: Problemy Eksploatacji
• Rocznik: 2016
• Tom: no. 4
• Strony: 7--16
• Opis fizyczny: Bibliogr. 10 poz., wykr., zdj.

Twórcy

autor

Mroziński S.

• University of Science and Technology in Bydgoszcz, al. Prof. S. Kaliskiego 7, 85-796 Bydgoszcz, Poland

autor

Dolny A.

• Wrocław University of Technology, Wybrzeże Wyspiańskiego 27, 50-370 Wrocław, Poland

autor

Hawryluk M.

• Wrocław University of Technology, Wybrzeże Wyspiańskiego 27, 50-370 Wrocław, Poland

autor

Jakubik J.

• Wrocław University of Technology, Wybrzeże Wyspiańskiego 27, 50-370 Wrocław, Poland

Bibliografia

• 1. Fatemi A., Yang L., 1998: Cumulative Fatigue Damage and Life Prediction Theories: A Survey of the State of the Art for Homogeneous Materials, International Journal of Fatigue, Vol. 20, No. I, 9-34.
• 2. Manson S.S., Halford G.R., 1986. Re-Examination of Cumulative Fatigue Damage Anałysis - an Engineering Perspective. Engineering Fracture Mechanics, Vol. 25, No 5/6, 539-571.
• 3. Coffin L.F., A study of the effects of cyclic thermal stresses on a ductile metal. Trans ASME 1954; 76: 931-950.
• 4. Manson S.S., Behaviour of materials under conditions of thermal stress. NACA TN - 2933 1953.
• 5. Ramberg W., Osgood W.R., Description of stress-strain curves by three parameters. NACA, Tech. Note 402. 1943.
• 6. ASTM E 606 - 04 Standard Practice for Strain-Controlled Fatigue Testing.
• 7. Mroziński S., Stabilizacja własności cyklicznych metali i jej wpływ na trwałość zmęczeniową. Wydawnictwo Uczelniane Uniwersytetu Technologiczno-Przyrodniczego, Rozprawy Nr 128, Bydgoszcz 2008.
• 8. Mroziński S., Golański G., Low cycle fatigue and cyclic softening behaviour of martensitic cast steel, Engineering Failure Analysis, EFA 2086 November 2013 pp. 692-702.
• 9. Nagesha A., Valsan M., Kannan R., Bhanu Sankara Rao K., Mannan K., 2002. Influence of temperature on the low cycle fatigue behaviour of a modified 9Cr-1Mo ferritic steel. International Journal of Fatigue. 24, 1285-1293.
• 10. Zhanpinga Z., Delagnes D., Bernhart G., 2011. Cyclic behaviour and plastic strain memory effect of 55NiCrMo V7 steel under low cycle fatigue. Rare Metals. Vol. 30, 443.

Uwagi

Opracowanie ze środków MNiSW w ramach umowy 812/P-DUN/2016 na działalność upowszechniającą naukę.