The aim of these studies was to obtain single phase cubic modification of Li7La3Zr2O12 by mechanical milling and annealing of La(OH)3, Li2CO3 and ZrO2 powder mixture. Fritsch P5 planetary ball mill, Rigaku MiniFlex II X-ray diffractometer, Setaram TG-DSC 1500 analyser and FEI Titan 80-300 transmission electron microscope were used for sample preparation and investigations. The applied milling and annealing parameters allowed to obtain the significant contribution of c-Li7La3Zr2O12 in the sample structure, reaching 90%. Thermal measurements revealed more complex reactions requiring further studies.
Słowa kluczowe
Wydawca
Czasopismo
Rocznik
Tom
Strony
13--16
Opis fizyczny
Bibliogr. 9 poz., fot., rys.
Twórcy
autor
- Warsaw University of Technology, Faculty of Materials Science and Engineering, 141 Woloska Str., 02-507 Warsaw, Poland
autor
- Warsaw University of Technology, Faculty of Materials Science and Engineering, 141 Woloska Str., 02-507 Warsaw, Poland
autor
- Lublin University of Technology, Faculty of Electronics and Information Technology, 38a Nadbystrzycka Str., 20-618 Lublin, Poland
autor
- Silesian University of Technology, Institute of Engineering Materials and Biomaterials, 18a Konarskiego Str., 44-100 Gliwice, Poland
autor
- Keio University, Faculty of Science and Technology, Yokohama, Japan
autor
- Shizuoka University, Research Institute of Electronics, Hamamatsu, Japan
Bibliografia
- [1] V. Thangadurai, Ionics 12, 81-92 (2006).
- [2] N. A. Anurova, V. A. Blatov, G. D. Ilyushin, O. A. Blatova, A. K. Ivanov-Schitz, L. N. Demyanets, Solid State Ionics 179, 2248-2254 (2008).
- [3] S. Teng, J. Tan, A. Tiwari, Curr. Opin. Solid State Mater. Sci. 18, 29-38 (2014).
- [4] H. M. Rietveld, J. Appl. Cryst. 2, 65-71 (1969).
- [5] H. Xie, J. A. Alonso, Y. Li, M. T. Fernández-Díaz, J. B. Goodenough, Chem. Mater. 23, 3587-3589 (2011).
- [6] G. Hongxia, Ch. Kai, Y. Di, M. Ao, H. Mian, L. Yuanhua, N. Cewen, Rare Metal Materials and Engineering 45 (3), 612-616 (2016).
- [7] E. Yi, W. Wang, J. Kieffer, R. M. Laine, Journal of Power Sources 352, 156-164 (2017).
- [8] X. P. Wang, Y. Xia, J. Hu, Y. P. Xia, Z. Zhuang, L. J. Guo, H. Lu, T. Zhang, Q. F. Fang, Solid State Ionics 253, 137-142 (2013).
- [9] I. Quinzeni, D. Capsoni, V. Berbenni, P. O. Mustarelli, M. Sturini, M. Bini, Materials Chemistry and Physics 185, 55-64 (2017).
Uwagi
EN
1. Financial support from the National Centre for Research and Development in the framework of V4-Japan joint research project “AdOX” under the contract no V4-Jap/4/2016 is highly appreciated.
PL
2. Opracowanie rekordu w ramach umowy 509/P-DUN/2018 ze środków MNiSW przeznaczonych na działalność upowszechniającą naukę (2019).
Typ dokumentu
Bibliografia
Identyfikator YADDA
bwmeta1.element.baztech-52cc5cbe-32b7-4a24-9290-6efe0f3ed391